EN 10250-2 Grade C45E: Normalized or Normalized Formed Steel (+N) – Specifications & Applications

Steel C45 is suitable for mean loaded parts of higher dimensions (large forged parts) and complexer forms in vehicle and machine engineering (e.g. ship shafts, transmission parts, wheel hubs). As a bright steel product the steel is used in the form of bars, bright, straight, in various conditions (see DIN EN 10277 : 1999-10).

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.8 g/cm³

Mechanical

PropertyTemperatureValueComment

Elastic modulus

-100.0 °C

217 GPa

20.0 °C

212 GPa

100.0 °C

207 GPa

200.0 °C

199 GPa

300.0 °C

192 GPa

400.0 °C

184 GPa

500.0 °C

175 GPa

600.0 °C

164 GPa

Elongation

20.0 °C

15 - 18 %

Elongation, transverse

20.0 °C

10 - 12 %

Poisson's ratio

23.0 °C

0.29 [-]

Typical for Medium Carbon Steel

Shear modulus

23.0 °C

75 - 80 GPa

Typical for Carbon Steel

Tensile strength

20.0 °C

590 - 720 MPa

Tensile strength, transverse

20.0 °C

540 - 720 MPa

Yield strength

20.0 °C

295 - 325 MPa

Yield strength, transverse

20.0 °C

295 - 325 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1.08E-5 1/K

20.0 °C

1.19E-5 1/K

100.0 °C

1.25E-5 1/K

200.0 °C

1.3E-5 1/K

300.0 °C

1.36E-5 1/K

400.0 °C

1.41E-5 1/K

500.0 °C

1.45E-5 1/K

600.0 °C

1.49E-5 1/K

Max service temperature

500 °C

Typical for Carbon Steel

Melting point

1380 - 1514 °C

Typical for Medium Carbon Steel

Specific heat capacity

-100.0 °C

423 J/(kg·K)

20.0 °C

461 J/(kg·K)

100.0 °C

479 J/(kg·K)

200.0 °C

499 J/(kg·K)

300.0 °C

517 J/(kg·K)

400.0 °C

536 J/(kg·K)

500.0 °C

558 J/(kg·K)

600.0 °C

587 J/(kg·K)

Thermal conductivity

20.0 °C

41.7 W/(m·K)

100.0 °C

43.4 W/(m·K)

200.0 °C

43.2 W/(m·K)

300.0 °C

41.4 W/(m·K)

400.0 °C

39.1 W/(m·K)

500.0 °C

36.7 W/(m·K)

600.0 °C

34.1 W/(m·K)

Thermal diffusivity

20.0 °C

11.6 mm²/s

100.0 °C

11.3 mm²/s

200.0 °C

10.5 mm²/s

300.0 °C

9.5 mm²/s

400.0 °C

8.3 mm²/s

500.0 °C

7.1 mm²/s

600.0 °C

5.8 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

2.5E-7 Ω·m

100.0 °C

2.95E-7 Ω·m

200.0 °C

3.65E-7 Ω·m

300.0 °C

4.53E-7 Ω·m

400.0 °C

5.56E-7 Ω·m

500.0 °C

6.74E-7 Ω·m

600.0 °C

8.13E-7 Ω·m

Chemical properties

PropertyValue

Carbon

0.42 - 0.5 %

Chromium

0.4 %

Manganese

0.5 - 0.8 %

Molybdenum

0.1 %

Nickel

0.4 %

Phosphorus

0.04 %

Silicon

0.4 %

Sulfur

0.035 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. EN 10269 Grade C45E – Normalized or Normalized Formed Steel for Heavy-Duty Vehicle and Machine Components
    2. EN 10250‑2 S235J2G3 Steel – Normalized & Formed (±N) for Dynamic Load Welding
    3. EN 10250‑2 – S235JRG2 Low‑Carbon Steel (Normalized or Normalized‑Formed)
    4. EN 10250-2 Grade S355J2G3 – Normalized or Normalized Formed Steel for High-Performance Welding Applications
    5. EN 10250‑2 Grade C35E Steel – Normalized/Normal Formed (N) for Heavy‑Duty Automotive & Machine Components
    6. EN 10250-2 Grade C45E: Normalized & Tempered Steel for Heavy‑Duty Applications
    7. EN 10250-2 Grade C45E: Normalized or Normalized Formed Steel (+N) – Specifications & Applications
    8. EN 10250‑2 Grade C60E: Normalized or +N Steel for Heavy‑Duty Applications
    9. ISO 683-1 Grade C45E: Normalized & Formed Steel for Heavy‑Duty Applications
    10. EN 10216-2 Grade St 45.8: High‑Temperature Normalized Tube Steel (+N) for Seamless Tubes