EN 12163 Grade Cu-DLP R230 – Premium Deoxidized Copper for Advanced Engineering
Cu-DLP, mat. No CW023A, is a deoxidized copper with limited, low residual copper-content. To the comparable DIN-make SW-Cu, mat. No 2.0076 acc. to DIN 1787 : 1973-01 applies: Tensile strength and Brinell hardness are increasable by cold forming. SW-Cu is hydrogen resistant and shows the lowest thermal and electrical conductivity of the pure copper materials. Processing properties: hot forming: very good cold forming: very good machinability: unfavorable hard soldering: very good soft soldering: very good gas-shielded welding: good burnishing: very good Application: Preferably in apparatus engineering and construction trade. For the electrolytically tinned strip the coatings (Sn bright, Sn matt, Sn fuzed, SnPb) are listed by the application (better solderability, better corrosion resistance, reduction of the electrical contact resistance, better appearance) in the DIN EN 14436 : 2004-11 (Table 5)
Properties
General
| Property | Temperature | Value |
|---|---|---|
Density | 20.0 °C | 8.9 g/cm³ |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elastic modulus | 20.0 °C | 129 GPa | |
Elongation | 20.0 °C | 18 % | |
Poisson's ratio | 23.0 °C | 0.34 [-] | Typical for Wrought Copper Pure / Low Alloyed Copper |
Shear modulus | 23.0 °C | 48 GPa | Typical for Wrought Copper Pure / Low Alloyed Copper |
Tensile strength | 20.0 °C | 230 MPa | |
Yield strength Rp0.2 | 20.0 °C | 190 MPa |
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.6E-5 - 1.8E-5 1/K | Typical for Wrought Copper Pure / Low Alloyed Copper |
Melting point | 965 - 1100 °C | Typical for Wrought Copper Pure / Low Alloyed Copper | |
Specific heat capacity | 20.0 °C | 385 J/(kg·K) | |
Thermal conductivity | 20.0 °C | 352 W/(m·K) |
Electrical
| Property | Temperature | Value |
|---|---|---|
Electrical conductivity | 20.0 °C | 5.20E+7 S/m |
Electrical resistivity | 20.0 °C | 1.9E-8 Ω·m |
Chemical properties
| Property | Value |
|---|---|
Bismuth | 5E-4 % |
Copper | 99.9 % |
Lead | 5E-3 % |
Phosphorus | 0.01 % |
Metal
- EN 12163 Grade CuZr H090 – High Strength, High Conductivity Copper Alloy
- EN 12163 Grade H120 CuZr Copper Alloy – High Strength, Excellent Conductivity
- EN 12163 Grade H075 CuZr Alloy – High Strength & Conductivity
- EN 12163 Grade Cu-DLP R200 – Premium Wrought Copper for Engineering Applications
- EN 12163 Cu-DLP H075: Premium Deoxidized Copper for High-Performance Applications
- EN 12163 Cu-DLP H085 – Premium Deoxidized Copper for High-Performance Applications
- EN 12163 Grade Cu-DLP H100 – Premium Deoxidized Copper with Superior Strength & Cold Forming
- EN 12163 Grade Cu-DHP R230 – Premium Phosphoric Pure Copper
- EN 12163 Grade Cu-DLP R260: Premium Deoxidized Copper for Superior Performance
- EN 12163 Cu-DLP R280: High-Performance Deoxidized Copper Grade