EN 10088‑1 X2CrNiMo18‑15‑4: Solution‑Annealed, High‑Molybdenum Stainless Steel (+AT)

Material X2CrNiMo18-15-4 is comparable to X 2 CrNiMo 18 16 4 acc. to DIN 17440 : 1985-07. The steel shows due to its high molybdenum content (above 3 per cent) very good resistance to non oxidizing and halogenated media. It is resistant to intercrystalline corrosion also in sensitized condition. This material is suitable for mirror finishing and cold formable. Application in chemical apparatus engineering, especially in cellulose industry, in textile and rayon industry as well as in tankship construction.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

8 - 8.01 g/cm³

Mechanical

PropertyTemperatureValue

Elastic modulus

-100.0 °C

206 GPa

20.0 °C

196 - 200 GPa

100.0 °C

190 - 194 GPa

200.0 °C

182 - 186 GPa

300.0 °C

174 - 179 GPa

400.0 °C

166 - 172 GPa

500.0 °C

158 - 165 GPa

600.0 °C

150 GPa

700.0 °C

142 GPa

800.0 °C

134 GPa

Elongation

20.0 °C

40 %

Elongation A80, transverse

20.0 °C

35 - 40 %

Elongation, transverse

20.0 °C

30 - 40 %

Hardness, Brinell

20.0 °C

215 [-]

Hardness, Brinell, trans

20.0 °C

215 [-]

Poisson's ratio

20.0 °C

0.28 [-]

Shear modulus

20.0 °C

77.3 GPa

Tensile strength

20.0 °C

500 - 700 MPa

Tensile strength, transverse

20.0 °C

500 - 720 MPa

Yield strength Rp0.2

20.0 °C

200 MPa

100.0 °C

172 MPa

150.0 °C

157 MPa

200.0 °C

147 MPa

250.0 °C

137 MPa

300.0 °C

127 MPa

350.0 °C

120 MPa

400.0 °C

115 MPa

450.0 °C

112 MPa

500.0 °C

110 MPa

550.0 °C

108 MPa

Yield strength Rp0.2, transverse

20.0 °C

200 - 240 MPa

Yield strength Rp1.0

20.0 °C

235 MPa

100.0 °C

206 MPa

150.0 °C

186 - 188 MPa

200.0 °C

177 MPa

250.0 °C

167 MPa

300.0 °C

156 - 157 MPa

350.0 °C

148 - 150 MPa

400.0 °C

144 MPa

450.0 °C

140 MPa

500.0 °C

138 MPa

550.0 °C

136 MPa

Yield strength Rp1.0, transverse

20.0 °C

235 - 270 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1.49E-5 1/K

20.0 °C

1.61E-5 1/K

100.0 °C

1.6E-5 - 1.67E-5 1/K

200.0 °C

1.65E-5 - 1.72E-5 1/K

300.0 °C

1.7E-5 - 1.77E-5 1/K

400.0 °C

1.75E-5 - 1.81E-5 1/K

500.0 °C

1.8E-5 - 1.84E-5 1/K

600.0 °C

1.88E-5 1/K

700.0 °C

1.91E-5 1/K

800.0 °C

1.94E-5 1/K

900.0 °C

1.97E-5 1/K

1000.0 °C

2E-5 1/K

Melting point

1230 - 1480 °C

Typical for Austenitic Stainless Steel

Specific heat capacity

-100.0 °C

440 J/(kg·K)

20.0 °C

472 - 500 J/(kg·K)

100.0 °C

487 J/(kg·K)

200.0 °C

503 J/(kg·K)

300.0 °C

512 J/(kg·K)

400.0 °C

520 J/(kg·K)

500.0 °C

530 J/(kg·K)

600.0 °C

541 J/(kg·K)

700.0 °C

551 J/(kg·K)

800.0 °C

559 J/(kg·K)

900.0 °C

565 J/(kg·K)

1000.0 °C

571 J/(kg·K)

Thermal conductivity

20.0 °C

13.5 - 14 W/(m·K)

100.0 °C

14.9 W/(m·K)

200.0 °C

16.7 W/(m·K)

300.0 °C

18.3 W/(m·K)

400.0 °C

19.8 W/(m·K)

500.0 °C

21.3 W/(m·K)

600.0 °C

22.7 W/(m·K)

700.0 °C

24.2 W/(m·K)

800.0 °C

25.6 W/(m·K)

Thermal diffusivity

20.0 °C

3.6 mm²/s

100.0 °C

3.7 mm²/s

200.0 °C

4 mm²/s

300.0 °C

4.4 mm²/s

400.0 °C

4.6 mm²/s

500.0 °C

4.7 mm²/s

600.0 °C

4.9 mm²/s

700.0 °C

5.2 mm²/s

800.0 °C

5.5 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

7.75E-7 - 8.5E-7 Ω·m

100.0 °C

8.42E-7 Ω·m

200.0 °C

9.04E-7 Ω·m

300.0 °C

9.62E-7 Ω·m

400.0 °C

1.01E-6 Ω·m

500.0 °C

1.06E-6 Ω·m

600.0 °C

1.1E-6 Ω·m

700.0 °C

1.13E-6 Ω·m

800.0 °C

1.16E-6 Ω·m

Chemical properties

PropertyValue

Carbon

0.03 %

Chromium

17.5 - 19.5 %

Manganese

2 %

Molybdenum

3 - 4 %

Nickel

13 - 16 %

Nitrogen

0.11 %

Phosphorus

0.05 %

Silicon

1 %

Sulfur

0.015 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. Grade X3CrNiCuMo17-11-3-2 Austenitic Steel – EN 10088-1, Solution Annealed + AT
    2. EN 10088-1 X3CrNiCu19-9-2 Austenitic Steel – Solution Annealed for Superior Corrosion Resistance
    3. EN 10088-1 X6CrNiCuS18-9-2 – Solution Annealed Austenitic Steel for Rods & Wire Rods
    4. EN 10088-1 Grade X7CrNiAl17-7: Solution-Annealed Stainless Steel with Enhanced Performance
    5. EN 10088-1 Grade X3CrNiMoN27-5-2: Solution‑Annealed (AT) – High‑Performance Ferritic Austenitic Steel
    6. EN 10088‑1 X3CrNiCu18‑9‑4 Austenitic Stainless Steel – Solution Annealed & AT Certified
    7. X2CrNiMoN25-7-4 Solution-Annealed Stainless Steel – EN 10088‑1 Grade X2
    8. EN 10088-1 X2CrNiMoCuWN25-7-4: Solution‑Annealed Alloy for Superior Corrosion Resistance
    9. X2CrNiMo18-15-4 Austenitic Steel – Solution Annealed, High Corrosion Resistance, Ideal for Welded Tubes
    10. EN 10088-1 Grade X2CrNiMoN18-12-4: High-Performance Solution-Annealed Stainless Steel (+AT)