EN 10312 X3CrNiMo17-13-3: Heat‑Treated & Quenched Grade for Corrosion‑Resistant Applications

The material X3CrNiMo17-13-3 has a similar corrosion resistance like 1.4401. It shows slightly improved resistance to selective corrosion due to the higher Mo-content. The material is in delivery condition resistant to intercrystalline corrosion. Application for acid resistant apparatus in chemical and pharmaceutical industry, cellulose, color, fatty acid, textile and rayon industry, petrochemistry. The welding method for the tube manufacturing is up to the producer.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

8.01 g/cm³

Mechanical

PropertyTemperatureValueComment

Elastic modulus

-100.0 °C

206 GPa

20.0 °C

196 GPa

100.0 °C

190 GPa

200.0 °C

182 GPa

300.0 °C

174 GPa

400.0 °C

166 GPa

500.0 °C

158 GPa

600.0 °C

150 GPa

700.0 °C

142 GPa

800.0 °C

134 GPa

Elongation

20.0 °C

40 %

Elongation, transverse

20.0 °C

35 %

Poisson's ratio

23.0 °C

0.3 [-]

Typical for Austenitic Stainless Steel

Shear modulus

23.0 °C

77 GPa

Typical for Austenitic Stainless Steel

Tensile strength

20.0 °C

510 - 710 MPa

Tensile strength, transverse

20.0 °C

510 - 710 MPa

Yield strength

20.0 °C

205 MPa

Yield strength Rp0.2

50.0 °C

196 MPa

100.0 °C

177 MPa

150.0 °C

162 MPa

200.0 °C

147 MPa

250.0 °C

137 MPa

300.0 °C

127 MPa

350.0 °C

120 MPa

400.0 °C

115 MPa

450.0 °C

112 MPa

500.0 °C

110 MPa

550.0 °C

108 MPa

Yield strength Rp1.0

20.0 °C

240 MPa

50.0 °C

230 MPa

100.0 °C

211 MPa

150.0 °C

191 MPa

200.0 °C

177 MPa

250.0 °C

167 MPa

300.0 °C

156 MPa

350.0 °C

150 MPa

400.0 °C

144 MPa

450.0 °C

141 MPa

500.0 °C

139 MPa

550.0 °C

137 MPa

Yield strength Rp1.0, transverse

20.0 °C

240 MPa

Yield strength, transverse

20.0 °C

205 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1.49E-5 1/K

20.0 °C

1.61E-5 1/K

100.0 °C

1.67E-5 1/K

200.0 °C

1.72E-5 1/K

300.0 °C

1.77E-5 1/K

400.0 °C

1.81E-5 1/K

500.0 °C

1.84E-5 1/K

600.0 °C

1.88E-5 1/K

700.0 °C

1.91E-5 1/K

800.0 °C

1.94E-5 1/K

900.0 °C

1.97E-5 1/K

1000.0 °C

2E-5 1/K

Melting point

1230 - 1480 °C

Typical for Austenitic Stainless Steel

Specific heat capacity

-100.0 °C

440 J/(kg·K)

20.0 °C

472 J/(kg·K)

100.0 °C

487 J/(kg·K)

200.0 °C

503 J/(kg·K)

300.0 °C

512 J/(kg·K)

400.0 °C

520 J/(kg·K)

500.0 °C

530 J/(kg·K)

600.0 °C

541 J/(kg·K)

700.0 °C

551 J/(kg·K)

800.0 °C

559 J/(kg·K)

900.0 °C

565 J/(kg·K)

1000.0 °C

571 J/(kg·K)

Thermal conductivity

20.0 °C

13.5 W/(m·K)

100.0 °C

14.9 W/(m·K)

200.0 °C

16.7 W/(m·K)

300.0 °C

18.3 W/(m·K)

400.0 °C

19.8 W/(m·K)

500.0 °C

21.3 W/(m·K)

600.0 °C

22.7 W/(m·K)

700.0 °C

24.2 W/(m·K)

800.0 °C

25.6 W/(m·K)

Thermal diffusivity

20.0 °C

3.6 mm²/s

100.0 °C

3.7 mm²/s

200.0 °C

4 mm²/s

300.0 °C

4.4 mm²/s

400.0 °C

4.6 mm²/s

500.0 °C

4.7 mm²/s

600.0 °C

4.9 mm²/s

700.0 °C

5.2 mm²/s

800.0 °C

5.5 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

7.75E-7 Ω·m

100.0 °C

8.42E-7 Ω·m

200.0 °C

9.04E-7 Ω·m

300.0 °C

9.62E-7 Ω·m

400.0 °C

1.01E-6 Ω·m

500.0 °C

1.06E-6 Ω·m

600.0 °C

1.1E-6 Ω·m

700.0 °C

1.13E-6 Ω·m

800.0 °C

1.16E-6 Ω·m

Chemical properties

PropertyValue

Carbon

0.05 %

Chromium

16.5 - 18.5 %

Manganese

2 %

Molybdenum

2.5 - 3 %

Nickel

10.5 - 13 %

Nitrogen

0.11 %

Phosphorus

0.05 %

Silicon

1 %

Sulfur

0.015 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. SEW 395 Grade GX12CrNi18-11: High‑Performance Austenitic Steel, Heat‑Treated & Quenched
    2. EN 10213-4 Grade GX2CrNi19-11 – High‑Performance Austenitic Stainless Steel, Solution Heat‑Treated & Quenched
    3. EN 10213-4 Grade GX2CrNiMo19-11-2: Solution Heat‑Treated & Quenched Austenitic Stainless Steel for Pressure Vessels
    4. EN 10213-4 Grade GX2NiCrMo28-20-2 – Premium Solution‑Heat Treated Stainless Steel for Pressure Vessels
    5. EN 10213-4 Grade GX5CrNiMoNb19-11-2: Heat‑Treated, Quenched, Corrosion‑Resistant Austenitic Steel
    6. EN 10213-4 Grade GX5CrNi19-10 – Heat-Treated and Quenched Austenitic Stainless Steel
    7. EN 10213-4 Grade GX5CrNiMo19-11-2: High‑Performance Solution Heat‑Treated and Quenched Steel for Chemical & Textile Industries
    8. GX5CrNiNb19-11: Heat-Treated, Quenched Grade for High-Performance Cast Parts & Industrial Applications
    9. EN 10312 Grade X2CrNiMo17-12-2 – High‑Performance Heat‑Treated and Quenched Stainless Steel
    10. DIN 17456 X3CrNiMo17-13-3 – Heat‑Treated, Quenched Stainless Steel with Superior Corrosion Resistance