EN 10250‑2 Grade C35E – Normalized & Tempered Steel for High-Performance Applications

Steel C35E is suitable for slightly higher loaded parts of higher dimensions (large forged parts) and complexer forms as well as for higher requirements to uniformity of properties and to surface quality in vehicle and machine engineering. (e.g. transmission parts, crankshafts). As a bright steel product the steel is used in the form of bars, bright, straight, in various conditions (see DIN EN 10277 : 1999-10).

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.82 g/cm³

Mechanical

PropertyTemperatureValueComment

Elastic modulus

-100.0 °C

217 GPa

20.0 °C

212 GPa

100.0 °C

207 GPa

200.0 °C

199 GPa

300.0 °C

192 GPa

400.0 °C

184 GPa

500.0 °C

175 GPa

600.0 °C

164 GPa

Elongation

20.0 °C

18 - 19 %

Elongation, transverse

20.0 °C

14 - 15 %

Poisson's ratio

23.0 °C

0.29 [-]

Typical for Medium Carbon Steel

Shear modulus

23.0 °C

75 - 80 GPa

Typical for Carbon Steel

Tensile strength

20.0 °C

470 - 520 MPa

Tensile strength, transverse

20.0 °C

470 - 500 MPa

Yield strength

20.0 °C

210 - 270 MPa

Yield strength, transverse

20.0 °C

210 - 245 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1.08E-5 1/K

20.0 °C

1.19E-5 1/K

100.0 °C

1.25E-5 1/K

200.0 °C

1.3E-5 1/K

300.0 °C

1.36E-5 1/K

400.0 °C

1.41E-5 1/K

500.0 °C

1.45E-5 1/K

600.0 °C

1.49E-5 1/K

Max service temperature

500 °C

Typical for Carbon Steel

Melting point

1380 - 1514 °C

Typical for Medium Carbon Steel

Specific heat capacity

-100.0 °C

423 J/(kg·K)

20.0 °C

461 J/(kg·K)

100.0 °C

479 J/(kg·K)

200.0 °C

499 J/(kg·K)

300.0 °C

517 J/(kg·K)

400.0 °C

536 J/(kg·K)

500.0 °C

558 J/(kg·K)

600.0 °C

587 J/(kg·K)

Thermal conductivity

20.0 °C

48 W/(m·K)

100.0 °C

48.9 W/(m·K)

200.0 °C

47.5 W/(m·K)

300.0 °C

44.7 W/(m·K)

400.0 °C

41.6 W/(m·K)

500.0 °C

38.6 W/(m·K)

600.0 °C

35.5 W/(m·K)

Thermal diffusivity

20.0 °C

13.3 mm²/s

100.0 °C

12.6 mm²/s

200.0 °C

11.5 mm²/s

300.0 °C

10.2 mm²/s

400.0 °C

8.9 mm²/s

500.0 °C

7.5 mm²/s

600.0 °C

6 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

2.17E-7 Ω·m

100.0 °C

2.62E-7 Ω·m

200.0 °C

3.32E-7 Ω·m

300.0 °C

4.2E-7 Ω·m

400.0 °C

5.23E-7 Ω·m

500.0 °C

6.41E-7 Ω·m

600.0 °C

7.8E-7 Ω·m

Chemical properties

PropertyValue

Carbon

0.32 - 0.39 %

Chromium

0.4 %

Manganese

0.5 - 0.8 %

Molybdenum

0.1 %

Nickel

0.4 %

Phosphorus

0.04 %

Silicon

0.4 %

Sulfur

0.035 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. EN 10250-2 Grade C30 Steel – Normalized & Tempered (+NT) for High Ductility Applications
    2. EN 10250‑2 Grade C40 Steel – Normalized & Tempered (NT) – Key Properties & Applications
    3. EN 10250-2 Grade C50 Normalized & Tempered Steel – High Strength & Abrasion Resistance
    4. EN 10250-2 Grade 28Mn6 Steel – Normalized & Tempered for High-Performance Applications
    5. EN 10250-2 Grade C45E: Normalized & Tempered Steel for Heavy‑Duty Applications
    6. EN 10250-2 Grade C55E: Normalized & Tempered Steel for Heavy-Duty Applications
    7. EN 10250-2 Grade C60E Steel – Normalized & Tempered (NT) – High-Performance Industrial Alloy
    8. EN 10250-2 Grade C35 Steel – Normalized & Tempered (NT)
    9. EN 10250‑2 Grade C22 Steel – Normalized & Tempered (NT) for High‑Performance Vehicle Components
    10. EN 10250-2 C45 Steel – Normalized & Tempered Grade for Automotive & Machinery Applications