WL 3.4394 T7452 High‑Strength Steel – Superior Fracture Toughness & Corrosion Resistance
The high-strength material has a high fracture toughness also for larger thicknesses and resistance to stress corrosion also in the ST direction and exfoliation corrosion. It has a low distortion post machining. Application: integral and fittings of larger dimensions
Properties
General
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Density | 2.82 g/cm³ | T7452 | WL 3.4394 | Sheet, Strip, Bar, Wire |
Mechanical
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
Elastic modulus | 70.0 GPa | T7452 | WL 3.4394 | Sheet, Strip, Bar, Wire | ||
Elongation | 9.0 % | T7452 | WL 3.4394 | Sheet, Strip, Bar, Wire | A50 | |
20.0 °C | 9.0 % | T7452 | WL 3.4394 | Forging | ||
Hardness, Brinell | 135.0 [-] | T7452 | WL 3.4394 | Sheet, Strip, Bar, Wire | ||
20.0 °C | 135.0 [-] | T7452 | WL 3.4394 | Forging | ||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 7000 Series Aluminium | ||||
Poisson's ratio | 0.33 [-] | Typical for Wrought 7000 Series Aluminium | ||||
Shear modulus | 27.0 GPa | T7452 | WL 3.4394 | Sheet, Strip, Bar, Wire | ||
Tensile strength | 480.0 MPa | T7452 | WL 3.4394 | Sheet, Strip, Bar, Wire | ||
490.0 MPa | T7452 | WL 3.4394 | Sheet, Strip, Bar, Wire | |||
495.0 MPa | T7452 | WL 3.4394 | Sheet, Strip, Bar, Wire | |||
20.0 °C | 460.0 MPa | T7452 | WL 3.4394 | Forging | ||
20.0 °C | 470.0 MPa | T7452 | WL 3.4394 | Forging | ||
20.0 °C | 475.0 MPa | T7452 | WL 3.4394 | Forging | ||
20.0 °C | 480.0 MPa | T7452 | WL 3.4394 | Forging | ||
20.0 °C | 490.0 MPa | T7452 | WL 3.4394 | Forging | ||
20.0 °C | 495.0 MPa | T7452 | WL 3.4394 | Forging |
Thermal
| Property | Value | Comment |
|---|---|---|
Coefficient of thermal expansion | 2.1e-05 - 2.4e-05 1/K | Typical for Wrought 7000 Series Aluminium |
Melting point | 465.0 - 655.0 °C | Typical for Wrought 7000 Series Aluminium |
Specific heat capacity | 795.0 - 1050.0 J/(kg·K) | Typical for Wrought 7000 Series Aluminium |
Thermal conductivity | 121.0 - 170.0 W/(m·K) | Typical for Wrought 7000 Series Aluminium |
Electrical
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Electrical conductivity | 23000000.0 - 25000000.0 S/m | T7452 | WL 3.4394 | Sheet, Strip, Bar, Wire |
Electrical resistivity | 4e-08 - 4.35e-08 Ω·m | T7452 | WL 3.4394 | Sheet, Strip, Bar, Wire |
Chemical properties
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Chromium | 0.05 % | T7452 | WL 3.4394 | Forging, Sheet, Strip, Bar, Wire |
Copper | 1.5 - 2.0 % | T7452 | WL 3.4394 | Forging, Sheet, Strip, Bar, Wire |
Iron | 0.15 % | T7452 | WL 3.4394 | Forging |
0.15 % | T7452 | WL 3.4394 | Sheet, Strip, Bar, Wire | |
Magnesium | 2.1 - 2.6 % | T7452 | WL 3.4394 | Forging, Sheet, Strip, Bar, Wire |
Manganese | 0.1 % | T7452 | WL 3.4394 | Forging, Sheet, Strip, Bar, Wire |
Nickel | 0.05 % | T7452 | WL 3.4394 | Forging, Sheet, Strip, Bar, Wire |
Silicon | 0.12 % | T7452 | WL 3.4394 | Forging, Sheet, Strip, Bar, Wire |
Titanium | 0.06 % | T7452 | WL 3.4394 | Forging, Sheet, Strip, Bar, Wire |
Zinc | 5.7 - 6.7 % | T7452 | WL 3.4394 | Forging, Sheet, Strip, Bar, Wire |
Zirconium | 0.1 - 0.16 % | T7452 | WL 3.4394 | Forging, Sheet, Strip, Bar, Wire |
Technological properties
| Property | ||
|---|---|---|
| Brazing | Excellent | |
Metal
- EN 10305-5 Grade St 33 Welded Precision Steel Tubes
- BS 3100 Grade A1 Steel Specifications & Properties
- WL 3.2364 T5: Superior Weldable Cast Alloy for High-Integrity Applications
- AA 7175 T7452 Aluminium Alloy – Standard and Key Properties
- WL 3.4394 T7451 Steel – High Strength, Toughness & Corrosion Resistance
- WL 3.4394 T74 Steel: High Strength, Superior Toughness & Corrosion Resistance for Large-Scale Applications
- AA 7050 T7452 – High‑Strength, Heat‑Treatable Aluminium Alloy for Aerospace
- DIN 3.4144 T7452: High-Strength, Corrosion-Resistant Aerospace Alloy
- WL 3.4334-1 Grade 3.4334 T7452 – High-Performance Forged Aviation Alloy
- WL 3.4354-1 (Grade 3.4354) – T7452: High‑Strength, Corrosion‑Resistant Al‑Zn‑Mg Alloy