EN 10088‑1 Grade X2CrTi17 Soft‑Annealed Stainless Steel (+A) – Low‑Carbon, Corrosion‑Resistant for Industrial Use

Material X2CrTi17 is comparable to X 1 CrTi 15 nach SEW 400 : 1991-02. This material is a stainless steel with an extremely low carbon content for special applications in household, automotive and electrical industry. It is resistant to intercrystalline corrosion both in delivery and welded condition.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.7 - 7.73 g/cm³

Mechanical

PropertyTemperatureValue

Elastic modulus

20.0 °C

217 - 220 GPa

100.0 °C

215 GPa

200.0 °C

188 - 210 GPa

300.0 °C

164 - 205 GPa

400.0 °C

195 GPa

Elongation

20.0 °C

8 - 24 %

Elongation A80

20.0 °C

24 %

Elongation A80, transverse

20.0 °C

24 %

Elongation, transverse

20.0 °C

24 %

Hardness, Brinell

20.0 °C

200 [-]

Poisson's ratio

20.0 °C

0.29 [-]

Shear modulus

20.0 °C

84.82 GPa

Tensile strength

20.0 °C

380 - 750 MPa

Tensile strength, transverse

20.0 °C

380 - 530 MPa

Yield strength Rp0.2

20.0 °C

180 - 320 MPa

100.0 °C

190 - 195 MPa

150.0 °C

180 MPa

200.0 °C

170 MPa

250.0 °C

160 MPa

300.0 °C

155 MPa

Yield strength Rp0.2, transverse

20.0 °C

200 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

20.0 °C

1.02E-5 1/K

100.0 °C

1.04E-5 - 1.05E-5 1/K

200.0 °C

1.08E-5 - 1.09E-5 1/K

300.0 °C

1.12E-5 - 1.13E-5 1/K

400.0 °C

1.16E-5 1/K

500.0 °C

1.19E-5 - 1.2E-5 1/K

600.0 °C

1.22E-5 1/K

Melting point

1425 - 1530 °C

Typical for Ferritic Stainless Steel

Specific heat capacity

20.0 °C

430 - 439 J/(kg·K)

100.0 °C

474 J/(kg·K)

200.0 °C

498 J/(kg·K)

300.0 °C

517 J/(kg·K)

400.0 °C

538 J/(kg·K)

500.0 °C

564 J/(kg·K)

600.0 °C

598 J/(kg·K)

Thermal conductivity

20.0 °C

20 - 25.9 W/(m·K)

100.0 °C

25.3 W/(m·K)

200.0 °C

25.2 W/(m·K)

300.0 °C

25.2 W/(m·K)

400.0 °C

25.4 W/(m·K)

500.0 °C

25.7 W/(m·K)

600.0 °C

25.9 W/(m·K)

Thermal diffusivity

20.0 °C

7.6 mm²/s

100.0 °C

6.6 mm²/s

200.0 °C

6.1 mm²/s

300.0 °C

5.8 mm²/s

400.0 °C

5.3 mm²/s

500.0 °C

4.8 mm²/s

600.0 °C

4.1 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

5.59E-7 - 7E-7 Ω·m

100.0 °C

6.4E-7 Ω·m

200.0 °C

7.32E-7 Ω·m

300.0 °C

8.17E-7 Ω·m

400.0 °C

8.97E-7 Ω·m

500.0 °C

9.74E-7 Ω·m

600.0 °C

1.05E-6 Ω·m

Chemical properties

PropertyValue

Carbon

0.025 %

Chromium

16 - 18 %

Manganese

0.5 %

Nitrogen

0.02 %

Phosphorus

0.04 %

Silicon

0.5 %

Sulfur

0.015 %

Titanium

0.3 - 0.6 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. EN 10088-1 X70CrMo15: Soft Annealed Grade for Cutting Tools & Industrial Applications
    2. X105CrMo17 Soft Annealed Steel (EN 10088-1) – High Hardening & Wear Resistance
    3. EN 10088-1 Grade X90CrMoV18 – Soft Annealed Steel for High‑Performance Cutting Tools
    4. EN 10088‑1 Grade X2CrMoTiS18‑2 Soft‑Annealed Steel (+A) – Premium Ferritic Properties
    5. EN 10088-1 X50CrMoV15 Soft-Annealed Steel: High Strength & Abrasion Resistance
    6. EN 10088-1 Grade X2CrMoTi29-4 Soft-Annealed Steel for Cold-Rolled Strips
    7. EN 10088-1 Grade X2CrAlTi18-2 Soft-Annealed Steel – Superior Corrosion Resistance & Mechanical Performance
    8. EN 10088-1 X6CrNi17-1 Soft‑Annealed Steel (+A) – High Corrosion Resistance & Strength
    9. EN 10088‑1 X6CrNiTi12 Soft‑Annealed Steel – Grade X6CrNiTi12 (+A) – Specifications & Properties
    10. EN 10088-1 X2CrMoTi17-1 Soft Annealed Steel – Superior Formability for Appliances & Pipes