DIN 17440 Grade X6CrNiNb18-10 – Heat‑Treated & Quenched Steel for High‑Performance Applications

Properties: - corrosion characteristics can be compared with those of 1.4541 - bends with certain welding conditions tohot cracking - due to the Nb-content not high polishable - for construction of pressure vessels to 300 °C certified, with appraisals to 550 °C Application: - in large extent applicable for welded parts in the chemical apparatus engineering, in food industry, in film and photo industry as well as for houseware

Quantity: 220,00€Additional services: Processing in our products

ALLEIMA (FORMERLY SANDVIK MATERIALS TECHNOLOGY)

MANUFACTURER

Information and services

Additional services: To ensure our customers' processes and/or products attain – and even exceed – their performance expectations, we offer a wide range of services within both the technical area and delivery logistics. Our technical services include: • Material consultations through our worldwide sales network • Advice in process optimization based on an in-depth applications knowledge • Joint new product development supported by our extensive R&D program View product groups and services

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.9 - 7.93 g/cm³

Mechanical

PropertyTemperatureValue

Elastic modulus

-100.0 °C

206 GPa

20.0 °C

196 - 200 GPa

95.0 °C

194.43 GPa

100.0 °C

190 - 194 GPa

150.0 °C

189.61 GPa

200.0 °C

182 - 186 GPa

205.0 °C

184.78 GPa

260.0 °C

179.95 GPa

300.0 °C

174 - 179 GPa

315.0 °C

175.13 GPa

370.0 °C

170.99 GPa

400.0 °C

166 - 172 GPa

425.0 °C

166.16 GPa

485.0 °C

161.34 GPa

500.0 °C

158 - 165 GPa

540.0 °C

157.2 GPa

595.0 °C

151.69 GPa

600.0 °C

150 GPa

650.0 °C

147.54 GPa

700.0 °C

142 GPa

705.0 °C

142.72 GPa

760.0 °C

137.9 GPa

800.0 °C

134 GPa

815.0 °C

133.76 GPa

870.0 °C

128.93 GPa

900.0 °C

127 GPa

1000.0 °C

120 GPa

Elongation

20.0 °C

35 %

Elongation, transverse

20.0 °C

30 %

Poisson's ratio

20.0 °C

0.27 [-]

95.0 °C

0.28 [-]

150.0 °C

0.29 [-]

205.0 °C

0.29 [-]

260.0 °C

0.29 [-]

315.0 °C

0.3 [-]

370.0 °C

0.31 [-]

425.0 °C

0.31 [-]

485.0 °C

0.32 [-]

540.0 °C

0.33 [-]

595.0 °C

0.33 [-]

650.0 °C

0.32 [-]

705.0 °C

0.33 [-]

760.0 °C

0.35 [-]

815.0 °C

0.35 [-]

870.0 °C

0.36 [-]

Shear modulus

20.0 °C

78.6 GPa

95.0 °C

75.84 GPa

150.0 °C

73.77 GPa

205.0 °C

71.71 GPa

260.0 °C

69.64 GPa

315.0 °C

67.57 GPa

370.0 °C

65.5 GPa

425.0 °C

63.43 GPa

485.0 °C

61.36 GPa

540.0 °C

59.3 GPa

595.0 °C

57.23 GPa

650.0 °C

55.85 GPa

705.0 °C

53.78 GPa

760.0 °C

51.11 GPa

815.0 °C

49.64 GPa

870.0 °C

47.57 GPa

Tensile strength

20.0 °C

510 - 740 MPa

Tensile strength, transverse

20.0 °C

510 - 740 MPa

Yield strength

20.0 °C

205 MPa

Yield strength Rp0.2

20.0 °C

205 MPa

50.0 °C

191 MPa

100.0 °C

177 MPa

150.0 °C

167 MPa

200.0 °C

157 MPa

250.0 °C

147 MPa

300.0 °C

136 MPa

350.0 °C

130 MPa

400.0 °C

125 MPa

450.0 °C

121 MPa

500.0 °C

119 MPa

550.0 °C

118 MPa

Yield strength Rp0.2, transverse

20.0 °C

205 MPa

Yield strength Rp1.0

20.0 °C

240 MPa

50.0 °C

226 MPa

100.0 °C

211 MPa

150.0 °C

196 MPa

200.0 °C

186 MPa

250.0 °C

177 MPa

300.0 °C

167 MPa

350.0 °C

161 MPa

400.0 °C

156 MPa

450.0 °C

152 MPa

500.0 °C

149 MPa

550.0 °C

147 MPa

Yield strength Rp1.0, transverse

20.0 °C

240 MPa

Yield strength, transverse

20.0 °C

205 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1.49E-5 1/K

20.0 °C

1.61E-5 1/K

100.0 °C

1.6E-5 - 1.67E-5 1/K

200.0 °C

1.7E-5 - 1.72E-5 1/K

300.0 °C

1.7E-5 - 1.77E-5 1/K

400.0 °C

1.8E-5 - 1.81E-5 1/K

425.0 °C

1.76E-5 1/K

485.0 °C

1.78E-5 1/K

500.0 °C

1.8E-5 - 1.84E-5 1/K

540.0 °C

1.8E-5 1/K

595.0 °C

1.83E-5 1/K

600.0 °C

1.88E-5 1/K

650.0 °C

1.85E-5 1/K

700.0 °C

1.91E-5 1/K

705.0 °C

1.87E-5 1/K

800.0 °C

1.94E-5 1/K

900.0 °C

1.97E-5 1/K

1000.0 °C

2E-5 1/K

Max service temperature, long

0 - 550 °C

Melting point

1230 - 1480 °C

Typical for Austenitic Stainless Steel

Specific heat capacity

-100.0 °C

440 J/(kg·K)

20.0 °C

472 - 500 J/(kg·K)

100.0 °C

487 J/(kg·K)

200.0 °C

503 J/(kg·K)

300.0 °C

512 J/(kg·K)

400.0 °C

520 J/(kg·K)

500.0 °C

530 J/(kg·K)

600.0 °C

541 J/(kg·K)

700.0 °C

551 J/(kg·K)

800.0 °C

559 J/(kg·K)

900.0 °C

565 J/(kg·K)

1000.0 °C

571 J/(kg·K)

Thermal conductivity

20.0 °C

14.3 - 15 W/(m·K)

100.0 °C

15.8 W/(m·K)

200.0 °C

17.5 W/(m·K)

300.0 °C

19 W/(m·K)

400.0 °C

20.5 W/(m·K)

500.0 °C

21.9 W/(m·K)

600.0 °C

23.3 W/(m·K)

700.0 °C

24.6 W/(m·K)

800.0 °C

26 W/(m·K)

900.0 °C

27.4 W/(m·K)

1000.0 °C

28.8 W/(m·K)

Thermal diffusivity

20.0 °C

3.8 mm²/s

100.0 °C

4 mm²/s

200.0 °C

4.2 mm²/s

300.0 °C

4.6 mm²/s

400.0 °C

4.8 mm²/s

500.0 °C

4.9 mm²/s

600.0 °C

5 mm²/s

700.0 °C

5.3 mm²/s

800.0 °C

5.6 mm²/s

900.0 °C

5.9 mm²/s

1000.0 °C

6 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

7.1E-7 - 7.3E-7 Ω·m

100.0 °C

7.76E-7 Ω·m

200.0 °C

8.49E-7 Ω·m

300.0 °C

9.14E-7 Ω·m

400.0 °C

9.71E-7 Ω·m

500.0 °C

1.02E-6 Ω·m

600.0 °C

1.07E-6 Ω·m

700.0 °C

1.1E-6 Ω·m

800.0 °C

1.14E-6 Ω·m

900.0 °C

1.17E-6 Ω·m

1000.0 °C

1.19E-6 Ω·m

Chemical properties

PropertyValue

Carbon

0.08 %

Chromium

17 - 19 %

Manganese

2 %

Nickel

9 - 12 %

Niobium

1 %

Phosphorus

0.05 - 0.45 %

Silicon

1 %

Sulfur

0.015 - 0.03 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. DIN 17440 X5CrNiMo17-13-3 Steel – Heat‑treated & Quenched for Superior Corrosion Resistance
    2. DIN 17440 X2CrNiMo17-13-2: Premium Heat-Treated Alloy for Chemical & Pressure Applications
    3. DIN 17440 X2CrNiMo18-14-3 Alloy: Heat‑Treated & Quenched for Superior Corrosion Resistance
    4. DIN 17440 X5CrNi18-10 Austenitic Steel – Heat‑Treated & Quenched for Superior Corrosion Resistance
    5. DIN 17440 X6CrNiMoTi17-12-2 Steel – Solution Heat‑Treated & Quenched for Superior Corrosion Resistance
    6. DIN 17440 X5CrNiMo17-12-2: High-Performance Solution Heat‑Treated & Quenched Austenitic Steel
    7. DIN 17440 X2CrNiMoN17-13-5 – Heat-Treated, Quenched Stainless Steel for Corrosion-Resistant Applications
    8. X6CrNiTi18‑10 (DIN 17440) – Titanium‑Stabilised, Heat‑Treated Stainless Steel for High‑Temperature Welded Components
    9. DIN 17440 X2CrNi19-11 Solution‑Heat‑Treated & Quenched Steel – Superior Corrosion Resistance & High‑Gloss Finish
    10. DIN 17440 X2CrNiMoN17-13-3: High-Performance Austenitic Stainless Steel