The alloy AlZn1 is nature hard. A strength increase can be achieved only by cold forming, not by a purposeful heat treatment. It is used due to its good corrosion resistance mainly as plating material. The alloy AlZn1 is well hot and cold formable and weldable, but it can be worked on less well spli

The steel C 10 Pb is used for smaller parts with low core strength and good machinability in the vehicle and mechanical engineering (e.g. pins, lever, mandrels). The lowest application amounts to -25 °C, the best application from 5 to 10 mm nominal size.PropertiesGeneralPropertyTemperatureValueDensi

The steel C 15 Pb is used for parts with a little higher core strength and better machinability in the vehicle and mechanical engineering (e.g. pins, lever, driver). The lowest application amounts to -25 °C, the best application from 5 to 10 mm nominal size.PropertiesGeneralPropertyTemperatureValueD

G-AlCu4Ti - solidifies in an wide range of temperature - complicated casting - application in part hardend or warm hardend state - applicable for simple cast pieces, with high demands to strength and toughness application: - wear resistant construction parts in automobile, machine and aircraft indu