EN 10028-7 Grade X2CrMoTi18-2 Soft-Annealed Steel (+A) – High Corrosion Resistance & Cold-Forming Performance

The ferritic steel X2CrMoTi18-2 has a high resistance to pitting and stress corrosion. Resistance to intercrystalline corrosion even in welded condition. Suitable for cold forming due to its low solidification tendency. Application: for cold heading parts, screws, nuts, heat-exchanger tubes and heater

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.56 - 7.7 g/cm³

Mechanical

PropertyTemperatureValueComment

Elastic modulus

20.0 °C

218 - 220 GPa

100.0 °C

213 - 215 GPa

200.0 °C

206 - 210 GPa

300.0 °C

198 - 205 GPa

400.0 °C

190 - 195 GPa

500.0 °C

180 GPa

600.0 °C

167 GPa

700.0 °C

150 GPa

Elongation

20.0 °C

20 %

Elongation A80

20.0 °C

20 %

Elongation A80, transverse

20.0 °C

20 %

Elongation, transverse

20.0 °C

20 %

Poisson's ratio

23.0 °C

0.3 [-]

Typical for Ferritic Stainless Steel

Shear modulus

23.0 °C

77 GPa

Typical for Ferritic Stainless Steel

Tensile strength

20.0 °C

420 - 640 MPa

Tensile strength, transverse

20.0 °C

420 - 640 MPa

Yield strength Rp0.2

20.0 °C

300 MPa

100.0 °C

250 MPa

150.0 °C

240 MPa

200.0 °C

230 MPa

250.0 °C

220 MPa

300.0 °C

210 MPa

350.0 °C

205 MPa

Yield strength Rp0.2, transverse

20.0 °C

320 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

20.0 °C

9.9E-6 1/K

100.0 °C

1.03E-5 - 1.04E-5 1/K

200.0 °C

1.08E-5 1/K

300.0 °C

1.12E-5 1/K

400.0 °C

1.16E-5 1/K

500.0 °C

1.19E-5 1/K

600.0 °C

1.21E-5 1/K

700.0 °C

1.24E-5 1/K

800.0 °C

1.29E-5 1/K

Melting point

1425 - 1530 °C

Typical for Ferritic Stainless Steel

Specific heat capacity

20.0 °C

430 - 450 J/(kg·K)

100.0 °C

482 J/(kg·K)

200.0 °C

506 J/(kg·K)

300.0 °C

525 J/(kg·K)

400.0 °C

547 J/(kg·K)

500.0 °C

576 J/(kg·K)

600.0 °C

616 J/(kg·K)

Thermal conductivity

20.0 °C

16 - 23 W/(m·K)

100.0 °C

17.2 W/(m·K)

200.0 °C

18.6 W/(m·K)

300.0 °C

20 W/(m·K)

400.0 °C

21.2 W/(m·K)

500.0 °C

22.3 W/(m·K)

600.0 °C

23.3 W/(m·K)

700.0 °C

24.1 W/(m·K)

800.0 °C

25.5 W/(m·K)

900.0 °C

26.9 W/(m·K)

1000.0 °C

28.3 W/(m·K)

Thermal diffusivity

20.0 °C

4.7 mm²/s

100.0 °C

4.5 mm²/s

200.0 °C

4.5 mm²/s

300.0 °C

4.6 mm²/s

400.0 °C

4.4 mm²/s

500.0 °C

4.1 mm²/s

600.0 °C

3.6 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

8E-7 - 9.06E-7 Ω·m

100.0 °C

9.42E-7 Ω·m

200.0 °C

9.87E-7 Ω·m

300.0 °C

1.03E-6 Ω·m

400.0 °C

1.08E-6 Ω·m

500.0 °C

1.12E-6 Ω·m

600.0 °C

1.18E-6 Ω·m

700.0 °C

1.22E-6 Ω·m

800.0 °C

1.24E-6 Ω·m

900.0 °C

1.26E-6 Ω·m

1000.0 °C

1.27E-6 Ω·m

Chemical properties

PropertyValue

Carbon

0.025 %

Chromium

17 - 20 %

Manganese

1 %

Molybdenum

1.8 - 2.5 %

Nitrogen

0.03 %

Phosphorus

0.04 %

Silicon

1 %

Sulfur

0.015 %

Titanium

0.8 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. EN 10088-1 X70CrMo15: Soft Annealed Grade for Cutting Tools & Industrial Applications
    2. X105CrMo17 Soft Annealed Steel (EN 10088-1) – High Hardening & Wear Resistance
    3. EN 10083-2 Grade C50R Soft Annealed Steel (+A) – High Strength & Workability
    4. EN 10028-7 Grade X2CrMoTi18-2: Solution-Annealed Ferritic Steel (+AT) – Superior Corrosion Resistance & Cold Forming
    5. EN 10028-7 Grade X6CrNiTi12 Soft Annealed Steel (+A) – Superior Mechanical Performance
    6. EN 10028-7 Grade X2CrTiNb18 Stainless Steel – Soft Annealed (A)
    7. EN 10088‑1 Grade X2CrMoTi18‑2 Soft‑Annealed Steel – Superior Corrosion Resistance & Cold‑Formability
    8. EN 10028-7 X2CrTi17 Stainless Steel – Soft Annealed, Low-Carbon, High-Performance Grade
    9. EN 10028-7 X3CrTi17 Soft-Annealed Steel – High Corrosion Resistance & Heat-Resistant Properties
    10. EN 10028-7 Grade X2CrNi12 Soft Annealed Steel (+A) – High Corrosion Resistance & Strength