DIN 1654-5 Grade X2CrNiMoN17-13-3: Premium Quenched & Tempered Austenitic Steel for Superior Strength and Chemical Resistance

X 2 CrNiMoN 17 13 3 is a fully austenitic steel that is well suited for cold-forming and can undergo high-gloss polishing. Due to the added nitrogen alloy it possesses a higher strength and the molybdenium additive causes increased resistance especially to non-oxidizing acids and substances containing halogen. Higher resistance to selective attacks and an extraordinary endurance limit performance even under chemical stress. Good low temperature toughness which makes the steel suitable for temperatures to -270 degrees C the refrigeration industry. It is used for stainless steel screws, nuts and molded parts.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

8.01 g/cm³

Mechanical

PropertyTemperatureValue

Elastic modulus

-100.0 °C

206 GPa

20.0 °C

196 - 197.57 GPa

100.0 °C

190 - 194 GPa

200.0 °C

182 - 186 GPa

300.0 °C

174 - 179 GPa

400.0 °C

166 - 172 GPa

500.0 °C

158 - 165 GPa

600.0 °C

150 GPa

700.0 °C

142 GPa

800.0 °C

134 GPa

Poisson's ratio

20.0 °C

0.28 [-]

Reduction of area

20.0 °C

55 %

Shear modulus

20.0 °C

77.3 GPa

Tensile strength

20.0 °C

780 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1.49E-5 1/K

20.0 °C

1.61E-5 1/K

100.0 °C

1.65E-5 - 1.67E-5 1/K

200.0 °C

1.72E-5 - 1.75E-5 1/K

300.0 °C

1.75E-5 - 1.77E-5 1/K

400.0 °C

1.81E-5 - 1.85E-5 1/K

500.0 °C

1.84E-5 - 1.85E-5 1/K

600.0 °C

1.88E-5 1/K

700.0 °C

1.91E-5 1/K

800.0 °C

1.94E-5 1/K

900.0 °C

1.97E-5 1/K

1000.0 °C

2E-5 1/K

Max service temperature, long

-270 - 0 °C

Melting point

1230 - 1480 °C

Typical for Austenitic Stainless Steel

Specific heat capacity

-100.0 °C

440 J/(kg·K)

20.0 °C

472 J/(kg·K)

100.0 °C

487 J/(kg·K)

200.0 °C

503 J/(kg·K)

300.0 °C

512 J/(kg·K)

400.0 °C

520 J/(kg·K)

500.0 °C

530 J/(kg·K)

600.0 °C

541 J/(kg·K)

700.0 °C

551 J/(kg·K)

800.0 °C

559 J/(kg·K)

900.0 °C

565 J/(kg·K)

1000.0 °C

571 J/(kg·K)

Thermal conductivity

20.0 °C

13.5 W/(m·K)

100.0 °C

14.9 W/(m·K)

200.0 °C

16.7 W/(m·K)

300.0 °C

18.3 W/(m·K)

400.0 °C

19.8 W/(m·K)

500.0 °C

21.3 W/(m·K)

600.0 °C

22.7 W/(m·K)

700.0 °C

24.2 W/(m·K)

800.0 °C

25.6 W/(m·K)

Thermal diffusivity

20.0 °C

3.6 mm²/s

100.0 °C

3.7 mm²/s

200.0 °C

4 mm²/s

300.0 °C

4.4 mm²/s

400.0 °C

4.6 mm²/s

500.0 °C

4.7 mm²/s

600.0 °C

4.9 mm²/s

700.0 °C

5.2 mm²/s

800.0 °C

5.5 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

7.75E-7 Ω·m

100.0 °C

8.42E-7 Ω·m

200.0 °C

9.04E-7 Ω·m

300.0 °C

9.62E-7 Ω·m

400.0 °C

1.01E-6 Ω·m

500.0 °C

1.06E-6 Ω·m

600.0 °C

1.1E-6 Ω·m

700.0 °C

1.13E-6 Ω·m

800.0 °C

1.16E-6 Ω·m

Chemical properties

PropertyValue

Carbon

0.03 %

Chromium

16.5 - 18.5 %

Manganese

2 %

Molybdenum

2.5 - 3 %

Nickel

12 - 14.5 %

Phosphorus

0.05 %

Silicon

1 %

Sulfur

0.025 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. X5CrNi18-12 Stainless Steel (DIN 1654-5) – Quenched & Tempered Grade
    2. DIN 1654-5 X3CrNiCu18-9: Premium Cold-Drawn & Turned Austenitic Stainless Steel
    3. DIN 1654-5 X3CrNiCu18-9: High-Performance Austenitic Stainless Steel, Quenched & Cold-Worked
    4. DIN 1654-5 X5CrNiMo17-12-2: High-Performance Quenched & Turned Steel for Chemical & Pharmaceutical Applications
    5. DIN 1654-5 Grade X6CrNiMoTi17-12-2 – Quenched & Turned: Exceptional Cold-Forming & Corrosion Resistance
    6. DIN 1654-5 Grade X6CrNiTi18-10 – Quenched & Tempered Stainless Steel for High‑Performance Applications
    7. DIN 1654-5 X2CrNi19-11 Steel – Quenched & Tempered for Superior Cold-Forming
    8. DIN 1654-5 Grade X2CrNiMoN17-13-3 – Cold‑Drawn & Quenched Austenitic Steel
    9. DIN 1654-5 X2CrNiN18-10 Austenitic Steel – Quenched & Turned for High-Performance Applications
    10. DIN 1654-5 X2CrNiMoN17-13-3 Quenched Steel – High Strength, Corrosion Resistance, and Low‑Temperature Toughness