EN 10277‑5 Grade C60: Cold‑Drawn, Turned & Normalized Steel for High‑Ductility, Wear‑Resistant Automotive Parts

Steel C 60 is suitable for high ductility parts and parts of increased wear resistance requirements in vehicle manufacturing, engine and machine engineering surface hardenable (e.g. transmission parts, shafts, axles). Additional application in tooling. Lowest application temp. -25 °C.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.8 g/cm³

Mechanical

PropertyTemperatureValue

Elastic modulus

-100.0 °C

217 GPa

20.0 °C

208.26 - 212 GPa

100.0 °C

203.78 - 207 GPa

200.0 °C

198.06 - 199 GPa

300.0 °C

190.8 - 192 GPa

400.0 °C

182.61 - 184 GPa

500.0 °C

173.04 - 175 GPa

600.0 °C

164 GPa

Elongation

20.0 °C

10 - 11 %

Poisson's ratio

20.0 °C

0.27 [-]

100.0 °C

0.27 [-]

200.0 °C

0.28 [-]

300.0 °C

0.28 [-]

400.0 °C

0.28 [-]

500.0 °C

0.28 [-]

Shear modulus

20.0 °C

82.04 GPa

100.0 °C

80.18 GPa

200.0 °C

77.56 GPa

300.0 °C

74.62 GPa

400.0 °C

71.22 GPa

500.0 °C

67.36 GPa

Tensile strength

20.0 °C

670 - 710 MPa

Yield strength

20.0 °C

340 - 380 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1.08E-5 1/K

20.0 °C

1.19E-5 1/K

100.0 °C

1.25E-5 1/K

200.0 °C

1.3E-5 1/K

300.0 °C

1.36E-5 1/K

400.0 °C

1.41E-5 1/K

500.0 °C

1.45E-5 1/K

600.0 °C

1.49E-5 1/K

Max service temperature

500 °C

Typical for Carbon Steel

Max service temperature, long

-25 - 0 °C

Melting point

1289 - 1478 °C

Typical for High Carbon Steel

Specific heat capacity

-100.0 °C

423 J/(kg·K)

20.0 °C

461 J/(kg·K)

100.0 °C

479 J/(kg·K)

200.0 °C

499 J/(kg·K)

300.0 °C

517 J/(kg·K)

400.0 °C

536 J/(kg·K)

500.0 °C

558 J/(kg·K)

600.0 °C

587 J/(kg·K)

Thermal conductivity

20.0 °C

41.7 W/(m·K)

100.0 °C

43.4 W/(m·K)

200.0 °C

43.2 W/(m·K)

300.0 °C

41.4 W/(m·K)

400.0 °C

39.1 W/(m·K)

500.0 °C

36.7 W/(m·K)

600.0 °C

34.1 W/(m·K)

Thermal diffusivity

20.0 °C

11.6 mm²/s

100.0 °C

11.3 mm²/s

200.0 °C

10.5 mm²/s

300.0 °C

9.5 mm²/s

400.0 °C

8.3 mm²/s

500.0 °C

7.1 mm²/s

600.0 °C

5.8 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

2.5E-7 Ω·m

100.0 °C

2.95E-7 Ω·m

200.0 °C

3.65E-7 Ω·m

300.0 °C

4.53E-7 Ω·m

400.0 °C

5.56E-7 Ω·m

500.0 °C

6.74E-7 Ω·m

600.0 °C

8.13E-7 Ω·m

Chemical properties

PropertyValue

Carbon

0.57 - 0.65 %

Manganese

0.6 - 0.9 %

Phosphorus

0.05 %

Silicon

0.4 %

Sulfur

0.045 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. EN 10277-5 Grade Cm60: Cold-Drawn or Turned and Normalized Steel for High-Strain Applications
    2. EN 10277-5 Grade C35: Cold-Drawn or Turned, Normalized Steel for Automotive & Machine Applications
    3. EN 10277-5 Grade C45: Cold Drawn, Turned & Normalized Steel for Automotive & Machinery
    4. EN 10277-5 Grade CK35: Cold‑Drawn, Turned & Normalized Steel for Automotive & Heavy‑Duty Applications
    5. CK45 Steel – EN 10277-5 Grade, Cold‑Drawn & Normalized
    6. EN 10277-5 Grade Ck60 Steel – Cold Drawn/Turned & Normalized for Heavy-Duty Applications
    7. EN 10277-5 Grade CM35 – Cold-Drawn/Turned & Normalized Steel for High-Performance Automotive Components
    8. EN 10277-5 Grade Cm45: Cold-Drawn, Turned, and Normalized Steel for Automotive & Industrial Applications
    9. EN 10277-5: Grade C22 Cold‑Drawn/Turned and Normalized Steel – Ideal for Low‑Strain Automotive Parts
    10. EN 10277-5 Grade CK22 – Cold-Drawn or Turned & Normalized Steel for Vehicle and Heavy Engineering Applications