EN 10269 Grade 19MnB4: Advanced Annealing for Spheroidized Carbides (+AC)

The cold upsettable steel 19MnB4 is cold formable in hard rolled condition at low and mean deforming degrees and in heat trated condition GKZ resp. K+GKZ+K cold formable at high deformation degrees. Application in unnealed condition for outside hexagonal screws of strength category 8.8 in a small and mean dimensional range. Suitability for complex presswork components. Further application for mounting elements at lower temperatures.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.82 - 7.85 g/cm³

Mechanical

PropertyTemperatureValueComment

Elastic modulus

-100.0 °C

217 GPa

20.0 °C

212 GPa

100.0 °C

205 - 207 GPa

200.0 °C

195 - 199 GPa

300.0 °C

185 - 192 GPa

400.0 °C

175 - 184 GPa

500.0 °C

175 GPa

600.0 °C

164 GPa

Poisson's ratio

23.0 °C

0.29 [-]

Typical for Low Carbon Steel

Reduction of area

20.0 °C

64 %

Shear modulus

23.0 °C

82 GPa

Typical for Low Carbon Steel

Tensile strength

20.0 °C

520 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1.08E-5 1/K

20.0 °C

1.19E-5 1/K

100.0 °C

1.11E-5 - 1.25E-5 1/K

200.0 °C

1.21E-5 - 1.3E-5 1/K

300.0 °C

1.29E-5 - 1.36E-5 1/K

400.0 °C

1.35E-5 - 1.41E-5 1/K

500.0 °C

1.45E-5 1/K

600.0 °C

1.49E-5 1/K

Max service temperature

500 °C

Typical for Carbon Steel

Melting point

1480 - 1526 °C

Typical for Low Carbon Steel

Specific heat capacity

-100.0 °C

423 J/(kg·K)

20.0 °C

461 J/(kg·K)

100.0 °C

479 J/(kg·K)

200.0 °C

499 J/(kg·K)

300.0 °C

517 J/(kg·K)

400.0 °C

536 J/(kg·K)

500.0 °C

558 J/(kg·K)

600.0 °C

587 J/(kg·K)

Thermal conductivity

20.0 °C

39.6 W/(m·K)

100.0 °C

41 W/(m·K)

200.0 °C

41 W/(m·K)

300.0 °C

39.9 W/(m·K)

400.0 °C

38.1 W/(m·K)

500.0 °C

35.9 W/(m·K)

600.0 °C

33.6 W/(m·K)

Thermal diffusivity

20.0 °C

11 mm²/s

100.0 °C

10.6 mm²/s

200.0 °C

9.9 mm²/s

300.0 °C

9 mm²/s

400.0 °C

8.1 mm²/s

500.0 °C

6.9 mm²/s

600.0 °C

5.7 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

2.63E-7 Ω·m

100.0 °C

3.12E-7 Ω·m

200.0 °C

3.85E-7 Ω·m

300.0 °C

4.7E-7 Ω·m

400.0 °C

5.71E-7 Ω·m

500.0 °C

6.88E-7 Ω·m

600.0 °C

8.25E-7 Ω·m

Magnetic

PropertyValueComment

Curie temperature

770 °C

Typical for Low Carbon Steel

Chemical properties

PropertyValue

Aluminium

0.02 %

Boron

1E-3 - 5E-3 %

Carbon

0.17 - 0.24 %

Manganese

0.8 - 1.15 %

Phosphorus

0.03 - 0.04 %

Silicon

0.4 %

Sulfur

0.035 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. EN 10269 Grade 21CrMoV5‑7 (Annealed + AC) – High‑Temperature Steel for Screws & Nuts
    2. EN 10263-4 Grade 41Cr4 Steel - Annealing for Spheroidized Carbides (+AC)
    3. EN 10263‑4 Grade 42CrMo4: Annealed for Spheroidized Carbides – High‑Performance Steel
    4. EN 10263-4 Grade 46Cr2: Optimized Annealing for Spheroidized Carbides (+AC)
    5. EN 10263-3 Grade 17Cr3 Steel – Annealed for Spheroidized Carbides (+AC)
    6. EN 10263-3 Grade 20MoCr4: High-Performance Steel with Annealed Spheroidized Carbides (+AC)
    7. EN 10269 42CrMo4 Steel – Annealed for Spheroidized Carbides (+AC)
    8. EN 10269 Grade 25CrMo4 Annealed for Spheroidized Carbides (+AC) – High Strength & Toughness
    9. EN 10269 Grade 35B2 – Annealed for Spheroidized Carbides: Enhanced High-Temperature Performance
    10. EN 10263-4: Grade 19MnB4 Steel – Annealed for Spheroidized Carbides (AC)