EN 10250‑2 Grade 20Mn5 Steel – Normalized & Tempered for High‑Temperature Applications

High-temperature tempered steel, application as larger forged parts for machine engineering, for steam boiler and pressure vessels. Further application for fastening elements at increased temperatures.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.82 g/cm³

Mechanical

PropertyTemperatureValueComment

Elastic modulus

-100.0 °C

217 GPa

20.0 °C

212 GPa

100.0 °C

207 GPa

200.0 °C

199 GPa

300.0 °C

192 GPa

400.0 °C

184 GPa

500.0 °C

175 GPa

600.0 °C

164 GPa

Elongation

20.0 °C

22 %

Elongation, transverse

20.0 °C

20 %

Poisson's ratio

23.0 °C

0.29 [-]

Typical for Low Carbon Steel

Shear modulus

23.0 °C

82 GPa

Typical for Low Carbon Steel

Tensile strength

20.0 °C

490 - 530 MPa

Tensile strength, transverse

20.0 °C

490 - 530 MPa

Yield strength

20.0 °C

250 - 300 MPa

Yield strength, transverse

20.0 °C

250 - 300 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1.08E-5 1/K

20.0 °C

1.19E-5 1/K

100.0 °C

1.25E-5 1/K

200.0 °C

1.3E-5 1/K

300.0 °C

1.36E-5 1/K

400.0 °C

1.41E-5 1/K

500.0 °C

1.45E-5 1/K

600.0 °C

1.49E-5 1/K

Max service temperature

500 °C

Typical for Carbon Steel

Melting point

1480 - 1526 °C

Typical for Low Carbon Steel

Specific heat capacity

-100.0 °C

423 J/(kg·K)

20.0 °C

461 J/(kg·K)

100.0 °C

479 J/(kg·K)

200.0 °C

499 J/(kg·K)

300.0 °C

517 J/(kg·K)

400.0 °C

536 J/(kg·K)

500.0 °C

558 J/(kg·K)

600.0 °C

587 J/(kg·K)

Thermal conductivity

20.0 °C

39.6 W/(m·K)

100.0 °C

41 W/(m·K)

200.0 °C

41 W/(m·K)

300.0 °C

39.9 W/(m·K)

400.0 °C

38.1 W/(m·K)

500.0 °C

35.9 W/(m·K)

600.0 °C

33.6 W/(m·K)

Thermal diffusivity

20.0 °C

11 mm²/s

100.0 °C

10.6 mm²/s

200.0 °C

9.9 mm²/s

300.0 °C

9 mm²/s

400.0 °C

8.1 mm²/s

500.0 °C

6.9 mm²/s

600.0 °C

5.7 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

2.63E-7 Ω·m

100.0 °C

3.12E-7 Ω·m

200.0 °C

3.85E-7 Ω·m

300.0 °C

4.7E-7 Ω·m

400.0 °C

5.71E-7 Ω·m

500.0 °C

6.88E-7 Ω·m

600.0 °C

8.25E-7 Ω·m

Magnetic

PropertyValueComment

Curie temperature

770 °C

Typical for Low Carbon Steel

Chemical properties

PropertyValue

Aluminium

0.02 %

Carbon

0.17 - 0.23 %

Chromium

0.4 %

Manganese

1 - 1.5 %

Molybdenum

0.1 %

Nickel

0.4 %

Phosphorus

0.04 %

Silicon

0.4 %

Sulfur

0.035 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. EN 10250-2 Grade C30 Steel – Normalized & Tempered (+NT) for High Ductility Applications
    2. EN 10250‑2 Grade C40 Steel – Normalized & Tempered (NT) – Key Properties & Applications
    3. EN 10250-2 Grade C50 Normalized & Tempered Steel – High Strength & Abrasion Resistance
    4. EN 10250-2 Grade 28Mn6 Steel – Normalized & Tempered for High-Performance Applications
    5. EN 10250‑2 Grade C35E – Normalized & Tempered Steel for High-Performance Applications
    6. EN 10250-2 Grade C45E: Normalized & Tempered Steel for Heavy‑Duty Applications
    7. EN 10250-2 Grade C55E: Normalized & Tempered Steel for Heavy-Duty Applications
    8. EN 10250-2 Grade C60E Steel – Normalized & Tempered (NT) – High-Performance Industrial Alloy
    9. EN 10250-2 Grade C35 Steel – Normalized & Tempered (NT)
    10. EN 10250‑2 Grade C22 Steel – Normalized & Tempered (NT) for High‑Performance Vehicle Components