EN 10216-2 Grade 20CrMoV13-5-5 Quenched & Tempered Seamless Tubes for High-Temperature Applications

Seamless tubes of the high-temperature 20CrMoV13-5-5 are used in steam boiler and pipeline construction, pressure vessel and apparatus engineering, especially in chemical industry and power station construction at temperatures from approx. 200 °C to maximum 400 °C and simultaneously high pressures. The total load and the special scaling circumstances can decrease or increase the temperature limit. Weldability is available.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.83 g/cm³

Mechanical

PropertyTemperatureValueComment

Elastic modulus

-100.0 °C

217 GPa

20.0 °C

212 GPa

100.0 °C

207 GPa

200.0 °C

199 GPa

300.0 °C

192 GPa

400.0 °C

184 GPa

500.0 °C

175 GPa

600.0 °C

164 GPa

Elongation

20.0 °C

16 %

Elongation, transverse

20.0 °C

14 %

Poisson's ratio

23.0 °C

0.29 [-]

Typical for Chromium Molybdenum Steel

Tensile strength

20.0 °C

740 - 880 MPa

Tensile strength, transverse

20.0 °C

740 - 880 MPa

Yield strength Rp0.2

20.0 °C

590 MPa

150.0 °C

575 MPa

200.0 °C

570 MPa

250.0 °C

560 MPa

300.0 °C

550 MPa

350.0 °C

510 MPa

400.0 °C

470 MPa

450.0 °C

420 MPa

500.0 °C

370 MPa

Yield strength Rp0.2, transverse

20.0 °C

590 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1.05E-5 1/K

20.0 °C

1.15E-5 1/K

100.0 °C

1.21E-5 1/K

200.0 °C

1.27E-5 1/K

300.0 °C

1.32E-5 1/K

400.0 °C

1.36E-5 1/K

500.0 °C

1.4E-5 1/K

600.0 °C

1.44E-5 1/K

Max service temperature, long

200 - 550 °C

Melting point

1382 - 1529 °C

Typical for Chromium Molybdenum Steel

Specific heat capacity

-100.0 °C

423 J/(kg·K)

20.0 °C

461 J/(kg·K)

100.0 °C

479 J/(kg·K)

200.0 °C

499 J/(kg·K)

300.0 °C

517 J/(kg·K)

400.0 °C

536 J/(kg·K)

500.0 °C

558 J/(kg·K)

600.0 °C

587 J/(kg·K)

Thermal conductivity

20.0 °C

25.7 W/(m·K)

100.0 °C

27.4 W/(m·K)

200.0 °C

28.5 W/(m·K)

300.0 °C

28.9 W/(m·K)

400.0 °C

28.5 W/(m·K)

500.0 °C

27.7 W/(m·K)

600.0 °C

26.8 W/(m·K)

Thermal diffusivity

20.0 °C

7.1 mm²/s

100.0 °C

7.1 mm²/s

200.0 °C

6.9 mm²/s

300.0 °C

6.6 mm²/s

400.0 °C

6.1 mm²/s

500.0 °C

5.3 mm²/s

600.0 °C

4.5 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

4.05E-7 Ω·m

100.0 °C

4.67E-7 Ω·m

200.0 °C

5.53E-7 Ω·m

300.0 °C

6.5E-7 Ω·m

400.0 °C

7.62E-7 Ω·m

500.0 °C

8.92E-7 Ω·m

600.0 °C

1.03E-6 Ω·m

Chemical properties

PropertyValue

Aluminium

0.04 %

Carbon

0.17 - 0.23 %

Chromium

3 - 3.3 %

Copper

0.3 %

Manganese

0.3 - 0.5 %

Molybdenum

0.5 - 0.6 %

Nickel

0.3 %

Phosphorus

0.03 %

Silicon

0.15 - 0.35 %

Sulfur

0.01 - 0.02 %

Vanadium

0.45 - 0.55 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. EN 10137-2 Grade S890QL – High-Strength Quenched & Tempered Steel for Heavy-Duty Applications
    2. EN 10137-3 Grade S500A: Quenched & Tempered Fine‑Grained Steel for Structural Applications
    3. EN 10083-1 Grade 51CrV4: Quenched & Tempered Steel (QT)
    4. EN 10213 Grade G17CrMo9-10 – Quenched & Tempered (QT) Steel for High-Temperature Applications
    5. EN 10085 Grade 15 CrMoV 5.9: Quenched & Tempered Steel for Durable Machine Components
    6. EN 10216-2 Grade 11CrMo9-10 Quenched & Tempered Seamless Tubes – High‑Temperature, High‑Pressure Applications
    7. EN 10216-2 Grade 20CrMoV13-5 Quenched & Tempered Steel – High‑Temperature, High‑Pressure Hydrogenation Applications
    8. EN 10216‑2 Grade X12CrMo91 (Quenched & Tempered) – Premium High‑Temperature Steel for Hydrogenation Vessels
    9. EN 10216-2 Grade 25CrMo4 Quenched & Tempered Seamless Tubes for High‑Temperature Applications
    10. EN 10216‑2 X20CrMoV12‑1 – Tempered Steel with Exceptional High‑Temperature Strength