EN 10083‑1 Grade C25E Quenched & Tempered Steel – Superior Strength & Surface Finish

Steel C25E is suitable for low strained parts of higher dimension and more complex form as well as higher demands on uniformity of proprties and surface appearance (e.g. transmission parts, crankshafts). Lowest working temperature -25 °C.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.82 - 7.85 g/cm³

Mechanical

PropertyTemperatureValueComment

Elastic modulus

-100.0 °C

217 GPa

20.0 °C

210 - 212 GPa

100.0 °C

205 - 207 GPa

200.0 °C

195 - 199 GPa

300.0 °C

185 - 192 GPa

400.0 °C

175 - 184 GPa

500.0 °C

175 GPa

600.0 °C

164 GPa

Elongation

20.0 °C

19 - 21 %

Poisson's ratio

23.0 °C

0.29 [-]

Typical for Low Carbon Steel

Reduction of area

20.0 °C

45 - 50 %

Shear modulus

20.0 °C

81 GPa

Tensile strength

20.0 °C

500 - 700 MPa

Yield strength

20.0 °C

320 - 370 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1.08E-5 1/K

20.0 °C

1.19E-5 1/K

100.0 °C

1.11E-5 - 1.25E-5 1/K

200.0 °C

1.21E-5 - 1.3E-5 1/K

300.0 °C

1.29E-5 - 1.36E-5 1/K

400.0 °C

1.35E-5 - 1.41E-5 1/K

500.0 °C

1.45E-5 1/K

600.0 °C

1.49E-5 1/K

Max service temperature

500 °C

Typical for Carbon Steel

Max service temperature, long

-25 - 0 °C

Melting point

1480 - 1526 °C

Typical for Low Carbon Steel

Specific heat capacity

-100.0 °C

423 J/(kg·K)

20.0 °C

460 - 461 J/(kg·K)

100.0 °C

479 - 480 J/(kg·K)

200.0 °C

499 - 520 J/(kg·K)

300.0 °C

517 J/(kg·K)

400.0 °C

536 - 610 J/(kg·K)

500.0 °C

558 J/(kg·K)

600.0 °C

587 J/(kg·K)

Thermal conductivity

20.0 °C

39.6 - 52 W/(m·K)

100.0 °C

41 - 51 W/(m·K)

200.0 °C

41 - 49 W/(m·K)

300.0 °C

39.9 - 46 W/(m·K)

400.0 °C

38.1 W/(m·K)

500.0 °C

35.9 W/(m·K)

600.0 °C

33.6 W/(m·K)

Thermal diffusivity

20.0 °C

11 mm²/s

100.0 °C

10.6 mm²/s

200.0 °C

9.9 mm²/s

300.0 °C

9 mm²/s

400.0 °C

8.1 mm²/s

500.0 °C

6.9 mm²/s

600.0 °C

5.7 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

1.2E-7 - 2.63E-7 Ω·m

100.0 °C

3.12E-7 Ω·m

200.0 °C

3.85E-7 Ω·m

300.0 °C

4.7E-7 Ω·m

400.0 °C

5.71E-7 Ω·m

500.0 °C

6.88E-7 Ω·m

600.0 °C

8.25E-7 Ω·m

Magnetic

PropertyValueComment

Curie temperature

770 °C

Typical for Low Carbon Steel

Chemical properties

PropertyValue

Carbon

0.22 - 0.29 %

Chromium

0.4 %

Copper

0.3 %

Manganese

0.4 - 0.7 %

Molybdenum

0.1 %

Nickel

0.4 %

Phosphorus

0.03 - 0.04 %

Silicon

0.1 - 0.4 %

Sulfur

0.035 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. EN 10083-1 Grade 51CrV4: Quenched & Tempered Steel (QT)
    2. EN 10083-1 Grade 25CrMo4 Quenched & Tempered Steel: High Strength & Ductility for Automotive & Engine Components
    3. EN 10083-1 Grade 30CrNiMo8: High-Performance Quenched & Tempered Steel for Heavy-Duty Applications
    4. EN 10083-1 Grade 34Cr4 Quenched & Tempered Steel (+QT) – High Performance for Automotive & Industrial Applications
    5. EN 10083-1 Grade 34CrMo4 Quenched & Tempered Steel: High Strength & Toughness for Automotive & Industrial Applications
    6. EN 10083‑1 Grade 34CrNiMo6 Steel – Quenched & Tempered (+QT) for High‑Load Applications
    7. EN 10083‑1 Grade C30E Quenched & Tempered Steel – Ideal for High‑Performance Vehicle & Machine Components
    8. EN 10083-1 Grade C30R Quenched & Tempered Steel – Ideal for Automotive & Engine Components
    9. EN 10083‑1 Grade C45E Quenched & Tempered Steel – High‑Performance for Automotive & Machinery Applications
    10. EN 10083-1 Grade C25R Quenched & Tempered Steel – Ideal for Vehicle & Machine Engineering