EN 10028-7 X2CrNiMoN17-11-2 Solution-Annealed Steel (+AT) – High Strength, Corrosion Resistance, and Oxidation Stability

The austenitic steel X2CrNiMoN17-11-2 shows a higher strength and structural stability by N-addition. High resistance in oxidizing media. Increase of interaction parameter (pitting index) by N-addition. The steel is suitable for mirror-polishing and resistant to selective attack. It shows favorable corrosion resistance especially in welded condition. The material shows resistance to intercrystalline corrosion also in sensitized condition. Application: in chemical apparatus engineering for pressure vessels, in cellulose, coloring, oil, soap and textile industry, in breweries and dairies

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.96 - 8 g/cm³

Mechanical

PropertyTemperatureValueComment

Elastic modulus

-100.0 °C

206 GPa

20.0 °C

196 - 200 GPa

100.0 °C

190 - 194 GPa

200.0 °C

182 - 186 GPa

300.0 °C

174 - 179 GPa

400.0 °C

166 - 172 GPa

500.0 °C

158 - 165 GPa

600.0 °C

150 GPa

700.0 °C

142 GPa

800.0 °C

134 GPa

900.0 °C

127 GPa

1000.0 °C

120 GPa

Elongation

-196.0 °C

30 %

-150.0 °C

35 %

-80.0 °C

35 %

20.0 °C

40 %

Elongation A80, transverse

20.0 °C

40 %

Elongation, transverse

20.0 °C

40 %

Poisson's ratio

23.0 °C

0.3 [-]

Typical for Austenitic Stainless Steel

Shear modulus

23.0 °C

77 GPa

Typical for Austenitic Stainless Steel

Tensile strength

-196.0 °C

1150 MPa

-150.0 °C

1000 MPa

-80.0 °C

800 MPa

20.0 °C

580 - 780 MPa

50.0 °C

557 MPa

100.0 °C

520 MPa

150.0 °C

490 MPa

200.0 °C

460 MPa

250.0 °C

450 MPa

300.0 °C

440 MPa

350.0 °C

435 MPa

Tensile strength, transverse

20.0 °C

580 - 780 MPa

Yield strength Rp0.2

-196.0 °C

600 MPa

-150.0 °C

500 MPa

-80.0 °C

380 MPa

20.0 °C

280 MPa

50.0 °C

254 MPa

100.0 °C

211 MPa

150.0 °C

185 MPa

200.0 °C

167 MPa

250.0 °C

155 MPa

300.0 °C

145 MPa

350.0 °C

140 MPa

400.0 °C

135 MPa

450.0 °C

131 MPa

500.0 °C

128 MPa

550.0 °C

127 MPa

Yield strength Rp0.2, transverse

20.0 °C

280 - 300 MPa

Yield strength Rp1.0

-196.0 °C

700 MPa

-150.0 °C

600 MPa

-80.0 °C

450 MPa

20.0 °C

320 MPa

50.0 °C

292 MPa

100.0 °C

246 MPa

150.0 °C

218 MPa

200.0 °C

198 MPa

250.0 °C

183 MPa

300.0 °C

175 MPa

350.0 °C

169 MPa

400.0 °C

164 MPa

450.0 °C

160 MPa

500.0 °C

158 MPa

550.0 °C

157 MPa

Yield strength Rp1.0, transverse

20.0 °C

320 - 330 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1.49E-5 1/K

20.0 °C

1.61E-5 1/K

100.0 °C

1.6E-5 - 1.67E-5 1/K

200.0 °C

1.65E-5 - 1.72E-5 1/K

300.0 °C

1.7E-5 - 1.77E-5 1/K

400.0 °C

1.75E-5 - 1.81E-5 1/K

500.0 °C

1.8E-5 - 1.84E-5 1/K

600.0 °C

1.88E-5 1/K

700.0 °C

1.91E-5 1/K

800.0 °C

1.94E-5 1/K

900.0 °C

1.97E-5 1/K

1000.0 °C

2E-5 1/K

Melting point

1230 - 1480 °C

Typical for Austenitic Stainless Steel

Specific heat capacity

-100.0 °C

440 J/(kg·K)

20.0 °C

472 - 500 J/(kg·K)

100.0 °C

487 J/(kg·K)

200.0 °C

503 J/(kg·K)

300.0 °C

512 J/(kg·K)

400.0 °C

520 J/(kg·K)

500.0 °C

530 J/(kg·K)

600.0 °C

541 J/(kg·K)

700.0 °C

551 J/(kg·K)

800.0 °C

559 J/(kg·K)

900.0 °C

565 J/(kg·K)

1000.0 °C

571 J/(kg·K)

Thermal conductivity

20.0 °C

13.3 - 15 W/(m·K)

100.0 °C

14.9 W/(m·K)

200.0 °C

16.5 W/(m·K)

300.0 °C

18.1 W/(m·K)

400.0 °C

19.5 W/(m·K)

500.0 °C

21 W/(m·K)

600.0 °C

22.4 W/(m·K)

700.0 °C

23.8 W/(m·K)

800.0 °C

25.2 W/(m·K)

Thermal diffusivity

20.0 °C

3.5 mm²/s

100.0 °C

3.8 mm²/s

200.0 °C

4 mm²/s

300.0 °C

4.3 mm²/s

400.0 °C

4.5 mm²/s

500.0 °C

4.7 mm²/s

600.0 °C

4.8 mm²/s

700.0 °C

5.1 mm²/s

800.0 °C

5.4 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

7.5E-7 - 7.91E-7 Ω·m

100.0 °C

8.45E-7 Ω·m

200.0 °C

9.19E-7 Ω·m

300.0 °C

9.77E-7 Ω·m

400.0 °C

1.03E-6 Ω·m

500.0 °C

1.08E-6 Ω·m

600.0 °C

1.12E-6 Ω·m

700.0 °C

1.15E-6 Ω·m

800.0 °C

1.18E-6 Ω·m

Chemical properties

PropertyValue

Carbon

0.03 %

Chromium

16.5 - 18.5 %

Manganese

2 %

Molybdenum

2 - 2.5 %

Nickel

10 - 12.5 %

Nitrogen

0.12 - 0.22 %

Phosphorus

0.05 %

Silicon

1 %

Sulfur

0.015 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. EN 10028-7 Grade X2CrTi17 – Solution-Annealed Ferritic Stainless Steel for Automotive, Electrical, and Household Use
    2. X3CrTi17 Ferritic Steel – EN 10028-7 Grade, Solution Annealed (+AT) – Superior Corrosion Resistance
    3. EN 10028-7 Grade X2CrMoTi18-2: Solution-Annealed Ferritic Steel (+AT) – Superior Corrosion Resistance & Cold Forming
    4. EN 10028-7 Grade X2CrNi12: Solution-Annealed Steel with Superior Corrosion Resistance
    5. EN 10222-5 Grade X2CrNiMoN17-11-2 – Solution Annealed Steel with Enhanced Corrosion Resistance
    6. EN 10250-4 X2CrNiMoN17-11-2 Solution-Annealed Steel for High-Performance Chemical Applications
    7. EN 10028-7 Grade X6CrNi23-13 Solution Annealed Steel – High-Temperature Resistant Alloy
    8. EN 10028-7 Grade X6CrNi25-20: Solution-Annealed Austenitic Steel for High-Temperature Applications
    9. EN 10028-7 X1CrNiMoCuN20-18-7 Solution‑Annealed Steel (AT) – Premium Corrosion Resistance
    10. EN 10028-7 X2CrNiMoN17-11-2 Solution-Annealed Steel (+AT) – High Strength, Corrosion Resistance, and Oxidation Stability