The cold-upsettable steel 25 CrMo 4 can be cold-formed with a medium to high rate of forming according to the usual forming methods on single-stage and multi-stage presses. It is used for screws and pressed parts of strength class in the medium dimension range.PropertiesGeneralPropertyTemperatureVal

The cold-upsettable steel 25 CrMo 4 can be cold-formed with a medium to high rate of forming according to the usual forming methods on single-stage and multi-stage presses. It is used for screws and pressed parts of strength class in the medium dimension range.PropertiesGeneralPropertyTemperatureVal

The cold-upsettable steel 25 CrMo 4 can be cold-formed with a medium to high rate of forming according to the usual forming methods on single-stage and multi-stage presses. It is used for screws and pressed parts of strength class in the medium dimension range.PropertiesGeneralPropertyTemperatureVal

The cold-upsettable steel 21 NiCrMo 2 is suitable for the manufacture of screws and nuts (soft-annealed condition with pre- and/or post treatment) used in automobile, motor and equipment construction and in general engineering. The steel finds additional use, amongst other things, for drive sprocket

The cold-upsettable steel 21 NiCrMo 2 is suitable for the manufacture of screws and nuts (soft-annealed condition with pre- and/or post treatment) used in automobile, motor and equipment construction and in general engineering. The steel finds additional use, amongst other things, for drive sprocket

The cold-upsettable steel 21 NiCrMo 2 is suitable for the manufacture of screws and nuts (soft-annealed condition with pre- and/or post treatment) used in automobile, motor and equipment construction and in general engineering. The steel finds additional use, amongst other things, for drive sprocket

The cold-upsettable steel 15 CrNi 6 is suitable for the manufacture of screws and nuts (soft-annealed condition with pre- and/or post treatment) used in automobile, motor and equipment construction and in general engineering. The steel finds additional use, amongst other things, for drive sprockets,

The cold-upsettable steel 15 CrNi 6 is suitable for the manufacture of screws and nuts (soft-annealed condition with pre- and/or post treatment) used in automobile, motor and equipment construction and in general engineering. The steel finds additional use, amongst other things, for drive sprockets,

The cold-upsettable steel 15 CrNi 6 is suitable for the manufacture of screws and nuts (soft-annealed condition with pre- and/or post treatment) used in automobile, motor and equipment construction and in general engineering. The steel finds additional use, amongst other things, for drive sprockets,

Steel Cm 60 is suitable for high strained parts in vehicle manufacturing, engine and machine engineering that require an enhanced workability while maintaining strength qualities (e.g. gear wheels, pinion, shafts). Lowest application temp. -25 °C.PropertiesGeneralPropertyTemperatureValueDensity20.0

Steel 34 CrMo 4 is suitable for parts of high strength and ductility requirements at mean and higher heat-treatment sections (also heavy forged parts) in vehicle manufacturing, engine and machine engineering (e.g. shafts, wheel gears, steering knuckles). The steel shows a high specific mechanical r

Steel 34 CrMo 4 is suitable for parts of high strength and ductility requirements at mean and higher heat-treatment sections (also heavy forged parts) in vehicle manufacturing, engine and machine engineering (e.g. shafts, wheel gears, steering knuckles). The steel shows a high specific mechanical r

PropertiesGeneralPropertyTemperatureValueCommentDensity20.0 °C2.65 - 2.7 g/cm³Typical for Wrought 5000 Series AluminiumMechanicalPropertyTemperatureValueCommentElastic modulus20.0 °C69 - 70 GPaTypical for Wrought 5000 Series AluminiumFracture toughness20.0 °C22 - 35 MPa·√mTypical for Wrought 5000 Se

The austenitic material GX5CrNiMoNb19-11-2 is equivalent to trademark G-X 5CrNiMoNb 18 10 acc. to DIN 17445-84. This ic-resistant material is used for fittings, pumps, agitators, tanks in chemical industry, in cellulose, rayon staple, textile, color and rubber industry. It is weldable without prehea

The austenitic material GX2NiCrMo28-20-2 is mostly used in pressure vessel construction. It is weldable with preheating (20 to 100 °C).PropertiesGeneralPropertyTemperatureValueDensity20.0 °C8 g/cm³MechanicalPropertyTemperatureValueCommentElastic modulus23.0 °C195 GPaTypical for Austenitic Stainless

The austenitic material GX2CrNiMo19-11-2 is mostly used for pressure vessels. It is weldable without preheating and heat after treatment.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.9 g/cm³MechanicalPropertyTemperatureValueCommentElastic modulus23.0 °C195 GPaTypical for Austenitic Stainl

The fully killed machining steel 60 S 20 is used for mass parts of highest strength, especially for lower toughness demands cross-sectional. It has advantages regarding a higher cutting speed. Application in the automotive engineering, toolbuilding, apparatus engineering (screws, nuts, smal parts).P

The fully killed machining steel 45 S 20 is used for mass parts of higher strength, especially for lower toughness demands cross-sectional. It has advantages regarding a higher cutting speed. Application in the automotive engineering, toolbuilding, apparatus engineering (screws, nuts, smal parts).Pr

The fully killed machining steel 35 S 20 is used for mass parts of mean strength, especially for lower toughness demands cross-sectional. It has advantages regarding a higher cutting speed. Application in the automotive engineering, toolbuilding, apparatus engineering (screws, nuts, smal parts).Prop

GS-18 CrMo 9 10 is used for thick-walled cast pieces at high temperatures and pressures.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.85 g/cm³MechanicalPropertyTemperatureValueCommentElastic modulus20.0 °C211 GPa100.0 °C204 GPa200.0 °C196 GPa300.0 °C186 GPa400.0 °C177 GPa500.0 °C164 GPa60