EN 10269 Grade 35B2 QT Steel – Full Specs & Performance Overview

Application for mounting elements at increased temperatures.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.82 - 7.85 g/cm³

Mechanical

PropertyTemperatureValueComment

Elastic modulus

-100.0 °C

217 GPa

20.0 °C

212 GPa

100.0 °C

205 - 207 GPa

200.0 °C

195 - 199 GPa

300.0 °C

185 - 192 GPa

400.0 °C

184 GPa

500.0 °C

175 GPa

600.0 °C

164 GPa

Elongation

20.0 °C

22 %

Poisson's ratio

23.0 °C

0.29 [-]

Typical for Medium Carbon Steel

Reduction of area

20.0 °C

45 %

Shear modulus

23.0 °C

75 - 80 GPa

Typical for Carbon Steel

Tensile strength

20.0 °C

500 - 650 MPa

Yield strength

20.0 °C

280 - 300 MPa

Yield strength Rp0.2

20.0 °C

300 MPa

50.0 °C

287 - 289 MPa

100.0 °C

255 - 270 MPa

150.0 °C

235 - 251 MPa

200.0 °C

220 - 229 MPa

250.0 °C

203 - 213 MPa

300.0 °C

186 - 192 MPa

350.0 °C

167 - 182 MPa

400.0 °C

147 - 173 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1.08E-5 1/K

20.0 °C

1.19E-5 1/K

100.0 °C

1.11E-5 - 1.25E-5 1/K

200.0 °C

1.21E-5 - 1.3E-5 1/K

300.0 °C

1.29E-5 - 1.36E-5 1/K

400.0 °C

1.41E-5 1/K

500.0 °C

1.45E-5 1/K

600.0 °C

1.49E-5 1/K

Max service temperature

500 °C

Typical for Carbon Steel

Melting point

1380 - 1514 °C

Typical for Medium Carbon Steel

Specific heat capacity

-100.0 °C

423 J/(kg·K)

20.0 °C

461 J/(kg·K)

100.0 °C

479 J/(kg·K)

200.0 °C

499 J/(kg·K)

300.0 °C

517 J/(kg·K)

400.0 °C

536 J/(kg·K)

500.0 °C

558 J/(kg·K)

600.0 °C

587 J/(kg·K)

Thermal conductivity

20.0 °C

48 W/(m·K)

100.0 °C

48.9 W/(m·K)

200.0 °C

47.5 W/(m·K)

300.0 °C

44.7 W/(m·K)

400.0 °C

41.6 W/(m·K)

500.0 °C

38.6 W/(m·K)

600.0 °C

35.5 W/(m·K)

Thermal diffusivity

20.0 °C

13.3 mm²/s

100.0 °C

12.6 mm²/s

200.0 °C

11.5 mm²/s

300.0 °C

10.2 mm²/s

400.0 °C

8.9 mm²/s

500.0 °C

7.5 mm²/s

600.0 °C

6 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

2.17E-7 Ω·m

100.0 °C

2.62E-7 Ω·m

200.0 °C

3.32E-7 Ω·m

300.0 °C

4.2E-7 Ω·m

400.0 °C

5.23E-7 Ω·m

500.0 °C

6.41E-7 Ω·m

600.0 °C

7.8E-7 Ω·m

Chemical properties

PropertyValue

Aluminium

0.02 %

Boron

8E-4 - 5E-3 %

Carbon

0.32 - 0.4 %

Manganese

0.5 - 0.8 %

Phosphorus

0.03 - 0.04 %

Silicon

0.4 %

Sulfur

0.015 - 0.035 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. EN 10269 21CrMoV5-7 Quenched & Tempered Steel – Superior High-Temperature Strength
    2. EN 10269 Grade 25CrMo4 Quenched & Tempered: Premium High‑Strength Steel
    3. EN 10269 Grade 30CrNiMo8 – High‑Performance Quenched & Tempered Steel for Aircraft & Heavy Machinery
    4. EN 10269 Grade 34CrNiMo6 – Quenched & Tempered (QT) Steel for High-Stress Applications
    5. EN 10269 40CrMoV4-6 Quenched & Tempered Steel – High‑Temperature Performance up to 540 °C
    6. EN 10269 Grade 42CrMo4 Quenched & Tempered (QT) – High‑Performance Steel for Heavy‑Duty Applications
    7. EN 10269 X12CrNiMoV12-3 Quenched & Tempered Steel – Martensitic Stainless for Turbine Applications
    8. EN 10269 Grade X19CrMoNbVN11-1 - Quenched & Tempered Steel for High-Temperature Applications
    9. EN 10269 Grade X8Ni9 – Premium Low‑Temperature Quenched & Tempered Ni‑Alloyed Steel
    10. EN 10269 Grade C35E – High-Performance Quenched & Tempered Steel for Automotive & Machinery