EN 10095 Grade X10CrAlSi7 Soft Annealed (+A) – High‑Temperature Resistant Chrome Steel

The ferritic chrome steel X10CrAlSi7, mat. No 1.4713, shows very high resistance to oxidizing sulphureous gases, it is unsuitable for oxygen deficient and nitrogenous gases. Temperature limit for permanent operation accounts for 700 °C, scaling resistance up to 800 °C (highest application temperature in air). Application for oven components (sheet-metal brackets, tubes), in apparatus engineering for air preheater, annealing bells, pyrometer sheath tubes.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.65 - 7.7 g/cm³

Mechanical

PropertyTemperatureValueComment

Elastic modulus

20.0 °C

218 GPa

100.0 °C

213 GPa

200.0 °C

206 GPa

300.0 °C

198 GPa

400.0 °C

190 GPa

500.0 °C

180 GPa

600.0 °C

167 GPa

Elongation

20.0 °C

20 %

Elongation, transverse

20.0 °C

15 %

Hardness, Brinell

20.0 °C

192 [-]

Poisson's ratio

23.0 °C

0.3 [-]

Typical for Ferritic Stainless Steel

Shear modulus

23.0 °C

77 GPa

Typical for Ferritic Stainless Steel

Tensile strength

20.0 °C

420 - 620 MPa

Tensile strength, transverse

20.0 °C

420 - 620 MPa

Yield strength Rp0.2

20.0 °C

220 MPa

Yield strength Rp0.2, transverse

20.0 °C

220 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1E-5 1/K

20.0 °C

1.08E-5 1/K

100.0 °C

1.13E-5 1/K

200.0 °C

1.15E-5 - 1.18E-5 1/K

300.0 °C

1.23E-5 1/K

400.0 °C

1.2E-5 - 1.27E-5 1/K

500.0 °C

1.3E-5 1/K

600.0 °C

1.25E-5 - 1.32E-5 1/K

800.0 °C

1.3E-5 1/K

Max service temperature, long

0 - 700 °C

Melting point

1425 - 1530 °C

Typical for Ferritic Stainless Steel

Specific heat capacity

20.0 °C

425 - 450 J/(kg·K)

100.0 °C

461 J/(kg·K)

200.0 °C

489 J/(kg·K)

300.0 °C

508 J/(kg·K)

400.0 °C

527 J/(kg·K)

500.0 °C

550 J/(kg·K)

600.0 °C

579 J/(kg·K)

700.0 °C

618 J/(kg·K)

Thermal conductivity

20.0 °C

20.5 - 23 W/(m·K)

100.0 °C

21.9 W/(m·K)

200.0 °C

23.2 W/(m·K)

300.0 °C

24.2 W/(m·K)

400.0 °C

24.9 W/(m·K)

500.0 °C

25 - 25.4 W/(m·K)

600.0 °C

25.6 W/(m·K)

700.0 °C

25.5 W/(m·K)

Thermal diffusivity

20.0 °C

6.3 mm²/s

100.0 °C

5.9 mm²/s

200.0 °C

5.8 mm²/s

300.0 °C

5.7 mm²/s

400.0 °C

5.4 mm²/s

500.0 °C

5 mm²/s

600.0 °C

4.4 mm²/s

700.0 °C

3.8 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

7E-7 - 7.07E-7 Ω·m

100.0 °C

7.43E-7 Ω·m

200.0 °C

7.94E-7 Ω·m

300.0 °C

8.52E-7 Ω·m

400.0 °C

9.16E-7 Ω·m

500.0 °C

9.87E-7 Ω·m

600.0 °C

1.06E-6 Ω·m

700.0 °C

1.15E-6 Ω·m

Chemical properties

PropertyValue

Aluminium

0.5 - 1 %

Carbon

0.12 %

Chromium

6 - 8 %

Manganese

1 %

Phosphorus

0.04 %

Silicon

0.5 - 1 %

Sulfur

0.015 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. EN 10088-1 X70CrMo15: Soft Annealed Grade for Cutting Tools & Industrial Applications
    2. X105CrMo17 Soft Annealed Steel (EN 10088-1) – High Hardening & Wear Resistance
    3. EN 10095 NiCr22Mo9Nb Soft‑Annealed Alloy (+A) – High‑Temperature Corrosion Resistance
    4. EN 10095 NiCr15Fe Soft Annealed (+A) – High-Temperature, Corrosion-Resistant Alloy
    5. EN 10095 X18CrN28 Soft Annealed Steel – High Sulfureous Gas & Oil Ash Resistance
    6. EN 10095 X3CrAlTi18-2 Soft-Annealed Stainless Steel (+A) – High‑Temperature Performance to 1000 °C
    7. EN 10095 X10CrAlSi13 Heat‑Resistant Steel – Soft Annealed Grade (+A)
    8. EN 10095 X10CrAlSi18 Soft-Annealed Steel – High-Temperature Resistant Grade (+A)
    9. EN 10095 X10CrAlSi25 Soft Annealed Steel – High-Temperature Performance
    10. SEW 470 – Soft‑Annealed X10CrAlSi7 Chrome Steel (Grade X10CrAlSi7, +A)