EN 12168 Grade CuZn38Pb2 R410: Premium Wrought Copper Brass for Cold Forming & Machining
CW607N is suited for cold forming and easy to machine. Application: bending, riveting, embossing and upsetting parts
Properties
General
| Property | Temperature | Value |
|---|---|---|
Density | 20.0 °C | 8.4 - 8.44 g/cm³ |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elastic modulus | 20.0 °C | 102 GPa | |
Elongation | 20.0 °C | 12 - 15 % | |
Elongation A10 | 20.0 °C | 12 % | |
Elongation A100 | 20.0 °C | 8 - 10 % | |
Elongation A11.3 | 20.0 °C | 10 % | |
Poisson's ratio | 20.0 °C | 0.34 [-] | |
Shear modulus | 23.0 °C | 40 GPa | Typical for Wrought Copper Brass |
Tensile strength | 20.0 °C | 410 MPa | |
Yield strength Rp0.2 | 20.0 °C | 190 - 250 MPa |
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 100.0 °C | 2E-5 1/K | |
300.0 °C | 2.1E-5 1/K | ||
Melting point | 875 - 1075 °C | Typical for Wrought Copper Brass | |
Specific heat capacity | 20.0 °C | 377 J/(kg·K) | |
Thermal conductivity | 20.0 °C | 109 - 110 W/(m·K) | |
Electrical
| Property | Temperature | Value |
|---|---|---|
Electrical conductivity | 20.0 °C | 1.39E+7 - 1.40E+7 S/m |
Specific Electrical conductivity | 24 % IACS |
Chemical properties
| Property | Value |
|---|---|
Aluminium | 0.05 % |
Copper | 60 - 61 % |
Iron | 0.2 % |
Lead | 1.6 - 2.5 % |
Nickel | 0.3 % |
Tin | 0.2 % |
Metal
- EN 1652 CuNi30Mn1Fe R410 – Premium Copper-Nickel-Manganese Alloy
- EN 1652 Grade CuZn38Pb2 H110 – Premium Wrought Copper Brass
- EN 1652 Copper Brass CuZn38Pb2 R340 – Specifications & Performance
- EN 1652 Grade CuZn38Pb2 R400 – Specifications & Properties
- EN 12164 Grade CuZn38Pb2 R490 – Premium Wrought Copper Brass Specification
- EN 12168 Grade CuZn38Pb1 H120 – Premium Copper Brass Alloy for Precision Applications
- EN 12168 Grade CuZn40Mn1Pb1AlFeSn H130 – Premium Copper‑Brass Rods & Forged Parts
- EN 12168 Grade CuZn38Pb2 H120 Copper Alloy Bars – Properties & Specifications
- EN 12168 Grade CuZn38Pb2 R360 – Premium Copper‑Brass for Cold Forming
- EN 12168 Grade CuZn39Pb2 (R410) – Specifications & Performance