DIN 17440 X5CrNi18-12 Alloy Steel – Quenched +Q: High Corrosion Resistance & Strength

Properites: - resistant to medium with little chloride content up to pH-value of 4,5 - similar corrosion resistance to 1.4301 (graded as high corrosion resistan) Application: - in chemical industry, screws, nuts and cold formed parts - in arcitecture for joining elements of steel group A 2 and A 4, strength class 70, DIN 267 part 1 - standard parts, like screws, nuts and thread parts, are manufactured by cold forming without cutting

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.9 - 7.93 g/cm³

Mechanical

PropertyTemperatureValue

Elastic modulus

-100.0 °C

206 GPa

20.0 °C

196 - 202.24 GPa

100.0 °C

190 - 194.36 GPa

200.0 °C

182 - 186 GPa

300.0 °C

174 - 179 GPa

400.0 °C

166 - 172 GPa

500.0 °C

157.59 - 165 GPa

600.0 °C

149.24 - 150 GPa

700.0 °C

142 GPa

800.0 °C

134 GPa

900.0 °C

127 GPa

1000.0 °C

120 GPa

Elongation

20.0 °C

35 - 45 %

Elongation, transverse

20.0 °C

40 %

Poisson's ratio

20.0 °C

0.29 [-]

100.0 °C

0.29 [-]

200.0 °C

0.3 [-]

300.0 °C

0.3 [-]

400.0 °C

0.31 [-]

500.0 °C

0.32 [-]

600.0 °C

0.33 [-]

Shear modulus

20.0 °C

78.33 GPa

100.0 °C

75.08 GPa

200.0 °C

71.07 GPa

300.0 °C

67.21 GPa

400.0 °C

63.34 GPa

500.0 °C

59.64 GPa

600.0 °C

56.08 GPa

Tensile strength

20.0 °C

490 - 690 MPa

Tensile strength, transverse

20.0 °C

490 - 690 MPa

Yield strength Rp0.2

20.0 °C

185 MPa

50.0 °C

175 MPa

100.0 °C

155 MPa

150.0 °C

142 MPa

200.0 °C

127 MPa

250.0 °C

118 MPa

300.0 °C

110 MPa

350.0 °C

104 MPa

400.0 °C

98 MPa

450.0 °C

95 MPa

500.0 °C

92 MPa

550.0 °C

90 MPa

Yield strength Rp0.2, transverse

20.0 °C

185 MPa

Yield strength Rp1.0

20.0 °C

220 MPa

50.0 °C

208 MPa

100.0 °C

188 MPa

150.0 °C

172 MPa

200.0 °C

157 MPa

250.0 °C

145 MPa

300.0 °C

135 MPa

350.0 °C

129 MPa

400.0 °C

125 MPa

450.0 °C

122 MPa

500.0 °C

120 MPa

550.0 °C

120 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1.49E-5 1/K

20.0 °C

1.61E-5 1/K

100.0 °C

1.6E-5 - 1.67E-5 1/K

200.0 °C

1.7E-5 - 1.72E-5 1/K

300.0 °C

1.7E-5 - 1.77E-5 1/K

400.0 °C

1.8E-5 - 1.81E-5 1/K

500.0 °C

1.8E-5 - 1.84E-5 1/K

600.0 °C

1.88E-5 1/K

700.0 °C

1.91E-5 1/K

800.0 °C

1.94E-5 1/K

900.0 °C

1.97E-5 1/K

1000.0 °C

2E-5 1/K

Melting point

1230 - 1480 °C

Typical for Austenitic Stainless Steel

Specific heat capacity

-100.0 °C

440 J/(kg·K)

20.0 °C

472 - 500 J/(kg·K)

100.0 °C

487 J/(kg·K)

200.0 °C

503 J/(kg·K)

300.0 °C

512 J/(kg·K)

400.0 °C

520 J/(kg·K)

500.0 °C

530 J/(kg·K)

600.0 °C

541 J/(kg·K)

700.0 °C

551 J/(kg·K)

800.0 °C

559 J/(kg·K)

900.0 °C

565 J/(kg·K)

1000.0 °C

571 J/(kg·K)

Thermal conductivity

20.0 °C

14.3 - 15 W/(m·K)

100.0 °C

15.8 W/(m·K)

200.0 °C

17.5 W/(m·K)

300.0 °C

19 W/(m·K)

400.0 °C

20.5 W/(m·K)

500.0 °C

21.9 W/(m·K)

600.0 °C

23.3 W/(m·K)

700.0 °C

24.6 W/(m·K)

800.0 °C

26 W/(m·K)

900.0 °C

27.4 W/(m·K)

1000.0 °C

28.8 W/(m·K)

Thermal diffusivity

20.0 °C

3.8 mm²/s

100.0 °C

4 mm²/s

200.0 °C

4.2 mm²/s

300.0 °C

4.6 mm²/s

400.0 °C

4.8 mm²/s

500.0 °C

4.9 mm²/s

600.0 °C

5 mm²/s

700.0 °C

5.3 mm²/s

800.0 °C

5.6 mm²/s

900.0 °C

5.9 mm²/s

1000.0 °C

6 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

7.1E-7 - 7.3E-7 Ω·m

100.0 °C

7.76E-7 Ω·m

200.0 °C

8.49E-7 Ω·m

300.0 °C

9.14E-7 Ω·m

400.0 °C

9.71E-7 Ω·m

500.0 °C

1.02E-6 Ω·m

600.0 °C

1.07E-6 Ω·m

700.0 °C

1.1E-6 Ω·m

800.0 °C

1.14E-6 Ω·m

900.0 °C

1.17E-6 Ω·m

1000.0 °C

1.19E-6 Ω·m

Chemical properties

PropertyValue

Carbon

0.07 %

Chromium

17 - 19 %

Manganese

2 %

Nickel

11 - 13 %

Phosphorus

0.05 %

Silicon

1 %

Sulfur

0.03 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. X3CrNiMo17-13-3 Grade Steel (Quenched +Q) – DIN 17440 Certified for Pressure Vessels
    2. DIN 17440 X10CrNiS18-9 Quenched Steel – High-Performance Free-Cutting Alloy
    3. DIN 17440 Grade X2CrNiMoN17-12-2 Quenched: Premium Austenitic Steel for Chemical & Textile Industries
    4. DIN 17440 Grade X5CrNiMo17-13-3 (Q) – High-Performance Stainless Steel for Chemical Applications
    5. DIN 17440 X2CrNiMo18-16-4 Quenched Steel – Superior Corrosion Resistance & Precision Formability
    6. DIN 17440 X6CrNiMoNb17-12-2 Quenched Alloy: Superior Corrosion Resistance & High‑Temperature Performance
    7. DIN 17440 X6CrNiMoTi17-12-2 Quenched Steel – High Corrosion Resistance for Chemical Engineering
    8. DIN 17440 Grade X2CrNiMo18-15-4 Quenched Steel: Superior Corrosion Resistance & Formability
    9. DIN 17440 X2CrNiMo17-13-2 Quenched Steel: Superior Corrosion Resistance & Formability
    10. DIN 17440 Quenched Grade X2CrNiMo17-12-2 (1.4404) – Superior Corrosion Resistance & Formability