EN 10095 X3CrAlTi18-2 Soft-Annealed Stainless Steel (+A) – High‑Temperature Performance to 1000 °C

The make X12Cr13 is comparable to X 10 Cr 13 acc. to DIN 17440 : 1985-07. The material is applicated for construction parts in water and steam and mild acting media of food industry, predominantly in tempered condition (fitting parts, valve spindles, shafts, pump components, bolts, screws) with hone

The make X17CrNi16-2 is comparable to X 20 CrNi 17-2 acc. to DIN 17440 :1985-07. The material is a heat-treatable 17%-chromium-steel of favorable resistance to water, low acids and bases as well as to stronger oxidizing acids (e.g. nitrous acid). Application for high loaded machine parts such as pum

Make X20Cr13 is comparable to X 20 Cr 13 acc. to DIN 17440 : 1985-07. The material is applicated for construction parts of higher strength and higher mechanical load, such as axles, shafts, pump components, piston rods, valve cones, nozzle needles, ship`s propeller, but also beater bars, surgical in

Make X30Cr13 is comparable to X 30 Cr 13 acc. to DIN 17440 : 1985-07. The material is applicated for the production of cutting tools (knife blades, scissors, cutting surgical instruments), bearing balls, wear resistant construction parts for control and pump components, springs, piston rods, screws.