EN 10028-7 Grade X2CrNiMoN17-13-3 – Solution-Annealed Stainless Steel for High-Performance Applications

The steel X2CrNiMoN17-13-3 is a fully austenitic mirror-polishable steel showing higher strength by N-alloying and higher corrosion resistance especially to unoxidizing and halogenated media than 1.4406 by higher Mo-addition. Higher resistance to selective attack than 1.4435, excellent fatigue strength behavior even under chemical load. Favorable cryogenic ductility, therefore usable up to -270 °C in refrigeration, approved for pressure vessel construction.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

8 - 8.01 g/cm³

Mechanical

PropertyTemperatureValue

Elastic modulus

-100.0 °C

206 GPa

20.0 °C

196 - 200 GPa

100.0 °C

190 - 194 GPa

200.0 °C

182 - 186 GPa

300.0 °C

174 - 179 GPa

400.0 °C

166 - 172 GPa

500.0 °C

158 - 165 GPa

600.0 °C

150 GPa

700.0 °C

142 GPa

800.0 °C

134 GPa

Elongation

-196.0 °C

30 %

-150.0 °C

30 %

-80.0 °C

30 %

20.0 °C

35 %

Elongation A80, transverse

20.0 °C

35 - 40 %

Elongation, transverse

20.0 °C

35 - 40 %

Poisson's ratio

20.0 °C

0.28 [-]

Shear modulus

20.0 °C

77.3 GPa

Tensile strength

-196.0 °C

1150 MPa

-150.0 °C

1000 MPa

-80.0 °C

800 MPa

20.0 °C

580 - 780 MPa

50.0 °C

557 MPa

100.0 °C

520 MPa

150.0 °C

490 MPa

200.0 °C

460 MPa

250.0 °C

450 MPa

300.0 °C

440 MPa

350.0 °C

435 MPa

400.0 °C

435 MPa

500.0 °C

430 MPa

Tensile strength, transverse

20.0 °C

580 - 780 MPa

Yield strength Rp0.2

-196.0 °C

600 MPa

-150.0 °C

500 MPa

-80.0 °C

380 MPa

20.0 °C

280 MPa

50.0 °C

254 MPa

100.0 °C

211 MPa

150.0 °C

185 MPa

200.0 °C

167 MPa

250.0 °C

155 MPa

300.0 °C

145 MPa

350.0 °C

140 MPa

400.0 °C

135 MPa

450.0 °C

131 MPa

500.0 °C

129 MPa

550.0 °C

127 MPa

Yield strength Rp0.2, transverse

20.0 °C

280 - 300 MPa

Yield strength Rp1.0

-196.0 °C

700 MPa

-150.0 °C

600 MPa

-80.0 °C

450 MPa

20.0 °C

320 MPa

50.0 °C

292 MPa

100.0 °C

246 MPa

150.0 °C

218 MPa

200.0 °C

198 MPa

250.0 °C

183 MPa

300.0 °C

175 MPa

350.0 °C

169 MPa

400.0 °C

164 MPa

450.0 °C

160 MPa

500.0 °C

158 MPa

550.0 °C

157 MPa

Yield strength Rp1.0, transverse

20.0 °C

320 - 330 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1.49E-5 1/K

20.0 °C

1.61E-5 1/K

100.0 °C

1.6E-5 - 1.67E-5 1/K

200.0 °C

1.65E-5 - 1.72E-5 1/K

300.0 °C

1.7E-5 - 1.77E-5 1/K

400.0 °C

1.75E-5 - 1.81E-5 1/K

500.0 °C

1.8E-5 - 1.84E-5 1/K

600.0 °C

1.88E-5 1/K

700.0 °C

1.91E-5 1/K

800.0 °C

1.94E-5 1/K

900.0 °C

1.97E-5 1/K

1000.0 °C

2E-5 1/K

Max service temperature, long

-270 - 0 °C

Melting point

1230 - 1480 °C

Typical for Austenitic Stainless Steel

Specific heat capacity

-100.0 °C

440 J/(kg·K)

20.0 °C

472 - 500 J/(kg·K)

100.0 °C

487 J/(kg·K)

200.0 °C

503 J/(kg·K)

300.0 °C

512 J/(kg·K)

400.0 °C

520 J/(kg·K)

500.0 °C

530 J/(kg·K)

600.0 °C

541 J/(kg·K)

700.0 °C

551 J/(kg·K)

800.0 °C

559 J/(kg·K)

900.0 °C

565 J/(kg·K)

1000.0 °C

571 J/(kg·K)

Thermal conductivity

20.0 °C

13.5 - 15 W/(m·K)

100.0 °C

14.9 W/(m·K)

200.0 °C

16.7 W/(m·K)

300.0 °C

18.3 W/(m·K)

400.0 °C

19.8 W/(m·K)

500.0 °C

21.3 W/(m·K)

600.0 °C

22.7 W/(m·K)

700.0 °C

24.2 W/(m·K)

800.0 °C

25.6 W/(m·K)

Thermal diffusivity

20.0 °C

3.6 mm²/s

100.0 °C

3.7 mm²/s

200.0 °C

4 mm²/s

300.0 °C

4.4 mm²/s

400.0 °C

4.6 mm²/s

500.0 °C

4.7 mm²/s

600.0 °C

4.9 mm²/s

700.0 °C

5.2 mm²/s

800.0 °C

5.5 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

7.5E-7 - 7.75E-7 Ω·m

100.0 °C

8.42E-7 Ω·m

200.0 °C

9.04E-7 Ω·m

300.0 °C

9.62E-7 Ω·m

400.0 °C

1.01E-6 Ω·m

500.0 °C

1.06E-6 Ω·m

600.0 °C

1.1E-6 Ω·m

700.0 °C

1.13E-6 Ω·m

800.0 °C

1.16E-6 Ω·m

Chemical properties

PropertyValue

Carbon

0.03 %

Chromium

16.5 - 18.5 %

Manganese

2 %

Molybdenum

2.5 - 3 %

Nickel

11 - 14 %

Nitrogen

0.12 - 0.22 %

Phosphorus

0.05 %

Silicon

1 %

Sulfur

0.015 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. EN 10028-7 Grade X2CrTi17 – Solution-Annealed Ferritic Stainless Steel for Automotive, Electrical, and Household Use
    2. X3CrTi17 Ferritic Steel – EN 10028-7 Grade, Solution Annealed (+AT) – Superior Corrosion Resistance
    3. EN 10028-7 Grade X2CrMoTi18-2: Solution-Annealed Ferritic Steel (+AT) – Superior Corrosion Resistance & Cold Forming
    4. EN 10028-7 Grade X2CrNi12: Solution-Annealed Steel with Superior Corrosion Resistance
    5. EN 10269 X2CrNiMoN17-13-3 – High‑Strength, Corrosion‑Resistant Austenitic Steel, Solution Annealed (+AT)
    6. EN 10222-5 Grade X2CrNiMoN17-13-3 – Solution Annealed Steel with Superior Corrosion Resistance
    7. EN 10250-4 X2CrNiMoN17-13-3 Steel – Solution Annealed, Enhanced Corrosion Resistance
    8. EN 10217‑7 Grade X2CrNiMoN17‑13‑3 – Solution Annealed Steel for Corrosion‑Resistant, High‑Temperature Applications
    9. EN 10028-7 Grade X6CrNi23-13 Solution Annealed Steel – High-Temperature Resistant Alloy
    10. EN 10028-7 Grade X6CrNi25-20: Solution-Annealed Austenitic Steel for High-Temperature Applications