EN 10269 X10CrNiMoMnNbVB15‑10‑1: Heat‑Treatable, Warm‑Worked Austenitic Stainless Steel for High‑Temperature Applications

Application for mounting elements at increased temperatures.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.95 g/cm³

Mechanical

PropertyTemperatureValueComment

Elastic modulus

20.0 °C

207 GPa

100.0 °C

201 GPa

200.0 °C

193 GPa

300.0 °C

184 GPa

400.0 °C

175 GPa

500.0 °C

165 GPa

600.0 °C

158 GPa

700.0 °C

150 GPa

Elongation

20.0 °C

25 %

Poisson's ratio

23.0 °C

0.3 [-]

Typical for Austenitic Stainless Steel

Shear modulus

23.0 °C

77 GPa

Typical for Austenitic Stainless Steel

Tensile strength

20.0 °C

650 - 850 MPa

50.0 °C

610 MPa

100.0 °C

565 MPa

150.0 °C

530 MPa

200.0 °C

505 MPa

250.0 °C

490 MPa

300.0 °C

475 MPa

350.0 °C

465 MPa

400.0 °C

460 MPa

450.0 °C

450 MPa

500.0 °C

440 MPa

550.0 °C

430 MPa

600.0 °C

410 MPa

650.0 °C

390 MPa

Yield strength Rp0.2

20.0 °C

510 MPa

50.0 °C

490 MPa

100.0 °C

463 MPa

150.0 °C

446 MPa

200.0 °C

434 MPa

250.0 °C

423 MPa

300.0 °C

413 MPa

350.0 °C

405 MPa

400.0 °C

396 MPa

450.0 °C

391 MPa

500.0 °C

386 MPa

550.0 °C

378 MPa

600.0 °C

365 MPa

650.0 °C

346 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

100.0 °C

1.57E-5 1/K

200.0 °C

1.68E-5 1/K

300.0 °C

1.77E-5 1/K

400.0 °C

1.83E-5 1/K

500.0 °C

1.86E-5 1/K

600.0 °C

1.9E-5 1/K

Melting point

1230 - 1480 °C

Typical for Austenitic Stainless Steel

Specific heat capacity

20.0 °C

480 J/(kg·K)

Thermal conductivity

20.0 °C

12.5 W/(m·K)

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

7.4E-7 Ω·m

Chemical properties

PropertyValue

Boron

3E-3 - 9E-3 %

Carbon

0.07 - 0.13 %

Chromium

14 - 16 %

Manganese

5.5 - 7 %

Molybdenum

0.8 - 1.2 %

Nickel

9 - 11 %

Niobium

0.75 - 1.25 %

Nitrogen

0.1 - 0.11 %

Phosphorus

0.04 %

Silicon

1 %

Sulfur

0.015 - 0.03 %

Vanadium

0.15 - 0.4 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. EN 10269 NiCr15Fe7TiAl: Heat-Treated & Precipitation-Hardened Grade for High-Temperature Applications
    2. EN 10269 NiCr20TiAl: Solution Heat‑Treated & Precipitation Hardened for High‑Temperature Aerospace Applications
    3. EN 10213-4 Grade GX2CrNi19-11 – High‑Performance Austenitic Stainless Steel, Solution Heat‑Treated & Quenched
    4. EN 10213-4 Grade GX2CrNiMo19-11-2: Solution Heat‑Treated & Quenched Austenitic Stainless Steel for Pressure Vessels
    5. EN 10213-4 Grade GX2NiCrMo28-20-2 – Premium Solution‑Heat Treated Stainless Steel for Pressure Vessels
    6. EN 10213-4 Grade GX5CrNiMoNb19-11-2: Heat‑Treated, Quenched, Corrosion‑Resistant Austenitic Steel
    7. EN 10213-4 Grade GX5CrNi19-10 – Heat-Treated and Quenched Austenitic Stainless Steel
    8. EN 10213-4 Grade GX5CrNiMo19-11-2: High‑Performance Solution Heat‑Treated and Quenched Steel for Chemical & Textile Industries
    9. GX5CrNiNb19-11: Heat-Treated, Quenched Grade for High-Performance Cast Parts & Industrial Applications
    10. EN 10269 X7CrNiMoBNb16-16: Warm‑Worked & Precipitation‑Hardened High‑Temperature Steel