DIN 1654-5 X2CrNiN18-10 Austenitic Steel – Quenched & Turned for High-Performance Applications

X 2 CrNi 18 10 is an austenitic CrNi steel which, due to the added nitrogen alloy, possesses an increased yield strength which also persist in higher temperatures. It is suitable for the chemical equipment construction because of its resistance to nitric acid. The steel is well suited for cold-forming and can undergo high-gloss polishing. It is used for screws, nuts and molded parts at temperatures from -270 up to 400 degrees C.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.93 g/cm³

Mechanical

PropertyTemperatureValueComment

Elastic modulus

-100.0 °C

206 GPa

20.0 °C

196 GPa

100.0 °C

190 - 194 GPa

200.0 °C

182 - 186 GPa

300.0 °C

174 - 179 GPa

400.0 °C

166 - 172 GPa

500.0 °C

158 - 165 GPa

600.0 °C

150 GPa

700.0 °C

142 GPa

800.0 °C

134 GPa

900.0 °C

127 GPa

1000.0 °C

120 GPa

Poisson's ratio

23.0 °C

0.3 [-]

Typical for Austenitic Stainless Steel

Reduction of area

20.0 °C

55 %

Shear modulus

23.0 °C

77 GPa

Typical for Austenitic Stainless Steel

Tensile strength

20.0 °C

730 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1.49E-5 1/K

20.0 °C

1.61E-5 1/K

100.0 °C

1.6E-5 - 1.67E-5 1/K

200.0 °C

1.7E-5 - 1.72E-5 1/K

300.0 °C

1.7E-5 - 1.77E-5 1/K

400.0 °C

1.8E-5 - 1.81E-5 1/K

500.0 °C

1.8E-5 - 1.84E-5 1/K

600.0 °C

1.88E-5 1/K

700.0 °C

1.91E-5 1/K

800.0 °C

1.94E-5 1/K

900.0 °C

1.97E-5 1/K

1000.0 °C

2E-5 1/K

Max service temperature, long

-270 - 400 °C

Melting point

1230 - 1480 °C

Typical for Austenitic Stainless Steel

Specific heat capacity

-100.0 °C

440 J/(kg·K)

20.0 °C

472 J/(kg·K)

100.0 °C

487 J/(kg·K)

200.0 °C

503 J/(kg·K)

300.0 °C

512 J/(kg·K)

400.0 °C

520 J/(kg·K)

500.0 °C

530 J/(kg·K)

600.0 °C

541 J/(kg·K)

700.0 °C

551 J/(kg·K)

800.0 °C

559 J/(kg·K)

900.0 °C

565 J/(kg·K)

1000.0 °C

571 J/(kg·K)

Thermal conductivity

20.0 °C

14.3 W/(m·K)

100.0 °C

15.8 W/(m·K)

200.0 °C

17.5 W/(m·K)

300.0 °C

19 W/(m·K)

400.0 °C

20.5 W/(m·K)

500.0 °C

21.9 W/(m·K)

600.0 °C

23.3 W/(m·K)

700.0 °C

24.6 W/(m·K)

800.0 °C

26 W/(m·K)

900.0 °C

27.4 W/(m·K)

1000.0 °C

28.8 W/(m·K)

Thermal diffusivity

20.0 °C

3.8 mm²/s

100.0 °C

4 mm²/s

200.0 °C

4.2 mm²/s

300.0 °C

4.6 mm²/s

400.0 °C

4.8 mm²/s

500.0 °C

4.9 mm²/s

600.0 °C

5 mm²/s

700.0 °C

5.3 mm²/s

800.0 °C

5.6 mm²/s

900.0 °C

5.9 mm²/s

1000.0 °C

6 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

7.1E-7 Ω·m

100.0 °C

7.76E-7 Ω·m

200.0 °C

8.49E-7 Ω·m

300.0 °C

9.14E-7 Ω·m

400.0 °C

9.71E-7 Ω·m

500.0 °C

1.02E-6 Ω·m

600.0 °C

1.07E-6 Ω·m

700.0 °C

1.1E-6 Ω·m

800.0 °C

1.14E-6 Ω·m

900.0 °C

1.17E-6 Ω·m

1000.0 °C

1.19E-6 Ω·m

Chemical properties

PropertyValue

Carbon

0.03 %

Chromium

17 - 19 %

Manganese

2 %

Nickel

8.5 - 11.5 %

Phosphorus

0.05 %

Silicon

1 %

Sulfur

0.03 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. X5CrNi18-12 Stainless Steel (DIN 1654-5) – Quenched & Tempered Grade
    2. DIN 1654-5 X2CrNiN18-10: Premium Cold‑Drawn, Quenched Steel for High‑Temperature Chemical Applications
    3. DIN 1654-5 X3CrNiCu18-9: High-Performance Austenitic Stainless Steel, Quenched & Cold-Worked
    4. DIN 1654-5 X5CrNiMo17-12-2: High-Performance Quenched & Turned Steel for Chemical & Pharmaceutical Applications
    5. DIN 1654-5 Grade X6CrNiMoTi17-12-2 – Quenched & Turned: Exceptional Cold-Forming & Corrosion Resistance
    6. DIN 1654-5 Grade X6CrNiTi18-10 – Quenched & Tempered Stainless Steel for High‑Performance Applications
    7. DIN 1654-5 X2CrNi19-11 Steel – Quenched & Tempered for Superior Cold-Forming
    8. DIN 1654-5 Grade X2CrNiMoN17-13-3: Premium Quenched & Tempered Austenitic Steel for Superior Strength and Chemical Resistance
    9. DIN 1654-5 Grade X2CrNiN18-10 – Cold‑Drawn & Quenched Austenitic Stainless Steel
    10. X2CrNiN18-10 Quenched Steel (DIN 1654-5) – High Strength & Nitric Acid Resistance