EN 10277-5 Grade C35R – Quenched, Tempered & Cold Drawn Steel for Vehicle & Engine Components

Steel C35R is suitable for slightly higher loaded parts in vehicle, engine and machine engineering with enhanced workability at constant mechanical properties (e.g. transmission parts, crank shafts, cylinder). Lowest application temperature -25°C. As a bright steel product it is used in the form of bars, bright, straight, in various conditions (see DIN EN 10277 : 1999-10).

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.82 - 7.85 g/cm³

Mechanical

PropertyTemperatureValueComment

Elastic modulus

-100.0 °C

217 GPa

20.0 °C

210 - 212 GPa

100.0 °C

205 - 207 GPa

200.0 °C

195 - 199 GPa

300.0 °C

185 - 192 GPa

400.0 °C

175 - 184 GPa

500.0 °C

175 GPa

600.0 °C

164 GPa

Elongation

20.0 °C

9 - 12 %

Poisson's ratio

23.0 °C

0.29 [-]

Typical for Medium Carbon Steel

Shear modulus

20.0 °C

81 GPa

Tensile strength

20.0 °C

550 - 950 MPa

Yield strength Rp0.2

20.0 °C

360 - 650 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1.08E-5 1/K

20.0 °C

1.19E-5 1/K

100.0 °C

1.11E-5 - 1.25E-5 1/K

200.0 °C

1.21E-5 - 1.3E-5 1/K

300.0 °C

1.29E-5 - 1.36E-5 1/K

400.0 °C

1.35E-5 - 1.41E-5 1/K

500.0 °C

1.45E-5 1/K

600.0 °C

1.49E-5 1/K

Max service temperature

500 °C

Typical for Carbon Steel

Max service temperature, long

-25 - 0 °C

Melting point

1380 - 1514 °C

Typical for Medium Carbon Steel

Specific heat capacity

-100.0 °C

423 J/(kg·K)

20.0 °C

460 - 461 J/(kg·K)

100.0 °C

479 - 480 J/(kg·K)

200.0 °C

499 - 520 J/(kg·K)

300.0 °C

517 J/(kg·K)

400.0 °C

536 - 610 J/(kg·K)

500.0 °C

558 J/(kg·K)

600.0 °C

587 J/(kg·K)

Thermal conductivity

20.0 °C

48 - 50 W/(m·K)

100.0 °C

48.9 - 51 W/(m·K)

200.0 °C

47.5 - 48.2 W/(m·K)

300.0 °C

44.7 - 45.6 W/(m·K)

400.0 °C

41.6 W/(m·K)

500.0 °C

38.6 W/(m·K)

600.0 °C

35.5 W/(m·K)

Thermal diffusivity

20.0 °C

13.3 mm²/s

100.0 °C

12.6 mm²/s

200.0 °C

11.5 mm²/s

300.0 °C

10.2 mm²/s

400.0 °C

8.9 mm²/s

500.0 °C

7.5 mm²/s

600.0 °C

6 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

1.2E-7 - 2.17E-7 Ω·m

100.0 °C

2.62E-7 Ω·m

200.0 °C

3.32E-7 Ω·m

300.0 °C

4.2E-7 Ω·m

400.0 °C

5.23E-7 Ω·m

500.0 °C

6.41E-7 Ω·m

600.0 °C

7.8E-7 Ω·m

Chemical properties

PropertyValue

Carbon

0.32 - 0.39 %

Chromium

0.4 %

Manganese

0.5 - 0.8 %

Molybdenum

0.1 %

Nickel

0.4 %

Phosphorus

0.03 - 0.04 %

Silicon

0.4 %

Sulfur

0.02 - 0.04 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. EN 10277‑5 Grade 42CrMoS4 Quenched & Tempered Cold Drawn Steel – High‑Performance, Wear‑Resistant for Automotive & Machinery
    2. EN 10277-5 Grade 34CrS4 – Quenched, Tempered & Cold Drawn Steel for Automotive & Machine Applications
    3. Grade 41CrS4 Steel – EN 10277-5 Quenched, Tempered, and Cold Drawn for Vehicle and Machine Components
    4. EN 10277-5 Grade C60R – Quenched, Tempered & Cold Drawn Steel for High-Load Applications
    5. EN 10277-5: 25CrMoS4 Steel – Quenched, Tempered & Cold Drawn (QT+C) – High Strength & Ductility for Automotive & Machinery Applications
    6. EN 10277-5 Grade 34CrNiMo6 Quenched, Tempered, and Cold‑Drawn Steel (+QT+C) – High‑Strength, Low‑Temperature Performance
    7. EN 10277-5 Grade C50E: Quenched, Tempered, Cold-Drawn Steel for Heavy Engineering
    8. EN 10277-5 Grade C50R – Quenched, Tempered & Cold-Drawn Steel for Automotive & Industrial Applications
    9. Grade C60E Steel – Quenched, Tempered & Cold‑Drawn for High‑Load Applications
    10. EN 10277-5 Grade C35E Steel: Quenched, Tempered, and Cold‑Drawn for High‑Performance Applications