EN 10250-4 Grade X17CrNi16-2 Soft-Annealed Steel (+A) – Premium Corrosion Resistance & Wear Performance
The make X17CrNi16-2 is comparable to X 20 CrNi 17-2 acc. to DIN 17440 :1985-07. The material is a heat-treatable 17%-chromium-steel of favorable resistance to water, low acids and bases as well as to stronger oxidizing acids (e.g. nitrous acid). Application for high loaded machine parts such as pump and compressor construction, shipbuilding, food, soap, acetic acid industry. Favorable running characteristics and wear resistance. Usable for mirror finishing. Choose different tempering grades for components sliding on top of each other, otherwise risk of seizing.
Properties
General
| Property | Temperature | Value |
|---|---|---|
Density | 20.0 °C | 7.65 - 7.7 g/cm³ |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elastic modulus | 20.0 °C | 196 - 215 GPa | |
100.0 °C | 212 GPa | ||
200.0 °C | 205 GPa | ||
300.0 °C | 200 GPa | ||
400.0 °C | 190 GPa | ||
Hardness, Brinell | 20.0 °C | 295 [-] | |
Poisson's ratio | 23.0 °C | 0.3 [-] | Typical for Martensitic Stainless Steel |
Shear modulus | 23.0 °C | 77 GPa | Typical for Martensitic Stainless Steel |
Tensile strength | 20.0 °C | 1000 MPa | |
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | -100.0 °C | 9.2E-6 1/K | |
20.0 °C | 9.9E-6 1/K | ||
100.0 °C | 1E-5 - 1.03E-5 1/K | ||
200.0 °C | 1.05E-5 - 1.08E-5 1/K | ||
300.0 °C | 1.05E-5 - 1.12E-5 1/K | ||
400.0 °C | 1.05E-5 - 1.16E-5 1/K | ||
500.0 °C | 1.19E-5 1/K | ||
600.0 °C | 1.21E-5 1/K | ||
700.0 °C | 1.24E-5 1/K | ||
800.0 °C | 1.29E-5 1/K | ||
900.0 °C | 1.34E-5 1/K | ||
1000.0 °C | 1.39E-5 1/K | ||
Melting point | 1370 - 1530 °C | Typical for Martensitic Stainless Steel | |
Specific heat capacity | 20.0 °C | 450 - 460 J/(kg·K) | |
100.0 °C | 482 J/(kg·K) | ||
200.0 °C | 506 J/(kg·K) | ||
300.0 °C | 525 J/(kg·K) | ||
400.0 °C | 547 J/(kg·K) | ||
500.0 °C | 576 J/(kg·K) | ||
600.0 °C | 616 J/(kg·K) | ||
Thermal conductivity | 20.0 °C | 19.6 - 25 W/(m·K) | |
Thermal diffusivity | 20.0 °C | 5.7 mm²/s | |
Electrical
| Property | Temperature | Value |
|---|---|---|
Electrical resistivity | 20.0 °C | 6.17E-7 Ω·m |
Chemical properties
| Property | Value |
|---|---|
Carbon | 0.12 - 0.22 % |
Chromium | 15 - 17 % |
Manganese | 1.5 % |
Nickel | 1.5 - 2.5 % |
Phosphorus | 0.04 % |
Silicon | 1 % |
Sulfur | 0.03 % |
Metal
- EN 10088-1 X70CrMo15: Soft Annealed Grade for Cutting Tools & Industrial Applications
- X105CrMo17 Soft Annealed Steel (EN 10088-1) – High Hardening & Wear Resistance
- X12Cr13 Soft Annealed Steel (EN 10250-4): Key Properties & Industrial Uses
- EN 10250‑4 Grade X20Cr13 Soft Annealed Steel – High Strength, Corrosion‑Resistant Performance
- EN 10250-4 Grade X30Cr13 Soft Annealed: Premium Corrosion-Resistant Alloy for Precision Applications
- EN 10250‑4 Grade X3CrNiMo13‑4 Soft‑Annealed (+A) – Premium Corrosion‑Resistant Steel
- EN 10250-4 Grade X4CrNiMo16-5-1 Soft Annealed Stainless Steel (+A) – High Corrosion Resistance & Low‑Temperature Performance
- EN 10250-4 X6CrAl13 Soft Annealed (+A) – Superior Alloy for Petroleum & Power Plant Applications
- X17CrNi16-2 Soft Annealed Steel – DIN 17440 Grade for Pressure Vessels & Industrial Applications
- EN 10250-4 Grade X6Cr17 – Soft Annealed Ferritic Steel for Corrosion Resistance