DIN 17851 Grade TiAl6V4: Premium Artificially Aged Titanium Alloy – High Strength & Toughness

Titanium DIN TiAl6V4 alloy is the most commercially available of all titanium alloys. It offers an excellent combination of high strength and toughness. DIN TiAl6V4 titanium has good welding and fabrication characteristics.

Properties

General

PropertyTemperatureValueConditionRelated StandardsShape

Density

20.0 °C

4.43 g/cm³

Artificially Aged

DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860

Forging, Rod

Mechanical

PropertyTemperatureValueConditionRelated StandardsShape

Elastic modulus

-269.0 °C

119.6 GPa

Artificially Aged

DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860

Forging, Rod

-195.0 °C

118.2 GPa

Artificially Aged

DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860

Forging, Rod

20.0 °C

110.0 GPa

Artificially Aged

DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860

Forging, Rod

27.0 °C

109.2 GPa

Artificially Aged

DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860

Forging, Rod

200.0 °C

98.0 GPa

Artificially Aged

DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860

Forging, Rod

400.0 °C

84.0 GPa

Artificially Aged

DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860

Forging, Rod

Elongation

20.0 °C

8.0 %

Artificially Aged

DIN 17862, WL 3.7164-1, DIN 17851, DIN 17864, DIN 17860

Rod, Forging

Hardness, Brinell

20.0 °C

310.0

Artificially Aged

DIN 17862, WL 3.7164-1, DIN 17851, DIN 17864, DIN 17860

Rod

Poisson's ratio

-269.0 °C

0.311 [-]

Artificially Aged

DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860

Forging, Rod

-195.0 °C

0.327 [-]

Artificially Aged

DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860

Forging, Rod

27.0 °C

0.333 [-]

Artificially Aged

DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860

Forging, Rod

Reduction of area

20.0 °C

15.0 %

Artificially Aged

DIN 17862, WL 3.7164-1, DIN 17851, DIN 17864, DIN 17860

Rod, Forging

20.0 °C

20.0 %

Artificially Aged

DIN 17862, WL 3.7164-1, DIN 17851, DIN 17864, DIN 17860

Forging

Shear modulus

20.0 °C

43.0 GPa

Artificially Aged

WL 3.7164-1, DIN 17851, DIN 17862, DIN 17864, DIN 17860

Forging, Rod

Tensile strength

20.0 °C

1060.0 MPa

Artificially Aged

DIN 17862, WL 3.7164-1, DIN 17851, DIN 17864, DIN 17860

Forging

20.0 °C

1070.0 MPa

Artificially Aged

DIN 17862, WL 3.7164-1, DIN 17851, DIN 17864, DIN 17860

Rod, Forging

20.0 °C

1100.0 MPa

Artificially Aged

DIN 17862, WL 3.7164-1, DIN 17851, DIN 17864, DIN 17860

Forging, Rod

20.0 °C

1180.0 MPa

Artificially Aged

DIN 17862, WL 3.7164-1, DIN 17851, DIN 17864, DIN 17860

100.0 °C

1090.0 MPa

Artificially Aged

DIN 17862, WL 3.7164-1, DIN 17851, DIN 17864, DIN 17860

200.0 °C

1000.0 MPa

Artificially Aged

DIN 17862, WL 3.7164-1, DIN 17851, DIN 17864, DIN 17860

300.0 °C

910.0 MPa

Artificially Aged

DIN 17862, WL 3.7164-1, DIN 17851, DIN 17864, DIN 17860

400.0 °C

855.0 MPa

Artificially Aged

DIN 17862, WL 3.7164-1, DIN 17851, DIN 17864, DIN 17860

500.0 °C

735.0 MPa

Artificially Aged

DIN 17862, WL 3.7164-1, DIN 17851, DIN 17864, DIN 17860

Thermal

PropertyTemperatureValueConditionRelated StandardsShapeComment

Coefficient of thermal expansion

7.699999999999999e-06 - 1e-05 1/K

Typical for Titanium Alpha Beta Alloy

Melting point

1500.0 - 1750.0 °C

Typical for Titanium Alpha Beta Alloy

Specific heat capacity

370.0 - 674.0 J/(kg·K)

Typical for Titanium Alpha Beta Alloy

Thermal conductivity

20.0 °C

7.12 W/(m·K)

Artificially Aged

DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860

Forging, Rod

Electrical

PropertyTemperatureValueConditionRelated StandardsShape

Electrical resistivity

20.0 °C

1.71e-06 Ω·m

Artificially Aged

DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860

Forging, Rod

Chemical properties

PropertyValueConditionRelated StandardsShape

Aluminium

5.5 - 6.75 %

Artificially Aged

DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860

Forging, Rod

Carbon

0.08

Artificially Aged

DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860

Forging, Rod

Hydrogen

0.015

Artificially Aged

DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860

Forging, Rod

Iron

0.3

Artificially Aged

DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860

Forging, Rod

Nitrogen

0.05

Artificially Aged

DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860

Forging, Rod

Oxygen

0.2

Artificially Aged

DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860

Forging, Rod

Titanium

87.7 %

Artificially Aged

DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860

Forging, Rod

Vanadium

3.5 - 4.5 %

Artificially Aged

DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860

Forging, Rod


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. DIN 17851 Ti1Pd Alloy: High Corrosion Resistance & Excellent Weldability
    2. DIN 17851 Ti2Pd Grade – Superior Welded Titanium for Corrosion Resistance
    3. DIN 17864 TiAl6Zr5Mo0.5Si: Artificially Aged High‑Temperature Alloy
    4. DIN 17851 TiAl5Fe2.5 Annealed – High Strength, Corrosion Resistance & Biocompatibility
    5. DIN 17743 NiCu30Al: High-Temperature, Creep-Resistant Alloy for Corrosion-Resistant Applications
    6. DIN 17851 TiAl6Sn2Zr4Mo2Si: High-Strength, Artificially Aged Titanium Alloy
    7. DIN 17851 TiAl6V6Sn2 – Premium High-Strength, Corrosion-Resistant Titanium Alloy
    8. DIN 1614-1 Grade St 22: Premium Cold-Rolled Steel for Industrial Applications
    9. DIN 17851 TiAl6V6Sn2 Annealed Alloy: Superior Strength & Corrosion Resistance for Aerospace
    10. DIN 17851 Grade 3.7185 Titanium Billets – Premium Quality & Versatile Applications