X5CrNi18-12 Stainless Steel (DIN 1654-5) – Quenched & Tempered Grade

Because of its higher Ni content compared standard type to X 5CrNi 18 10, steel X 5 CrNi 18 12 possesses a higher austenitic stability. This decreaes the cold strain hardening. The forming properties for cold heading and extrusion pressing are good even at high forming rates. However, one must be aware of the increased cold strain hardening compared to carbon steels. It is used for stainless steel screws, nuts and cold-extruded parts. It is used for corrosive damage from water, atmosphere and oxidizing acids of higher concentration and higher temperatrues in the chemical industry.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.93 g/cm³

Mechanical

PropertyTemperatureValue

Elastic modulus

-100.0 °C

206 GPa

20.0 °C

196 - 202.24 GPa

100.0 °C

190 - 194.36 GPa

200.0 °C

182 - 186 GPa

300.0 °C

174 - 179 GPa

400.0 °C

166 - 172 GPa

500.0 °C

157.59 - 165 GPa

600.0 °C

149.24 - 150 GPa

700.0 °C

142 GPa

800.0 °C

134 GPa

900.0 °C

127 GPa

1000.0 °C

120 GPa

Poisson's ratio

20.0 °C

0.29 [-]

100.0 °C

0.29 [-]

200.0 °C

0.3 [-]

300.0 °C

0.3 [-]

400.0 °C

0.31 [-]

500.0 °C

0.32 [-]

600.0 °C

0.33 [-]

Reduction of area

20.0 °C

55 %

Shear modulus

20.0 °C

78.33 GPa

100.0 °C

75.08 GPa

200.0 °C

71.07 GPa

300.0 °C

67.21 GPa

400.0 °C

63.34 GPa

500.0 °C

59.64 GPa

600.0 °C

56.08 GPa

Tensile strength

20.0 °C

650 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1.49E-5 1/K

20.0 °C

1.61E-5 1/K

100.0 °C

1.6E-5 - 1.67E-5 1/K

200.0 °C

1.7E-5 - 1.72E-5 1/K

300.0 °C

1.7E-5 - 1.77E-5 1/K

400.0 °C

1.8E-5 - 1.81E-5 1/K

500.0 °C

1.8E-5 - 1.84E-5 1/K

600.0 °C

1.88E-5 1/K

700.0 °C

1.91E-5 1/K

800.0 °C

1.94E-5 1/K

900.0 °C

1.97E-5 1/K

1000.0 °C

2E-5 1/K

Melting point

1230 - 1480 °C

Typical for Austenitic Stainless Steel

Specific heat capacity

-100.0 °C

440 J/(kg·K)

20.0 °C

472 J/(kg·K)

100.0 °C

487 J/(kg·K)

200.0 °C

503 J/(kg·K)

300.0 °C

512 J/(kg·K)

400.0 °C

520 J/(kg·K)

500.0 °C

530 J/(kg·K)

600.0 °C

541 J/(kg·K)

700.0 °C

551 J/(kg·K)

800.0 °C

559 J/(kg·K)

900.0 °C

565 J/(kg·K)

1000.0 °C

571 J/(kg·K)

Thermal conductivity

20.0 °C

14.3 W/(m·K)

100.0 °C

15.8 W/(m·K)

200.0 °C

17.5 W/(m·K)

300.0 °C

19 W/(m·K)

400.0 °C

20.5 W/(m·K)

500.0 °C

21.9 W/(m·K)

600.0 °C

23.3 W/(m·K)

700.0 °C

24.6 W/(m·K)

800.0 °C

26 W/(m·K)

900.0 °C

27.4 W/(m·K)

1000.0 °C

28.8 W/(m·K)

Thermal diffusivity

20.0 °C

3.8 mm²/s

100.0 °C

4 mm²/s

200.0 °C

4.2 mm²/s

300.0 °C

4.6 mm²/s

400.0 °C

4.8 mm²/s

500.0 °C

4.9 mm²/s

600.0 °C

5 mm²/s

700.0 °C

5.3 mm²/s

800.0 °C

5.6 mm²/s

900.0 °C

5.9 mm²/s

1000.0 °C

6 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

7.1E-7 Ω·m

100.0 °C

7.76E-7 Ω·m

200.0 °C

8.49E-7 Ω·m

300.0 °C

9.14E-7 Ω·m

400.0 °C

9.71E-7 Ω·m

500.0 °C

1.02E-6 Ω·m

600.0 °C

1.07E-6 Ω·m

700.0 °C

1.1E-6 Ω·m

800.0 °C

1.14E-6 Ω·m

900.0 °C

1.17E-6 Ω·m

1000.0 °C

1.19E-6 Ω·m

Chemical properties

PropertyValue

Carbon

0.07 %

Chromium

17 - 19 %

Manganese

2 %

Nickel

11 - 13 %

Phosphorus

0.05 %

Silicon

1 %

Sulfur

0.03 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. X5CrNi18-12 Stainless Steel – DIN 1654-5 Grade, Cold‑Drawn, Quenched & Skin‑Passed
    2. DIN 1654-5 X3CrNiCu18-9: High-Performance Austenitic Stainless Steel, Quenched & Cold-Worked
    3. DIN 1654-5 X5CrNi18-12 – Premium Cold-Drawn & Quenched Austenitic Stainless Steel
    4. DIN 1654-5 X5CrNiMo17-12-2: High-Performance Quenched & Turned Steel for Chemical & Pharmaceutical Applications
    5. DIN 1654-5 Grade X6CrNiMoTi17-12-2 – Quenched & Turned: Exceptional Cold-Forming & Corrosion Resistance
    6. DIN 1654-5 Grade X6CrNiTi18-10 – Quenched & Tempered Stainless Steel for High‑Performance Applications
    7. DIN 1654-5 X2CrNi19-11 Steel – Quenched & Tempered for Superior Cold-Forming
    8. DIN 1654-5 Grade X2CrNiMoN17-13-3: Premium Quenched & Tempered Austenitic Steel for Superior Strength and Chemical Resistance
    9. DIN 1654-5 X2CrNiN18-10 Austenitic Steel – Quenched & Turned for High-Performance Applications
    10. DIN 1654-5 Grade X5CrNi18-12 Quenched Steel (+Q): Enhanced Austenitic Stability & Formability