DIN 1623-2 Grade S325G: Skin‑Passed, High‑Grade Steel Ready for Coating

The structural steel S325G (unalloyed high-grade steel) will be supplied as cold rolled (usually skin passed and oiled) flat product (sheet and strip) without coating up to thicknesses of 3 mm. The weldability is given for commonon procedures. The suitability for coatings is given.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.83 g/cm³

Mechanical

PropertyTemperatureValueComment

Elastic modulus

-100.0 °C

217 GPa

20.0 °C

212 GPa

100.0 °C

207 GPa

200.0 °C

199 GPa

300.0 °C

192 GPa

400.0 °C

184 GPa

500.0 °C

175 GPa

600.0 °C

164 GPa

Elongation A80, transverse

20.0 °C

16 %

Poisson's ratio

23.0 °C

0.29 [-]

Typical for Low Carbon Steel

Shear modulus

23.0 °C

82 GPa

Typical for Low Carbon Steel

Tensile strength, transverse

20.0 °C

510 - 680 MPa

Yield strength Rp0.2, transverse

20.0 °C

325 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1.08E-5 1/K

20.0 °C

1.19E-5 1/K

100.0 °C

1.25E-5 1/K

200.0 °C

1.3E-5 1/K

300.0 °C

1.36E-5 1/K

400.0 °C

1.41E-5 1/K

500.0 °C

1.45E-5 1/K

600.0 °C

1.49E-5 1/K

Max service temperature

500 °C

Typical for Carbon Steel

Max service temperature, long

0 - 300 °C

Melting point

1480 - 1526 °C

Typical for Low Carbon Steel

Specific heat capacity

-100.0 °C

423 J/(kg·K)

20.0 °C

461 J/(kg·K)

100.0 °C

479 J/(kg·K)

200.0 °C

499 J/(kg·K)

300.0 °C

517 J/(kg·K)

400.0 °C

536 J/(kg·K)

500.0 °C

558 J/(kg·K)

600.0 °C

587 J/(kg·K)

Thermal conductivity

-100.0 °C

37.6 W/(m·K)

20.0 °C

42.2 W/(m·K)

100.0 °C

43.2 W/(m·K)

200.0 °C

42.9 W/(m·K)

300.0 °C

41.2 W/(m·K)

400.0 °C

39.1 W/(m·K)

500.0 °C

36.6 W/(m·K)

600.0 °C

34.1 W/(m·K)

Thermal diffusivity

-100.0 °C

12.9 mm²/s

20.0 °C

11.7 mm²/s

100.0 °C

11.2 mm²/s

200.0 °C

10.3 mm²/s

300.0 °C

9.4 mm²/s

400.0 °C

8.3 mm²/s

500.0 °C

7.1 mm²/s

600.0 °C

5.7 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

-100.0 °C

1.82E-7 Ω·m

20.0 °C

2.47E-7 Ω·m

100.0 °C

2.96E-7 Ω·m

200.0 °C

3.68E-7 Ω·m

300.0 °C

4.55E-7 Ω·m

400.0 °C

5.56E-7 Ω·m

500.0 °C

6.75E-7 Ω·m

600.0 °C

8.13E-7 Ω·m

Magnetic

PropertyValueComment

Curie temperature

770 °C

Typical for Low Carbon Steel

Chemical properties

PropertyValue

Carbon

0.2 %

Manganese

1.6 %

Phosphorus

0.03 %

Silicon

0.55 %

Sulfur

0.025 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. DIN 1654-5 Grade X3CrNiCu18-9 Stainless Steel – Cold‑Drawn, Quenched & Slightly Skinned for Superior Performance
    2. DIN 5512-2 Grade DC01: Skin Passed – Compliance Confirmed
    3. EN 10268 Grade H240LA Skin Pass – High‑Tensile, Cold‑Formable Steel
    4. DIN 5512-2 Grade St 52-3 G Skin Approved – Optimal for Rail and Container Engineering
    5. EN 10268 Grade H280LA: Premium Micro-Alloyed Steel for Automotive & Construction
    6. EN 10268 H320LA Steel – Certified High‑Tensile, Lightweight, and Formable
    7. EN 10268 Grade H360LA Steel: Skin Test Passed & Certified
    8. EN 10268 Grade H400LA: Certified High-Strength Steel for Automotive & Construction
    9. DIN 1623‑2 Grade S215G: Skin‑Passed, Cold‑Rolled Steel for High Performance
    10. DIN 1623-2 S245G Structural Steel – Skin‑Passed, Cold‑Rolled Quality