DIN 17440 X5CrNiMo17-12-2 Quenched Steel – Superior Acid Resistance & Formability

Properties: - austenitic CrNiMo-steel with increased resistant to not-oxidizing acids and halogen containing media - high polishable, able for well cold forming Application: - for acid-proof apparatuses of the chemical and pharmaceutical industry - for cellulose, rubber, pigment, fatty acid , textile industry, petrochemie - for parts of the medical and photographic need, in purification plants, with higher chloride contents - in pressure tank construction to 300 °C applicable, beyond that subject to approval - in the building industry used for elements with highest corrosion loadings (e.g. brick-work anchorages in the concrete, chimneys, sanitary engineering, fronts outside, elevators) - is certified for construction units with basic function (extended licence notice No. Z-30.44.1 of Institut fürBautechnik Berlin, from 1 February 1994) - usual are the strength classes E 225, E 355

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.96 - 7.98 g/cm³

22.0 °C

7.96 g/cm³

Mechanical

PropertyTemperatureValue

Elastic modulus

-100.0 °C

206 GPa

20.0 °C

196 - 200 GPa

22.0 °C

196.2 GPa

24.0 °C

193.1 - 197.9 GPa

100.0 °C

190 - 194 GPa

149.0 °C

184.8 - 190.3 GPa

200.0 °C

182 - 186 GPa

260.0 °C

182 - 182.7 GPa

300.0 °C

174 - 179 GPa

371.0 °C

174.4 - 179.3 GPa

400.0 °C

166 - 172 GPa

483.0 °C

163.4 - 165.5 GPa

500.0 °C

158 - 165 GPa

593.0 °C

153.4 - 157.9 GPa

600.0 °C

150 GPa

700.0 °C

142 GPa

704.0 °C

143.4 - 146.2 GPa

800.0 °C

134 GPa

816.0 °C

124.1 - 133.1 GPa

900.0 °C

127 GPa

1000.0 °C

120 GPa

Elongation

20.0 °C

35 - 40 %

Elongation A80

20.0 °C

35 %

Elongation A80, transverse

20.0 °C

40 %

Elongation, transverse

20.0 °C

30 - 40 %

Poisson's ratio

22.0 °C

0.29 [-]

24.0 °C

0.23 - 0.28 [-]

149.0 °C

0.24 - 0.28 [-]

260.0 °C

0.28 - 0.31 [-]

371.0 °C

0.33 - 0.36 [-]

483.0 °C

0.29 - 0.32 [-]

593.0 °C

0.32 [-]

704.0 °C

0.28 - 0.34 [-]

816.0 °C

0.22 - 0.27 [-]

Shear modulus

22.0 °C

75.8 GPa

24.0 °C

77.2 - 78.6 GPa

149.0 °C

74.5 GPa

260.0 °C

69.6 - 71 GPa

371.0 °C

64.1 - 67.6 GPa

483.0 °C

62.1 - 64.1 GPa

593.0 °C

57.9 - 60 GPa

704.0 °C

54.5 - 55.9 GPa

816.0 °C

51 - 52.4 GPa

Tensile strength

20.0 °C

510 - 710 MPa

Tensile strength, transverse

20.0 °C

510 - 710 MPa

Yield strength Rp0.2

20.0 °C

205 MPa

50.0 °C

196 MPa

100.0 °C

177 MPa

150.0 °C

162 MPa

200.0 °C

147 MPa

250.0 °C

137 MPa

300.0 °C

127 MPa

350.0 °C

120 MPa

400.0 °C

115 MPa

450.0 °C

112 MPa

500.0 °C

110 MPa

550.0 °C

108 MPa

Yield strength Rp0.2, transverse

20.0 °C

205 MPa

Yield strength Rp1.0

20.0 °C

240 MPa

50.0 °C

230 MPa

100.0 °C

211 MPa

150.0 °C

191 MPa

200.0 °C

177 MPa

250.0 °C

167 MPa

300.0 °C

156 MPa

350.0 °C

150 MPa

400.0 °C

144 MPa

450.0 °C

141 MPa

500.0 °C

139 MPa

550.0 °C

137 MPa

Yield strength Rp1.0, transverse

20.0 °C

240 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1.49E-5 1/K

20.0 °C

1.61E-5 1/K

100.0 °C

1.65E-5 - 1.67E-5 1/K

200.0 °C

1.72E-5 - 1.75E-5 1/K

300.0 °C

1.75E-5 - 1.77E-5 1/K

400.0 °C

1.81E-5 - 1.85E-5 1/K

500.0 °C

1.84E-5 - 1.85E-5 1/K

600.0 °C

1.88E-5 1/K

700.0 °C

1.91E-5 1/K

800.0 °C

1.94E-5 1/K

900.0 °C

1.97E-5 1/K

1000.0 °C

2E-5 1/K

Max service temperature, long

0 - 300 °C

Melting point

1230 - 1480 °C

Typical for Austenitic Stainless Steel

Specific heat capacity

-100.0 °C

440 J/(kg·K)

20.0 °C

472 - 500 J/(kg·K)

100.0 °C

487 J/(kg·K)

200.0 °C

503 J/(kg·K)

300.0 °C

512 J/(kg·K)

400.0 °C

520 J/(kg·K)

500.0 °C

530 J/(kg·K)

600.0 °C

541 J/(kg·K)

700.0 °C

551 J/(kg·K)

800.0 °C

559 J/(kg·K)

900.0 °C

565 J/(kg·K)

1000.0 °C

571 J/(kg·K)

Thermal conductivity

20.0 °C

13.3 - 15 W/(m·K)

100.0 °C

14.9 W/(m·K)

200.0 °C

16.5 W/(m·K)

300.0 °C

18.1 W/(m·K)

400.0 °C

19.5 W/(m·K)

500.0 °C

21 W/(m·K)

600.0 °C

22.4 W/(m·K)

700.0 °C

23.8 W/(m·K)

800.0 °C

25.2 W/(m·K)

Thermal diffusivity

20.0 °C

3.5 mm²/s

100.0 °C

3.8 mm²/s

200.0 °C

4 mm²/s

300.0 °C

4.3 mm²/s

400.0 °C

4.5 mm²/s

500.0 °C

4.7 mm²/s

600.0 °C

4.8 mm²/s

700.0 °C

5.1 mm²/s

800.0 °C

5.4 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

7.5E-7 - 7.91E-7 Ω·m

100.0 °C

8.45E-7 Ω·m

200.0 °C

9.19E-7 Ω·m

300.0 °C

9.77E-7 Ω·m

400.0 °C

1.03E-6 Ω·m

500.0 °C

1.08E-6 Ω·m

600.0 °C

1.12E-6 Ω·m

700.0 °C

1.15E-6 Ω·m

800.0 °C

1.18E-6 Ω·m

Chemical properties

PropertyValue

Carbon

0.07 %

Chromium

16.5 - 18.5 %

Manganese

2 %

Molybdenum

2 - 2.5 %

Nickel

10 - 13.5 %

Nitrogen

0.11 %

Phosphorus

0.05 %

Silicon

1 %

Sulfur

0.015 - 0.03 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. X3CrNiMo17-13-3 Grade Steel (Quenched +Q) – DIN 17440 Certified for Pressure Vessels
    2. DIN 17440 X10CrNiS18-9 Quenched Steel – High-Performance Free-Cutting Alloy
    3. DIN 17440 X5CrNi18-12 Alloy Steel – Quenched +Q: High Corrosion Resistance & Strength
    4. DIN 1654-5 X5CrNiMo17-12-2 Stainless Steel (Quenched) – High Strength & Corrosion Resistance
    5. DIN 17440 Grade X2CrNiMoN17-12-2 Quenched: Premium Austenitic Steel for Chemical & Textile Industries
    6. DIN 17440 Grade X5CrNiMo17-13-3 (Q) – High-Performance Stainless Steel for Chemical Applications
    7. DIN 17440 X2CrNiMo18-16-4 Quenched Steel – Superior Corrosion Resistance & Precision Formability
    8. DIN 17440 X6CrNiMoNb17-12-2 Quenched Alloy: Superior Corrosion Resistance & High‑Temperature Performance
    9. DIN 17440 X6CrNiMoTi17-12-2 Quenched Steel – High Corrosion Resistance for Chemical Engineering
    10. DIN 17440 Grade X2CrNiMo18-15-4 Quenched Steel: Superior Corrosion Resistance & Formability