ISO 683-1 C45 Grade Steel – Normalized or Normalized Formed (N)
Steel C45 is suitable for medium loaded components in vehicle manufacturing, engine and machine engineering (e.g. gear shafts, gear wheels, clutch parts).
Properties
General
| Property | Temperature | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|---|
Density | 20 °C | 7.8 g/cm³ | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging |
20 °C | 7.8 - 7.85 g/cm³ | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | |
20 °C | 7.85 g/cm³ | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging |
Mechanical
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
Elastic modulus | -100 °C | 217 GPa | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | |
20 °C | 210 - 212 GPa | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | ||
20 °C | 210 - 210.1 GPa | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | ||
20 °C | 210 GPa | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | ||
20 °C | 210.1 - 212 GPa | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | ||
20 °C | 210.1 GPa | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | ||
20 °C | 212 GPa | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | ||
100 °C | 205.0 - 207 GPa | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | ||
100 °C | 205 - 207 GPa | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | ||
100 °C | 205.0 GPa | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | ||
100 °C | 205 - 205.0 GPa | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | ||
100 °C | 205 GPa | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | ||
100 °C | 207 GPa | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | ||
200 °C | 195 - 199 GPa | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | ||
200 °C | 195 - 198.8 GPa | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | ||
200 °C | 195 GPa | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | ||
200 °C | 198.8 - 199 GPa | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | ||
200 °C | 198.8 GPa | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | ||
200 °C | 199 GPa | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | ||
300 °C | 185 - 192 GPa | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | ||
300 °C | 185 - 191.4 GPa | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | ||
300 °C | 185 GPa | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | ||
300 °C | 191.4 - 192 GPa | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | ||
300 °C | 191.4 GPa | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | ||
300 °C | 192 GPa | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | ||
400 °C | 175 - 184 GPa | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | ||
400 °C | 175 - 183.2 GPa | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | ||
400 °C | 175 GPa | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | ||
400 °C | 183.2 - 184 GPa | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | ||
400 °C | 183.2 GPa | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | ||
400 °C | 184 GPa | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | ||
500 °C | 173.2 - 175 GPa | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | ||
500 °C | 173.2 GPa | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | ||
500 °C | 175 GPa | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | ||
600 °C | 164 GPa | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | ||
Elongation | 12.8 % | Predicted Value, Transverse | ||||
15.9 % | Predicted Value, A80 | |||||
17.7 % | Predicted Value, A80 Transverse | |||||
17.7 % | Predicted Value, A200 | |||||
19.7 % | Predicted Value, A50 | |||||
20.4 % | Predicted Value, A5 | |||||
20 °C | 14 % | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2, EN 10083-1 | Bar, wire, Flat, Sheet, Strip, Forging | ||
20 °C | 16 % | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2, EN 10083-1 | Bar, wire, Flat, Sheet, Strip, Forging | ||
Poisson's ratio | 20 °C | 0.281 [-] | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | |
100 °C | 0.281 [-] | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | ||
200 °C | 0.29 [-] | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | ||
300 °C | 0.291 [-] | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | ||
400 °C | 0.295 [-] | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | ||
500 °C | 0.297 [-] | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | ||
Shear modulus | 20 °C | 81 - 82.0 GPa | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | |
20 °C | 81 GPa | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | ||
20 °C | 82.0 GPa | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | ||
100 °C | 80.0 GPa | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | ||
200 °C | 77.1 GPa | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | ||
300 °C | 74.2 GPa | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | ||
400 °C | 70.8 GPa | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | ||
500 °C | 66.7 GPa | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | ||
Tensile strength | 20 °C | 560 MPa | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2, EN 10083-1 | Bar, wire, Flat, Sheet, Strip, Forging | |
20 °C | 580 MPa | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2, EN 10083-1 | Bar, wire, Flat, Sheet, Strip, Forging | ||
20 °C | 620 MPa | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2, EN 10083-1 | Bar, wire, Flat, Sheet, Strip, Forging | ||
Yield strength | 256.5 MPa | Predicted Value, RP1 | ||||
314.3 MPa | Predicted Value, RP1 Transverse | |||||
315.6 MPa | Predicted Value, RP05 | |||||
317.8 MPa | Predicted Value, Transverse | |||||
414.5 MPa | Predicted Value, RP02 | |||||
462.4 MPa | Predicted Value, RP002 | |||||
464.2 MPa | Predicted Value, RP02 Transverse | |||||
20 °C | 275 MPa | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2, EN 10083-1 | Bar, wire, Flat, Sheet, Strip, Forging | ||
20 °C | 305 MPa | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2, EN 10083-1 | Bar, wire, Flat, Sheet, Strip, Forging | ||
20 °C | 340 MPa | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2, EN 10083-1 | Bar, wire, Flat, Sheet, Strip, Forging |
Thermal
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
Coefficient of thermal expansion | -100 °C | 1.08e-05 1/K | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | |
20 °C | 1.19e-05 1/K | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | ||
100 °C | 1.11e-05 - 1.25e-05 1/K | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | ||
100 °C | 1.11e-05 1/K | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | ||
100 °C | 1.25e-05 1/K | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | ||
200 °C | 1.21e-05 - 1.3e-05 1/K | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | ||
200 °C | 1.21e-05 1/K | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | ||
200 °C | 1.3e-05 1/K | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | ||
300 °C | 1.29e-05 - 1.36e-05 1/K | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | ||
300 °C | 1.29e-05 1/K | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | ||
300 °C | 1.36e-05 1/K | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | ||
400 °C | 1.35e-05 - 1.41e-05 1/K | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | ||
400 °C | 1.35e-05 1/K | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | ||
400 °C | 1.41e-05 1/K | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | ||
500 °C | 1.45e-05 1/K | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | ||
600 °C | 1.49e-05 1/K | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | ||
Max service temperature | -25 - 480 °C | normalized or normalized formed (+N) | EN 10083-2, EN 10083-1 | Sheet, Strip, Flat, Bar, Forging | Long | |
500 °C | Typical for Carbon Steel | |||||
Melting point | 1380 - 1514 °C | Typical for Medium Carbon Steel | ||||
Specific heat capacity | -100 °C | 423 J/(kg·K) | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | |
20 °C | 461 J/(kg·K) | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | ||
20 °C | 461 - 480 J/(kg·K) | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | ||
20 °C | 480 J/(kg·K) | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | ||
100 °C | 479 J/(kg·K) | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | ||
100 °C | 479 - 500 J/(kg·K) | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | ||
100 °C | 500 J/(kg·K) | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | ||
200 °C | 499 J/(kg·K) | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | ||
200 °C | 499 - 550 J/(kg·K) | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | ||
200 °C | 550 J/(kg·K) | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | ||
300 °C | 517 J/(kg·K) | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | ||
300 °C | 517 - 590 J/(kg·K) | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | ||
300 °C | 590 J/(kg·K) | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | ||
400 °C | 536 J/(kg·K) | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | ||
500 °C | 558 J/(kg·K) | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | ||
600 °C | 587 J/(kg·K) | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | ||
Thermal conductivity | 20 °C | 41.7 W/(m·K) | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | |
20 °C | 41.7 - 52 W/(m·K) | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | ||
20 °C | 52 W/(m·K) | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | ||
100 °C | 43.4 W/(m·K) | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | ||
100 °C | 43.4 - 50.6 W/(m·K) | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | ||
100 °C | 50.6 W/(m·K) | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | ||
200 °C | 43.2 W/(m·K) | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | ||
200 °C | 43.2 - 48.1 W/(m·K) | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | ||
200 °C | 48.1 W/(m·K) | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | ||
300 °C | 41.4 W/(m·K) | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | ||
300 °C | 41.4 - 45.7 W/(m·K) | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | ||
300 °C | 45.7 W/(m·K) | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | ||
400 °C | 39.1 W/(m·K) | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | ||
500 °C | 36.7 W/(m·K) | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | ||
600 °C | 34.1 W/(m·K) | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | ||
Thermal diffusivity | 20 °C | 11.6 mm²/s | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | |
100 °C | 11.3 mm²/s | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | ||
200 °C | 10.5 mm²/s | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | ||
300 °C | 9.5 mm²/s | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | ||
400 °C | 8.3 mm²/s | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | ||
500 °C | 7.1 mm²/s | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | ||
600 °C | 5.8 mm²/s | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging |
Electrical
| Property | Temperature | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|---|
Electrical resistivity | 20 °C | 1.2e-07 - 2.5e-07 Ω·m | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging |
20 °C | 1.2e-07 Ω·m | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | |
20 °C | 2.5e-07 Ω·m | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | |
100 °C | 2.95e-07 Ω·m | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | |
200 °C | 3.65e-07 Ω·m | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | |
300 °C | 4.53e-07 Ω·m | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | |
400 °C | 5.56e-07 Ω·m | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | |
500 °C | 6.74e-07 Ω·m | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging | |
600 °C | 8.13e-07 Ω·m | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging |
Chemical properties
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Carbon | 0.42 - 0.5 % | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2, EN 10083-1 | Bar, wire, Flat, Sheet, Strip, Forging |
Chromium | 0.4 % | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging |
Copper | 0.3 % | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging |
Manganese | 0.5 - 0.8 % | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2, EN 10083-1 | Bar, wire, Flat, Sheet, Strip, Forging |
Molybdenum | 0.1 % | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging |
Nickel | 0.4 % | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging |
Phosphorus | 0.045 % | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2, EN 10083-1 | Bar, wire, Flat, Sheet, Strip, Forging |
Silicon | 0.1 - 0.4 % | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2 | Bar, wire, Flat, Sheet, Strip, Forging |
0.4 % | normalized or normalized formed (+N) | EN 10083-2, ISO 683-1, EN 10083-1 | Bar, wire, Flat, Sheet, Strip, Forging | |
Sulfur | 0.045 % | normalized or normalized formed (+N) | ISO 683-1, EN 10083-2, EN 10083-1 | Bar, wire, Flat, Sheet, Strip, Forging |
Technological properties
| Property | ||
|---|---|---|
| Supplier Disclaimer | The given information is a rough description and some properties can depend on various factors such as product thickness. Please contact the supplier or refer to the related norm or standard for further information. | |
Metal
- EN 10225 S355G7 Steel – Normalized or Normalized Formed (N) for Superior Workability and Weldability
- EN 10225 S355G8 Steel – Normalized or Normalized-Formed (+N) Grade
- DIN 2394-2: Grade St 28 Steel – Normalized & Normalized Formed (+N) Properties
- EN 10297-1 Grade C45: Normalized & Normalized Formed Steel Properties
- DIN 17200 Grade C45 – Normalized or Normalized‑Formed Steel for Automotive & Machinery Applications
- ISO 683-1 Grade C22E – Normalized & Normalized Formed Steel for Heavy Forged Parts
- ISO 683-1 Grade C45E: Normalized & Formed Steel for Heavy‑Duty Applications
- EN 10216-2 Grade St 45.8: High‑Temperature Normalized Tube Steel (+N) for Seamless Tubes
- EN 10217-2 Grade St 37.8: High‑Temperature Normalized Tube Steel for Industrial Use
- EN 10217‑2 Grade St 42.8 Tube Steel – High‑Temperature Normalized Formed for Vessels & Petrochemical Use