DIN 17440 X2CrNi19-11 Solution‑Heat‑Treated & Quenched Steel – Superior Corrosion Resistance & High‑Gloss Finish

Properties: - modification of 1.4301 - higher resistance to intergranular corrosion, caused of its lowered carbon content - application in chemical instrument construction and pharmacy industry - especially at demands for big wall thickness und simultaneous ability to polish to high gloss Application: - in nuclear reactor technique, for components in food industry exposed in organic acids - in soap and oil industry, plastics industry - for pressure tanks construction up to 300°C, above 300°C subjects to authorisation

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.9 - 7.92 g/cm³

Mechanical

PropertyTemperatureValue

Elastic modulus

-100.0 °C

206 GPa

20.0 °C

196 - 200 GPa

100.0 °C

190 - 194 GPa

200.0 °C

182 - 186 GPa

300.0 °C

174 - 179 GPa

400.0 °C

166 - 172 GPa

500.0 °C

158 - 165 GPa

600.0 °C

150 GPa

700.0 °C

142 GPa

800.0 °C

134 GPa

Elongation

20.0 °C

40 %

Elongation, transverse

20.0 °C

35 %

Poisson's ratio

20.0 °C

0.29 [-]

Shear modulus

20.0 °C

75.7 GPa

Tensile strength

20.0 °C

460 - 680 MPa

Tensile strength, transverse

20.0 °C

460 - 680 MPa

Yield strength

20.0 °C

180 MPa

Yield strength Rp0.2

20.0 °C

180 MPa

50.0 °C

162 MPa

100.0 °C

147 MPa

150.0 °C

132 MPa

200.0 °C

118 MPa

250.0 °C

108 MPa

300.0 °C

100 MPa

350.0 °C

94 MPa

400.0 °C

89 MPa

450.0 °C

85 MPa

500.0 °C

81 MPa

550.0 °C

80 MPa

Yield strength Rp0.2, transverse

20.0 °C

180 MPa

Yield strength Rp1.0

20.0 °C

215 MPa

50.0 °C

201 MPa

100.0 °C

181 MPa

150.0 °C

162 MPa

200.0 °C

147 MPa

250.0 °C

137 MPa

300.0 °C

127 MPa

350.0 °C

121 MPa

400.0 °C

116 MPa

450.0 °C

112 MPa

500.0 °C

109 MPa

550.0 °C

108 MPa

Yield strength Rp1.0, transverse

20.0 °C

215 MPa

Yield strength, transverse

20.0 °C

180 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1.49E-5 1/K

20.0 °C

1.61E-5 1/K

100.0 °C

1.6E-5 - 1.67E-5 1/K

200.0 °C

1.65E-5 - 1.72E-5 1/K

300.0 °C

1.7E-5 - 1.77E-5 1/K

400.0 °C

1.75E-5 - 1.81E-5 1/K

500.0 °C

1.8E-5 - 1.84E-5 1/K

600.0 °C

1.88E-5 1/K

700.0 °C

1.91E-5 1/K

800.0 °C

1.94E-5 1/K

Max service temperature, long

0 - 300 °C

Melting point

1230 - 1480 °C

Typical for Austenitic Stainless Steel

Specific heat capacity

-100.0 °C

440 J/(kg·K)

20.0 °C

472 - 500 J/(kg·K)

100.0 °C

487 J/(kg·K)

200.0 °C

503 J/(kg·K)

300.0 °C

512 J/(kg·K)

400.0 °C

520 J/(kg·K)

500.0 °C

530 J/(kg·K)

600.0 °C

541 J/(kg·K)

700.0 °C

551 J/(kg·K)

800.0 °C

559 J/(kg·K)

Thermal conductivity

20.0 °C

13.9 - 15 W/(m·K)

100.0 °C

15.4 W/(m·K)

200.0 °C

17.2 W/(m·K)

300.0 °C

18.7 W/(m·K)

400.0 °C

20.2 W/(m·K)

500.0 °C

21.6 W/(m·K)

600.0 °C

23 W/(m·K)

700.0 °C

24.4 W/(m·K)

800.0 °C

25.8 W/(m·K)

Thermal diffusivity

20.0 °C

3.7 mm²/s

100.0 °C

3.9 mm²/s

200.0 °C

4.2 mm²/s

300.0 °C

4.5 mm²/s

400.0 °C

4.7 mm²/s

500.0 °C

4.8 mm²/s

600.0 °C

5 mm²/s

700.0 °C

5.3 mm²/s

800.0 °C

5.6 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

7.3E-7 - 7.35E-7 Ω·m

100.0 °C

8E-7 Ω·m

200.0 °C

8.68E-7 Ω·m

300.0 °C

9.33E-7 Ω·m

400.0 °C

9.89E-7 Ω·m

500.0 °C

1.04E-6 Ω·m

600.0 °C

1.08E-6 Ω·m

700.0 °C

1.12E-6 Ω·m

800.0 °C

1.15E-6 Ω·m

Chemical properties

PropertyValue

Carbon

0.03 %

Chromium

18 - 20 %

Manganese

2 %

Nickel

10 - 12.5 %

Nitrogen

0.11 %

Phosphorus

0.05 - 0.45 %

Silicon

1 %

Sulfur

0.015 - 0.03 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. DIN 17440 X5CrNiMo17-13-3 Steel – Heat‑treated & Quenched for Superior Corrosion Resistance
    2. DIN 17440 X2CrNiMo17-13-2: Premium Heat-Treated Alloy for Chemical & Pressure Applications
    3. DIN 17440 X5CrNi18-10 Austenitic Steel – Heat‑Treated & Quenched for Superior Corrosion Resistance
    4. DIN 17440 Grade X6CrNiNb18-10 – Heat‑Treated & Quenched Steel for High‑Performance Applications
    5. DIN 17440 X6CrNiMoTi17-12-2 Steel – Solution Heat‑Treated & Quenched for Superior Corrosion Resistance
    6. DIN 17440 X5CrNiMo17-12-2: High-Performance Solution Heat‑Treated & Quenched Austenitic Steel
    7. DIN 17440 X2CrNiMoN17-13-5 – Heat-Treated, Quenched Stainless Steel for Corrosion-Resistant Applications
    8. DIN 17440 X2CrNiN18-10: Heat‑Treated, Quenched Austenitic Steel for High Strength & Corrosion Resistance
    9. X6CrNiTi18‑10 (DIN 17440) – Titanium‑Stabilised, Heat‑Treated Stainless Steel for High‑Temperature Welded Components
    10. DIN 17440 X2CrNiMoN17-13-3: High-Performance Austenitic Stainless Steel