3S144 is a British aerospace grade, precipitation hardenable stainless steel. It is widely used in the aerospace industry benefiting from a combination of strength and moderate corrosion resistance. BS S143 and BS S145 are chemically identical. S144 is supplied in bar form with heat treatment applie

Very tempering resistant Cr-Mo-V-alloyed universal applicable hot working steel with excellent low sensitivity to alternate temperatures, good sinkability and good water coolable. Application: liquid cooled forging and pressing tools for the steel and non ferrous metal forming, diecasting tools for

Very tough Mo-V-alloyed high speed steel with good cut accuracy and hot hardness. Application: cutter, spiral drills, tapper, saw toothsPropertiesGeneralPropertyTemperatureValueDensity20.0 °C8.12 g/cm³MechanicalPropertyTemperatureValueCommentElastic modulus20.0 °C224 GPa100.0 °C220 GPa200.0 °C214 GP

CuZn40 (CW509L) is an unhardenable wrought alloy. High hardness and strength parameter are achievable by cold forming only. Thermal and electrical conductivity are lower than for CuZn37. Corrosion resistance is similar to pure copper. Processing properties: warm forming: very good cold forming: goo

Steel 20NiCrMoS-2 is suitable for parts in vehicle manufacturing and machine engineering, which are wear loaded at mean core strength, high ductiltity and fatigue strength (e.g gear wheels, shafts, axles).It shows an enhanced workability.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.84 -

Steel 22CrMoS3-5 is suitable for parts in vehicle manufacturing and machine engineering, which are wear loaded at mean core strength, high ductility and fatigue strength and show an enhanced workability (gear wheels, axles, shafts).PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.83 - 7.85 g

CuZn10 (CW501L) is an unhardenable wrought alloy. High hardness and strength parameter are achievable by cold forming only. Thermal conductivity is lower than for CuZn5. Favorable electrical conductivity. Corrosion resistance is similar to pure copper. Processing properties: warm forming: moderatel

The steel 20 MoCrS 4 is used for wear loaded parts in the vehicle and mechanical engineering with medium core strength, better machinability, high toughness and high fatigue strength (e.g. gears, shafts, axles). The lowest application amounts to -60 °C, the best application up to 60 mm nominal size.

102Cr6 is an oil-hardening tool steel. It achieves at least 60 HRC in hardened condition. The steel is particularly ductile and wear resistant. Application: smaller up to medium cutting tools, pressure and beading rolls, shear and roll shear cutter, cold roller, drawing mandrels, thread tools, wood

Material X6CrNiNb18-10 is comparable to X 6 CrNiNb 18 10 acc. to DIN 17440: 1985-07. Its corrosion properties are comparable to 1.4541. The steel is resistant to intercrystalline corrosion also in sensitized condition, but it shows heat-crack susceptibility under certain welding conditions. Widely a

The steel 20 Cr 4 is used for high wear loaded parts in the vehicle and mechanical engineering (e.g. camshafts, piston pins, cylinder). The lowest application amounts to -25 °C, the best application up to 25 mm nominal size.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.83 - 7.85 g/cm³Mech

Cu-DHP, mat. No CW021A, is a deoxidized copper with low phosphorus-content. To the comparable DIN-mark SF-Cu, mat. No 2.0070 acc. to DIN 1787: 1973-01 (precondition for the comparability: Cu-content min. 99,95%, deoxidation agent phosphorus) applies: The material is also available in a special quali

The steel 21 NiCrMoS 2 is used for wear loaded parts in the vehicle and mechanical engineering with medium core strength, better machinability, high toughness and high fatigue strength (e.g. gears, shafts, axles). The lowest application amounts to -60 degrees C, the best application up to 60 mm nomi

The steel 20 CrS 4 is used for high wear loaded and better machinable parts in the vehicle and mechanical engineering (e.g. camshafts, piston pins, gears). The lowest application amounts to -25 °C, the best application from 5 to 10 mm nominal size.PropertiesGeneralPropertyTemperatureValueDensity20.0

The steel 21 NiCrMo 2 respectively 23 NiCrMo 2 is used for wear loaded parts in the vehicle and mechanical engineering with medium core strength, high toughness and high fatigue strength (e.g. gears, shafts, axles). The lowest application amounts to -60 degrees C, the best application up to 60 mm no

TH 50, mat. No 1.0371, is a single cold rolled band (black plate in coils) of soft unalloyed steel and in the surface qualities plain, stone finish and matt for conventional packaging sheet, hardness HR30T m max. 52. The band is produced in thicknesses of 0,17 to 0,49 mm in steps of 0,005 mm. The su

Molybdenum alloyed martensitic-austenitic (nickel martensitic) corrosion resisting steel.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.58 - 7.7 g/cm³MechanicalPropertyTemperatureValueCommentElastic modulus20.0 °C200 - 218 GPa100.0 °C195 - 213 GPa200.0 °C185 - 206 GPa300.0 °C175 - 198 GPa4

DD12 AM FCE for cold forming and deep drawing applications are characterised by guaranteed maximum yield and tensile strength and minimum elongation.PropertiesGeneralPropertyValueCommentCarbon equivalent (CEV)0.18 [-]max.DimensionPropertyValueDimensionsPlease feel free to check the figure on the rig

DD11 AM FCE for cold forming and deep drawing applications is characterised by guaranteed maximum yield and tensile strength and minimum elongation.PropertiesGeneralPropertyValueCommentCarbon equivalent (CEV)0.19 [-]max.DimensionPropertyValueDimensionsPlease feel free to check the figure on the righ

Alloy 10 from Materion Performance Alloys provides high electrical and thermal conductivity coupled with moderate strength.PropertiesGeneralPropertyTemperatureValueDensity23.0 °C8.83 g/cm³MechanicalPropertyTemperatureValueElastic modulus23.0 °C138 GPaElongation23.0 °C10 - 25 %Hardness, Rockwell B23.