EN 10277‑5 Grade 50CrV4: Premium Cold‑Drawn, Quenched & Tempered Steel for High‑Load, High‑Wear Applications

Steel 50 CrV 4 is suitable for high loaded parts that have to meet increased tempering and high wear resistance requirements at best core qualities in aircraft and vehicle construction and engine and machine engineering (e.g. transmission and joint parts, axles). Furthermore application to spring and tool steel. Lowest application temp. -25 °C.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.83 g/cm³

Mechanical

PropertyTemperatureValue

Elastic modulus

-100.0 °C

217 GPa

20.0 °C

212 - 212.6 GPa

100.0 °C

207 GPa

200.0 °C

199 GPa

300.0 °C

192 GPa

400.0 °C

184 GPa

500.0 °C

175 GPa

600.0 °C

164 GPa

Elongation

20.0 °C

9 - 12 %

Poisson's ratio

20.0 °C

0.29 [-]

Reduction of area

20.0 °C

40 - 50 %

Tensile strength

20.0 °C

900 - 1300 MPa

Yield strength

20.0 °C

700 - 900 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1.05E-5 1/K

20.0 °C

1.15E-5 1/K

100.0 °C

1.21E-5 1/K

200.0 °C

1.27E-5 1/K

300.0 °C

1.32E-5 1/K

400.0 °C

1.36E-5 1/K

500.0 °C

1.4E-5 1/K

600.0 °C

1.44E-5 1/K

Max service temperature, long

-25 - 0 °C

Melting point

1382 - 1529 °C

Typical for Chromium Vanadium Steel

Specific heat capacity

-100.0 °C

423 J/(kg·K)

20.0 °C

461 J/(kg·K)

100.0 °C

479 J/(kg·K)

200.0 °C

499 J/(kg·K)

300.0 °C

517 J/(kg·K)

400.0 °C

536 J/(kg·K)

500.0 °C

558 J/(kg·K)

600.0 °C

587 J/(kg·K)

Thermal conductivity

20.0 °C

45.1 W/(m·K)

100.0 °C

45.1 W/(m·K)

200.0 °C

44.1 W/(m·K)

300.0 °C

41.9 W/(m·K)

400.0 °C

39.4 W/(m·K)

500.0 °C

36.9 W/(m·K)

600.0 °C

34.4 W/(m·K)

Thermal diffusivity

20.0 °C

12.5 mm²/s

100.0 °C

11.6 mm²/s

200.0 °C

10.6 mm²/s

300.0 °C

9.5 mm²/s

400.0 °C

8.4 mm²/s

500.0 °C

7.1 mm²/s

600.0 °C

5.8 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

2.31E-7 Ω·m

100.0 °C

2.84E-7 Ω·m

200.0 °C

3.58E-7 Ω·m

300.0 °C

4.48E-7 Ω·m

400.0 °C

5.52E-7 Ω·m

500.0 °C

6.71E-7 Ω·m

600.0 °C

8.06E-7 Ω·m

Chemical properties

PropertyValue

Carbon

0.47 - 0.55 %

Chromium

0.9 - 1.2 %

Manganese

0.7 - 1.1 %

Phosphorus

0.04 %

Silicon

0.4 %

Sulfur

0.03 %

Vanadium

0.1 - 0.2 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. High-Strength 25CrMo4 Steel – EN 10277-5 Cold-Drawn, Turned, Quenched & Tempered
    2. EN 10277‑5: 25CrMoS4 Cold‑Drawn, Quenched & Tempered – Premium High‑Strength Steel for Automotive & Engine Parts
    3. EN 10277-5 Grade 28Cr4: High‑Strength Cold Drawn or Turned Steel, Quenched and Tempered
    4. EN 10277-5 Grade 34CrS4 Cold-Drawn or Turned Steel – Quenched & Tempered for Vehicle and Engine Applications
    5. EN 10277-5 Grade 36CrNiMo4 – Cold-Drawn, Turned, Quenched & Tempered Steel for High-Performance Applications
    6. EN 10277-5 Grade 37Cr4: Premium Cold-Drawn & Quenched Steel for High-Performance Automotive & Machine Parts
    7. EN 10277-5 Grade 37CrS4: High-Performance Cold-Drawn, Quenched, and Tempered Steel for Automotive & Machinery Applications
    8. EN 10277-5 Grade 38Cr2 – Cold‑Drawn, Quenched & Tempered Steel for High‑Strength Automotive Components
    9. EN 10277-5 Grade 38CrS2: High-Strength Cold-Drawn, Turned, Quenched & Tempered Steel
    10. EN 10277‑5 Grade 41Cr4 Steel – Cold‑Drawn, Turned, Quenched & Tempered