Temperable high strength steel with good high temperature strength up to 580 °C and resistance to scaling up to 600 °C. Application: pressure vessel and pipeline construction, turbine construction, chemicals industry, reactor engineering, screws, nutsPropertiesGeneralPropertyTemperatureValueDensity2

44 Cr 2 is an anti-friction bearing steel that can be refined and induction hardened. In the Jominy test it reaches surface hardnesses of approximately 62 HRC. It is used for discs and anti-friction bearing parts of larger dimensions.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.8 - 7.85

The nitriding steel 34 CrAlNi 7 can undergo quenchhardening and is used for heavy machine parts, piston rods, plunger pistons, spindles with particularly large dimensions. The steel contains a nitride agent (Cr and Al) which contributes through the nitriding process or the nitro-carburization proces

The nitriding steel 34 CrAlMo 5 can undergo quenchhardening and is used for parts of hot steam fittings that have a high fatigue strength at temperatures from 350 to 500 degrees C. Suitable for dimensions of up to 80 mm. Construction components: valve spindles and plates. Further use: plunger piston

The nitriding steel 31 CrMoV 9 can undergo quenchhardening and is used for parts for hot steam fittings, valve spindles, crank shafts, and similarly stressed wear parts that have a dimension of up to 100 mm. The steel contains a nitride agent (Cr) which contributes through the nitriding process or t

The fine grained steel WStE 460 (high temperature grade) is used for welded constructions of different kind like pressure vessels, stationary or mobile storage tanks, high pressure lines, bridge and support constructions etc. The application temperature of the high temperature grade amounts to 400 °

The fine grained steel TStE 500 is used for welded constructions of different kind like pressure vessels, stationary or mobile storage tanks, high pressure lines, bridge and support constructions etc. The application temperature of the tough at subzero temperatures grade amounts to -50 °C.Properties

The fine grained steel StE 500 is used for welded constructions of different kind like pressure vessels, stationary or mobile storage tanks, high pressure lines, bridge and support constructions etc. The lowest application temperature amounts to -20 °C.PropertiesGeneralPropertyTemperatureValueDensit

G-X 330 NiCr 4 2 is characterised by a high wear resistance. Usable under low impact stress.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.7 g/cm³MechanicalPropertyTemperatureValueCommentElastic modulus20.0 °C169 - 183 GPaHardness, Brinell20.0 °C430 - 690 [-]Hardness, Vickers20.0 °C450 - 7

G-X 300 CrNiSi 9 5 2 is characterised by a high wear resistance. Applicable at higher impact stress. The wear resistance inceases with the carbon content, while the resistance against impact stress decreases.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.7 g/cm³MechanicalPropertyTemperatur

The steel X 6 CrNiMoTi 17 12 2 is well suited for cold-forming, one must be aware of the increased cold strain hardening compared to carbon steels. Cold forming is worse than for X 5 CrNiMo 17 12 2. Its increased corrosion resistance to non-oxidizing acids and substances containing halogen allow it

Because of its higher Ni content compared standard type to X 5CrNi 18 10, steel X 5 CrNi 18 12 possesses a higher austenitic stability. This decreaes the cold strain hardening. The forming properties for cold heading and extrusion pressing are good even at high forming rates. However, one must be aw

Because of its higher Ni content compared standard type to X 5CrNi 18 10, steel X 5 CrNi 18 12 possesses a higher austenitic stability. This decreaes the cold strain hardening. The forming properties for cold heading and extrusion pressing are good even at high forming rates. However, one must be aw

The steel 67 SiCr 5 is used as cold rolled steel strip for springs with high dimensional accuracy and surface condition up to 3.0 mm thicknesses.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.83 g/cm³MechanicalPropertyTemperatureValueElastic modulus-100.0 °C217 GPa20.0 °C206 - 212 GPa100.0

The steel Ck 85 is used as cold rolled steel strip for springs with high dimensional accuracy and surface condition up to 2.5 mm thicknesses.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.8 g/cm³MechanicalPropertyTemperatureValueCommentElastic modulus-100.0 °C217 GPa20.0 °C206 - 212 GPa100

The steel 51CrV4 is used as cold rolled strip for springs and special applications in thicknesses of up to 6 mm and as tempered cold strip in thicknesses from 0.30 to 3.00 mm.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.83 g/cm³MechanicalPropertyTemperatureValueElastic modulus-100.0 °C21

The steel Ck 75 is used as cold rolled steel strip for springs with high dimensional accuracy and surface condition up to 2.0 mm thicknesses.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.8 g/cm³MechanicalPropertyTemperatureValueCommentElastic modulus-100.0 °C217 GPa20.0 °C206 - 212 GPa100

The steel 50 CrV 4 is used as cold rolled steel strip for springs with high dimensional accuracy and surface condition up to 3.0 mm thicknesses.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.83 g/cm³MechanicalPropertyTemperatureValueElastic modulus-100.0 °C217 GPa20.0 °C206 - 212.6 GPa100.

The steel 102Cr6 is used as cold rolled strip for springs and special applications in thicknesses of up to 6 mm and as tempered cold strip in thicknesses from 0.30 to 3.00 mm.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.81 g/cm³MechanicalPropertyTemperatureValueElastic modulus-100.0 °C21

The steel 21 NiCrMoS 2 is used for wear loaded parts in the vehicle and mechanical engineering with medium core strength, better machinability, high toughness and high fatigue strength (e.g. gears, shafts, axles). The lowest application amounts to -60 °C, the best application up to 60 mm nominal siz