DIN 17200 Grade C60 Steel – Cold Shearing Treatment for Enhanced Ductility and Wear Resistance

Steel C 60 is suitable for high ductility parts and parts of increased wear resistance requirements in vehicle manufacturing, engine and machine engineering surface hardenable (e.g. transmission parts, shafts, axles). Additional application in tooling. Lowest application temp. -25 °C.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.8 - 7.85 g/cm³

Mechanical

PropertyTemperatureValue

Elastic modulus

-100.0 °C

217 GPa

20.0 °C

208.26 - 212 GPa

100.0 °C

203.78 - 207 GPa

200.0 °C

195 - 199 GPa

300.0 °C

185 - 192 GPa

400.0 °C

175 - 184 GPa

500.0 °C

173.04 - 175 GPa

600.0 °C

164 GPa

Hardness, Brinell

20.0 °C

255 [-]

Poisson's ratio

20.0 °C

0.27 [-]

100.0 °C

0.27 [-]

200.0 °C

0.28 [-]

300.0 °C

0.28 [-]

400.0 °C

0.28 [-]

500.0 °C

0.28 [-]

Shear modulus

20.0 °C

81 - 82.04 GPa

100.0 °C

80.18 GPa

200.0 °C

77.56 GPa

300.0 °C

74.62 GPa

400.0 °C

71.22 GPa

500.0 °C

67.36 GPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1.08E-5 1/K

20.0 °C

1.19E-5 1/K

100.0 °C

1.11E-5 - 1.25E-5 1/K

200.0 °C

1.21E-5 - 1.3E-5 1/K

300.0 °C

1.29E-5 - 1.36E-5 1/K

400.0 °C

1.35E-5 - 1.41E-5 1/K

500.0 °C

1.45E-5 1/K

600.0 °C

1.49E-5 1/K

Max service temperature

500 °C

Typical for Carbon Steel

Max service temperature, long

-25 - 0 °C

Melting point

1289 - 1478 °C

Typical for High Carbon Steel

Specific heat capacity

-100.0 °C

423 J/(kg·K)

20.0 °C

461 J/(kg·K)

100.0 °C

479 J/(kg·K)

200.0 °C

499 J/(kg·K)

300.0 °C

517 J/(kg·K)

400.0 °C

536 J/(kg·K)

500.0 °C

558 J/(kg·K)

600.0 °C

587 J/(kg·K)

Thermal conductivity

20.0 °C

41.7 - 51 W/(m·K)

100.0 °C

43.4 - 49.9 W/(m·K)

200.0 °C

43.2 - 47.8 W/(m·K)

300.0 °C

41.4 - 44.8 W/(m·K)

400.0 °C

39.1 W/(m·K)

500.0 °C

36.7 W/(m·K)

600.0 °C

34.1 W/(m·K)

Thermal diffusivity

20.0 °C

11.6 mm²/s

100.0 °C

11.3 mm²/s

200.0 °C

10.5 mm²/s

300.0 °C

9.5 mm²/s

400.0 °C

8.3 mm²/s

500.0 °C

7.1 mm²/s

600.0 °C

5.8 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

1.3E-7 - 2.5E-7 Ω·m

100.0 °C

2.95E-7 Ω·m

200.0 °C

3.65E-7 Ω·m

300.0 °C

4.53E-7 Ω·m

400.0 °C

5.56E-7 Ω·m

500.0 °C

6.74E-7 Ω·m

600.0 °C

8.13E-7 Ω·m

Chemical properties

PropertyValue

Carbon

0.57 - 0.65 %

Manganese

0.6 - 0.9 %

Phosphorus

0.05 %

Silicon

0.4 %

Sulfur

0.045 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. DIN 17200 Grade 28CrS4: Cold‑Sheared Steel for High‑Load Automotive Parts (+S)
    2. DIN 17200 Grade 25CrMo4 Cold‑Sheared (+S) Steel – High Strength & Ductility for Automotive & Machinery
    3. DIN 17200 Grade 37Cr4 Steel – Cold‑Sheared, High‑Performance for Vehicle and Engine Components
    4. DIN 17200 Grade 37CrS4 – Cold Sheared & Heat‑Treated for Superior Performance
    5. DIN 17200 Grade 38Cr2 Steel – Cold‑Sheared, Superior Strength & Durability
    6. DIN 17200 Grade 46Cr2 – Cold‑Sheared Steel with Superior Strength for Automotive & Machinery Applications
    7. DIN 17200 Grade 28Cr4 – Cold‑Shear Treated Steel for High‑Load Automotive Parts
    8. DIN 17200 Grade 25CrMoS4 - Cold-Sheared with Enhanced Strength (S)
    9. DIN 17200 Grade 28Mn6 Steel – Cold Shear (+S) for Automotive & Machine Applications
    10. DIN 17200 Grade 34CrMoS4 – Cold Shear Treatment (+S) for High-Performance Automotive Components