DIN 1693-1 GGG-60 Cast Iron: High-Strength, Wear-Resistant Material for Industrial Use

GGG-60, a perlitic-ferritic cast iron material for cast pieces for static and dynamic loading in machines and construction of vehicles as well as in the machine tool manufacture, in civil engineering and energy industry with increased strength and wear-resisting quality, crankshafts, wheel hubs, brake housing, tunnel rings, face plates for centre lathes, camps of high-pressure grease guns, tables for machine tools. The material is comparable to UNS F 33800 of the USA.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

7.15 g/cm³

Typical for Ductile (Nodular) Cast Iron

Mechanical

PropertyTemperatureValueComment

Compressive yield strength

20.0 °C

870 MPa

Elastic modulus

23.0 °C

165 - 180 GPa

Typical for Ductile (Nodular) Cast Iron

Elongation

20.0 °C

3 %

Hardness, Brinell

20.0 °C

200 - 250 [-]

Poisson's ratio

20.0 °C

0.27 - 0.29 [-]

Shear modulus

23.0 °C

63 - 66 GPa

Typical for Ductile (Nodular) Cast Iron

Tensile strength

20.0 °C

600 MPa

Yield strength

20.0 °C

380 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

100.0 °C

1.25E-5 1/K

200.0 °C

1.3E-5 1/K

300.0 °C

1.35E-5 1/K

400.0 °C

1.4E-5 1/K

500.0 °C

1.45E-5 1/K

Melting point

1150 - 1200 °C

Typical for Ductile (Nodular) Cast Iron

Specific heat capacity

23.0 °C

460 - 502 J/(kg·K)

Typical for Ductile (Nodular) Cast Iron

Thermal conductivity

100.0 °C

33 W/(m·K)

200.0 °C

34 W/(m·K)

300.0 °C

33 W/(m·K)

400.0 °C

32 W/(m·K)

500.0 °C

30 W/(m·K)

Chemical properties

PropertyValue

Carbon

3.5 - 3.8 %

Magnesium

0.06 - 0.12 %

Manganese

0.4 %

Phosphorus

0.1 %

Silicon

2 - 3 %

Sulfur

0.01 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. DIN 1693‑1 GGG‑40 Cast Iron: High‑Performance, High‑Strain Material for Automotive, Marine, and Industrial Applications
    2. DIN 1693-1 GGG-50 Cast Iron – Properties, Applications, and Performance
    3. DIN 1693-1 Grade GGG-70 Cast Iron – High Strength, Wear-Resistant Material for Heavy‑Duty Applications
    4. DIN 1693-1 Grade GGG‑80: High‑Strength Nodular Cast Iron for Heavy‑Duty Applications
    5. DIN 17730 Grade G‑Ni93C: Low‑Galling, Corrosion‑Resistant Cast Material for Food‑Grade and Industrial Applications
    6. DIN 17465 Grade GX40CrSi23 Cast Condition: High-Temperature, Wear-Resistant Material for Industrial Applications
    7. DIN 17465 Grade GX40NiCrSiNb38-18: High‑Temperature Cast Alloy for Automotive & Industrial Parts
    8. DIN 17465 GX25CrNiSi18-9 Cast Alloy – Exceptional Heat Resistance & Temperature Stability
    9. DIN 17465 GX25CrNiSi20-14: High-Performance Austenitic Stainless Steel for Extreme Heat Applications
    10. DIN 17465: GX40CrNiSi25-12 – High‑Strength Austenitic Stainless Steel for Heavy‑Load Applications