EN 10263-4 Grade Cq35 Quenched & Tempered Steel – High Strength & Cold-Formability

The cold-upsettable steel Cq 35 can be cold-formed with a medium rate of forming according to the usual forming methods on single-stage and multi-stage presses. It is used, for example, for screws in the lower dimension range as well as for nuts of strength class 8.8.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.82 g/cm³

Mechanical

PropertyTemperatureValueComment

Elastic modulus

-100.0 °C

217 GPa

20.0 °C

212 GPa

100.0 °C

207 GPa

200.0 °C

199 GPa

300.0 °C

192 GPa

400.0 °C

184 GPa

500.0 °C

175 GPa

600.0 °C

164 GPa

Elongation

20.0 °C

17 - 20 %

Poisson's ratio

23.0 °C

0.29 [-]

Typical for Medium Carbon Steel

Reduction of area

20.0 °C

40 - 50 %

Shear modulus

23.0 °C

75 - 80 GPa

Typical for Carbon Steel

Tensile strength

20.0 °C

550 - 780 MPa

Yield strength

20.0 °C

320 - 430 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1.08E-5 1/K

20.0 °C

1.19E-5 1/K

100.0 °C

1.25E-5 1/K

200.0 °C

1.3E-5 1/K

300.0 °C

1.36E-5 1/K

400.0 °C

1.41E-5 1/K

500.0 °C

1.45E-5 1/K

600.0 °C

1.49E-5 1/K

Max service temperature

500 °C

Typical for Carbon Steel

Melting point

1380 - 1514 °C

Typical for Medium Carbon Steel

Specific heat capacity

-100.0 °C

423 J/(kg·K)

20.0 °C

461 J/(kg·K)

100.0 °C

479 J/(kg·K)

200.0 °C

499 J/(kg·K)

300.0 °C

517 J/(kg·K)

400.0 °C

536 J/(kg·K)

500.0 °C

558 J/(kg·K)

600.0 °C

587 J/(kg·K)

Thermal conductivity

20.0 °C

48 W/(m·K)

100.0 °C

48.9 W/(m·K)

200.0 °C

47.5 W/(m·K)

300.0 °C

44.7 W/(m·K)

400.0 °C

41.6 W/(m·K)

500.0 °C

38.6 W/(m·K)

600.0 °C

35.5 W/(m·K)

Thermal diffusivity

20.0 °C

13.3 mm²/s

100.0 °C

12.6 mm²/s

200.0 °C

11.5 mm²/s

300.0 °C

10.2 mm²/s

400.0 °C

8.9 mm²/s

500.0 °C

7.5 mm²/s

600.0 °C

6 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

2.17E-7 Ω·m

100.0 °C

2.62E-7 Ω·m

200.0 °C

3.32E-7 Ω·m

300.0 °C

4.2E-7 Ω·m

400.0 °C

5.23E-7 Ω·m

500.0 °C

6.41E-7 Ω·m

600.0 °C

7.8E-7 Ω·m

Chemical properties

PropertyValue

Carbon

0.32 - 0.39 %

Manganese

0.5 - 0.8 %

Phosphorus

0.04 %

Silicon

0.4 %

Sulfur

0.035 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. EN 10263-4 Grade 37Cr4 Quenched & Tempered Steel – High Strength & Durability
    2. EN 10263-4 Grade 38Cr2 Quenched & Tempered Steel – Specifications & Applications
    3. EN 10263-4 Grade 41Cr4 Quenched & Tempered Steel – Optimal for Cold-Forming, High-Strength Screws & Ball Studs
    4. EN 10263-4 Grade 42CrMo4 Quenched & Tempered Steel – High‑Strength, Cold‑Formable Grade 10.9/12.9
    5. EN 10263-4 Grade 46Cr2 Quenched & Tempered Steel: High-Strength, Precision-Engineered for Heavy-Duty Fasteners
    6. EN 10263-4 Grade 30CrNiMo8 Steel – Quenched & Tempered (QT) for High‑Strength Screws
    7. EN 10263-4 Grade 34Cr4 Quenched & Tempered Steel – High Strength & Formability
    8. EN 10263-4: Grade 34CrNiMo6 Quenched & Tempered Steel – High-Strength, Cold-Formable
    9. EN 10263-4 Grade 25CrMo4 Quenched & Tempered Steel – High Strength, Cold-Formable
    10. EN 10263-4 Grade 34CrMo4 Quenched & Tempered Steel – High Strength & Versatility