AW-1080A F: Premium Food‑Safe Aluminum Grade EN 573‑3
Food safe aluminum.
Properties
General
| Property | Temperature | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|---|
Density | 2.7 g/cm³ | F | EN 573-3, EN 1715-3, EN 1715-4, EN 485, EN 570 | Strip, Sheet, Plate, Wire | |
20.0 °C | 2.7 g/cm³ | F | EN 573-3 | Flat |
Mechanical
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
Elastic modulus | -270.0 °C | 70.0 GPa | F | EN 573-3 | Flat | |
70.0 GPa | F | EN 573-3, EN 1715-3, EN 1715-4, EN 485, EN 570 | Strip, Sheet, Plate, Wire | |||
20.0 °C | 60.0 - 70.0 GPa | F | EN 573-3 | Flat | ||
20.0 °C | 70.0 GPa | F | EN 573-3 | Flat | ||
50.0 °C | 69.0 GPa | F | EN 573-3 | Flat | ||
100.0 °C | 68.0 GPa | F | EN 573-3 | Flat | ||
150.0 °C | 66.0 GPa | F | EN 573-3 | Flat | ||
200.0 °C | 63.0 GPa | F | EN 573-3 | Flat | ||
250.0 °C | 57.0 GPa | F | EN 573-3 | Flat | ||
300.0 °C | 50.0 GPa | F | EN 573-3 | Flat | ||
Hardness, Brinell | 18.0 [-] | F | EN 573-3, EN 485 | Strip, Sheet, Plate, Wire | ||
19.0 [-] | F | EN 573-3, EN 570 | Strip, Sheet, Plate, Wire | |||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 1000 Series Aluminium | ||||
Poisson's ratio | 0.33 [-] | Typical for Wrought 1000 Series Aluminium | ||||
Shear modulus | 20.0 °C | 25.0 GPa | F | EN 573-3 | Flat | |
Tensile strength | 60.0 MPa | F | EN 573-3, EN 485 | Strip, Sheet, Plate, Wire | ||
80.0 - 110.0 MPa | F | EN 573-3, EN 1715-3, EN 1715-4 | Strip, Sheet, Plate, Wire | |||
20.0 °C | 60.0 MPa | F | EN 573-3 | Flat | Transverse | |
20.0 °C | 60.0 MPa | F | EN 573-3 | Flat |
Thermal
| Property | Temperature | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|---|
Coefficient of thermal expansion | 20 °C | 2.35e-05 1/K | F | EN 573-3, EN 1715-3, EN 1715-4, EN 485, EN 570 | Strip, Sheet, Plate, Wire |
100 °C | 2.35e-05 1/K | F | EN 573-3, EN 1715-3, EN 1715-4, EN 485, EN 570 | Strip, Sheet, Plate, Wire | |
Melting point | 659.0 °C | F | EN 573-3, EN 1715-3, EN 1715-4, EN 485, EN 570 | Strip, Sheet, Plate, Wire | |
Specific heat capacity | 20.0 °C | 921.0 J/(kg·K) | F | EN 573-3 | Flat |
Thermal conductivity | 225 W/(m·K) | F | EN 573-3, EN 1715-3, EN 1715-4, EN 485, EN 570 | Strip, Sheet, Plate, Wire | |
20.0 °C | 215.0 W/(m·K) | F | EN 573-3 | Flat |
Electrical
| Property | Temperature | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|---|
Electrical conductivity | 34500000.0 - 35000000.0 S/m | F | EN 573-3, EN 1715-3, EN 1715-4, EN 485, EN 570 | Strip, Sheet, Plate, Wire | |
20.0 °C | 36400000.0 - 37000000.0 S/m | F | EN 573-3 | Flat | |
Electrical resistivity | 2.86e-08 - 2.9e-08 Ω·m | F | EN 573-3, EN 1715-3, EN 1715-4, EN 485, EN 570 | Strip, Sheet, Plate, Wire |
Chemical properties
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Aluminium | 99.8 % | F | EN 573-3, EN 1715-3, EN 1715-4, EN 485, EN 570 | Flat, Strip, Sheet, Plate, Wire |
Copper | 0.03 % | F | EN 573-3, EN 1715-3, EN 1715-4, EN 485, EN 570 | Flat, Strip, Sheet, Plate, Wire |
Gallium | 0.03 % | F | EN 573-3, EN 1715-3, EN 1715-4, EN 485, EN 570 | Flat, Strip, Sheet, Plate, Wire |
Iron | 0.15 % | F | EN 573-3 | Flat |
0.15 % | F | EN 573-3, EN 1715-3, EN 1715-4, EN 485, EN 570 | Strip, Sheet, Plate, Wire | |
Magnesium | 0.02 % | F | EN 573-3, EN 1715-3, EN 1715-4, EN 485, EN 570 | Flat, Strip, Sheet, Plate, Wire |
Manganese | 0.02 % | F | EN 573-3, EN 1715-3, EN 1715-4, EN 485, EN 570 | Flat, Strip, Sheet, Plate, Wire |
Silicon | 0.15 % | F | EN 573-3, EN 1715-3, EN 1715-4, EN 485, EN 570 | Flat, Strip, Sheet, Plate, Wire |
Titanium | 0.02 % | F | EN 573-3, EN 1715-3, EN 1715-4, EN 485, EN 570 | Flat, Strip, Sheet, Plate, Wire |
Zinc | 0.06 % | F | EN 573-3, EN 1715-3, EN 1715-4, EN 485, EN 570 | Flat, Strip, Sheet, Plate, Wire |
Technological properties
| Property | ||
|---|---|---|
| Anodizing | decorative: very good, Protective: very good | |
| Brazing | hard brazing (with flux/ without flux): very good / very good, friction soldering: very good, soft brazing with flux: very good | |
| Workability | Bending / Spinning (cold): very good / very good, Impact extrusion (cold): very good, Deep drawing / upsetting (Condition) very good (H14) / very good (H12) | |
Metal
- EN 573-3 Grade 3.0515 O3 – Key Mechanical & Thermal Properties
- AW-4043A O3 – EN 573-3 Certified 4000 Series Aluminium
- EN 573-3 Grade AW-4047A O3 Aluminium Alloy Specifications
- EN 573-3 AW-5556A F – High-Performance 5000 Series Aluminium Alloy
- EN 573-3 Certified AW-5556A O3 Aluminum Grade
- EN 573-3 AW‑5087 F Aluminum Grade: Key Properties & Standards
- AW-5087 O3 Aluminium Alloy – EN 573-3 Certified Properties
- AW-1110F Aluminium Grade – EN 573-3 Compliance & Properties
- EN 573-3 Grade AW-1198: Food‑Safe Aluminum with Superior Strength and Toughness
- AW-6060 F Aluminium Alloy – EN 573-3 Certified Grade