ASTM A565 Grade 615: Heat-Treated Stainless Steel for High-Temperature Applications
Properties
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Density | 23.0 °C | 7.6 - 7.7 g/cm³ | Typical for Martensitic Stainless Steel |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elastic modulus | 23.0 °C | 220 GPa | Typical for Martensitic Stainless Steel |
Elongation A50 | 23.0 °C | 15 % | |
Hardness, Brinell | 23.0 °C | 302 - 352 [-] | |
Poisson's ratio | 23.0 °C | 0.3 [-] | Typical for Martensitic Stainless Steel |
Reduction of area | 23.0 °C | 45 % | |
Shear modulus | 23.0 °C | 77 GPa | Typical for Martensitic Stainless Steel |
Tensile strength | 23.0 °C | 965 MPa | |
Yield strength Rp0.2 | 23.0 °C | 760 MPa |
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1E-5 - 1.5E-5 1/K | Typical for Martensitic Stainless Steel |
Melting point | 1370 - 1530 °C | Typical for Martensitic Stainless Steel | |
Specific heat capacity | 23.0 °C | 460 J/(kg·K) | Typical for Martensitic Stainless Steel |
Thermal conductivity | 23.0 °C | 14 - 31 W/(m·K) | Typical for Martensitic Stainless Steel |
Electrical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Electrical resistivity | 23.0 °C | 6E-7 Ω·m | Typical for Martensitic Stainless Steel |
Chemical properties
| Property | Value |
|---|---|
Carbon | 0.15 - 0.2 % |
Chromium | 12 - 14 % |
Manganese | 0.5 % |
Molybdenum | 0.5 % |
Nickel | 1.8 - 2.2 % |
Phosphorus | 0.04 % |
Silicon | 0.5 % |
Sulfur | 0.03 % |
Tungsten | 2.5 - 3.5 % |
Metal
- ASTM A27 Steel: How to Select the Ideal Grade for Your Casting
- ASTM A565 Grade 616 Heat-Treated Martensitic Stainless Steel: Key Properties & Performance
- DIN 17440 Grade X4CrNi18-12 Heat‑Treated Stainless Steel – Corrosion‑Resistant Wire & Components
- DIN 17440 Grade X6Cr17 Heat Treated – Premium Corrosion‑Resistant Stainless Steel
- ASTM A565 Grade XM-32: Heat-Treated Steel Optimized for High-Temperature Applications
- ASTM A565 Grade 616 Heat‑Treated Stainless Steel for High‑Temperature Applications
- ASTM A565 Grade 619 – Heat‑Treated for High‑Temperature Service
- ASTM A565 Grade S41425 – Heat‑Treated, High‑Temperature Service Steel
- DIN 1681 GS-60 Heat‑Treated Steel – Superior Wear Resistance & Strength
- DIN 1681 GS-38 Heat-Treated Steel: Applications & Performance