High-Performance X6CrNiMoTi17-12-2 Steel – DIN 5512-3 Grade with +C700 Hardening

The steel is used for rail vehicle engineering acc. to the selected standard DIN 5512-3. The corresponding properties of EN 10088 shall be taken. Application example: tanks Remarks: For higher chemical loading and for welded constructions > 6 mm sheet thickness. Resistant to intercrystalline corrosion in the delivery and the welded condition.

Additional services: To ensure our customers' processes and/or products attain – and even exceed – their performance expectations, we offer a wide range of services within both the technical area and delivery logistics. Our technical services include: • Material consultations through our worldwide sales network • Advice in process optimization based on an in-depth applications knowledge • Joint new product development supported by our extensive R&D program View product groups and services

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.96 - 8 g/cm³

Mechanical

PropertyTemperatureValueComment

Elastic modulus

-100.0 °C

206 GPa

20.0 °C

196 - 200 GPa

100.0 °C

190 - 194 GPa

200.0 °C

182 - 186 GPa

300.0 °C

174 - 179 GPa

400.0 °C

166 - 172 GPa

500.0 °C

158 - 165 GPa

600.0 °C

150 GPa

700.0 °C

142 GPa

800.0 °C

134 GPa

900.0 °C

127 GPa

1000.0 °C

120 GPa

Elongation

20.0 °C

20 %

Poisson's ratio

23.0 °C

0.3 [-]

Typical for Austenitic Stainless Steel

Shear modulus

23.0 °C

77 GPa

Typical for Austenitic Stainless Steel

Tensile strength

20.0 °C

700 - 900 MPa

Yield strength Rp0.2

20.0 °C

350 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1.49E-5 1/K

20.0 °C

1.61E-5 1/K

100.0 °C

1.65E-5 - 1.67E-5 1/K

200.0 °C

1.72E-5 - 1.75E-5 1/K

300.0 °C

1.77E-5 - 1.8E-5 1/K

400.0 °C

1.81E-5 - 1.85E-5 1/K

500.0 °C

1.84E-5 - 1.9E-5 1/K

600.0 °C

1.88E-5 1/K

700.0 °C

1.91E-5 1/K

800.0 °C

1.94E-5 1/K

900.0 °C

1.97E-5 1/K

1000.0 °C

2E-5 1/K

Melting point

1230 - 1480 °C

Typical for Austenitic Stainless Steel

Specific heat capacity

-100.0 °C

440 J/(kg·K)

20.0 °C

472 - 500 J/(kg·K)

100.0 °C

487 J/(kg·K)

200.0 °C

503 J/(kg·K)

300.0 °C

512 J/(kg·K)

400.0 °C

520 J/(kg·K)

500.0 °C

530 J/(kg·K)

600.0 °C

541 J/(kg·K)

700.0 °C

551 J/(kg·K)

800.0 °C

559 J/(kg·K)

900.0 °C

565 J/(kg·K)

1000.0 °C

571 J/(kg·K)

Thermal conductivity

20.0 °C

13.3 - 15 W/(m·K)

100.0 °C

14.9 W/(m·K)

200.0 °C

16.5 W/(m·K)

300.0 °C

18.1 W/(m·K)

400.0 °C

19.5 W/(m·K)

500.0 °C

21 W/(m·K)

600.0 °C

22.4 W/(m·K)

700.0 °C

23.8 W/(m·K)

800.0 °C

25.2 W/(m·K)

Thermal diffusivity

20.0 °C

3.5 mm²/s

100.0 °C

3.8 mm²/s

200.0 °C

4 mm²/s

300.0 °C

4.3 mm²/s

400.0 °C

4.5 mm²/s

500.0 °C

4.7 mm²/s

600.0 °C

4.8 mm²/s

700.0 °C

5.1 mm²/s

800.0 °C

5.4 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

7.5E-7 - 7.91E-7 Ω·m

100.0 °C

8.45E-7 Ω·m

200.0 °C

9.19E-7 Ω·m

300.0 °C

9.77E-7 Ω·m

400.0 °C

1.03E-6 Ω·m

500.0 °C

1.08E-6 Ω·m

600.0 °C

1.12E-6 Ω·m

700.0 °C

1.15E-6 Ω·m

800.0 °C

1.18E-6 Ω·m

Chemical properties

PropertyValue

Carbon

0.08 %

Chromium

16.5 - 18.5 %

Manganese

2 %

Molybdenum

2 - 2.5 %

Nickel

10.5 - 13.5 %

Phosphorus

0.05 %

Silicon

1 %

Sulfur

0.015 %

Titanium

0.7 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. X2CrNiN18-7 Strain-Hardened Steel (DIN 5512-3) – Superior Corrosion Resistance & Toughness
    2. DIN 5512-3 X5CrNiMo17-12-2 Strain-Hardened Steel (+C700) – Ideal for Rail Vehicles & Tank Applications
    3. X6CrNiTi18-10 Grade Steel – DIN 5512-3 Strain‑Hardened with C700
    4. EN 10088-1 X6CrNiMoTi17-12-2 Strain-Hardened Steel (+C700) – High Corrosion Resistance
    5. Grade X5CrNi18-10 (C700) Strain‑Hardened Steel – DIN 5512‑3 for Rail Vehicle Applications
    6. DIN 1654-5 Grade X6CrNiMoTi17-12-2 – Quenched & Turned: Exceptional Cold-Forming & Corrosion Resistance
    7. X6CrNiTi18-10 Strain-Hardened Steel (+C700): Ti-Stabilized, Welding-Resistant, Corrosion-Resistant for Chemical & Food Industries
    8. EN 10088-1 Grade X5CrNi18-10 Strain-Hardened Steel (+C700) – Superior Corrosion Resistance & Workability
    9. DIN 1654‑5: X6CrNiMoTi17‑12‑2 Quenched Steel – Premium Cold‑Forming & Corrosion Resistance
    10. X2CrNiMoN22-5-3 Solution-Annealed Steel (Grade DIN 5512-3) – Ideal for Rail Vehicle Components