Material CuZn36Pb3, mat. No. CW603N, is an unhardenable wrought alloy. to the comparable make CuZn36Pb3, mat. No. 2.0375 acc. to DIN 17660 : 1983-12 applies:High hardness and strength parameter are achievable by cold forming only. Thermal and electrical conductivity are lower than for the unleaded b

Wire fom copper alloy for general purposes.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C8.4 - 8.45 g/cm³MechanicalPropertyTemperatureValueCommentElastic modulus20.0 °C110 GPa100.0 °C106 GPa200.0 °C102 GPa300.0 °C97 GPa400.0 °C89 GPa500.0 °C79 GPaHardness, Vickers20.0 °C115 - 155 [-]Poisson

Steel 28 Mn 6 is suitable for lower strained parts in vehicle manufacturing, engine and machine engineering, weldable (e.g. cardan shafts, camshafts, gear wheels). Lowest application temp. -25 °C.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.82 - 7.85 g/cm³MechanicalPropertyTemperatureVal

CuZn30 (CW505L) is an unhardenable wrought alloy. High hardness and strength parameter are achievable by cold forming only. Thermal and electrical conductivity are lower than for CuZn28. Corrosion resistance is similar to pure copper. Processing properties: warm forming: good cold forming: very goo

CuZn30 (CW505L) is an unhardenable wrought alloy. High hardness and strength parameter are achievable by cold forming only. Thermal and electrical conductivity are lower than for CuZn28. Corrosion resistance is similar to pure copper. Processing properties: warm forming: good cold forming: very goo

CuZn36 (CW507L) is an unhardenable wrought alloy. High hardness and strength parameter are achievable by cold forming only. Thermal and electrical conductivity are lower than for CuZn33. Corrosion resistance is similar to pure copper. Processing properties: warm forming: good cold forming: very goo

Steel 25 CrMoS 4 is suitable for parts of high strength and ductility requirements at mean and higher heat-treatment sections and enhanced workability in vehicle manufacturing, engine and machine engineering (e.g. crankshafts, steering knuckles, pinions). Lowest application temp. -40 °C.PropertiesGe

CuZn36 (CW507L) is an unhardenable wrought alloy. High hardness and strength parameter are achievable by cold forming only. Thermal and electrical conductivity are lower than for CuZn33. Corrosion resistance is similar to pure copper. Processing properties: warm forming: good cold forming: very goo

CuZn36 (CW507L) is an unhardenable wrought alloy. High hardness and strength parameter are achievable by cold forming only. Thermal and electrical conductivity are lower than for CuZn33. Corrosion resistance is similar to pure copper. Processing properties: warm forming: good cold forming: very goo

CuZn23Al6Mn4Fe3Pb (CW 704R former identification: CuZn23Al6Mn4Fe3) is an unhardenable copper alloy. High hardness and strength values are achievable by cold forming only. Strength properties are improved by AL- and Fe- addition. Manganese and aluminium increase corrosion resistance. The alloy is sea

Wire fom copper alloy for general purposes.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C8.4 - 8.45 g/cm³MechanicalPropertyTemperatureValueCommentElastic modulus20.0 °C110 GPa100.0 °C106 GPa200.0 °C102 GPa300.0 °C97 GPa400.0 °C89 GPa500.0 °C79 GPaHardness, Vickers20.0 °C160 [-]Poisson'

CuZn36 (CW507L) is an unhardenable wrought alloy. High hardness and strength parameter are achievable by cold forming only. Thermal and electrical conductivity are lower than for CuZn33. Corrosion resistance is similar to pure copper. Processing properties: warm forming: good cold forming: very goo

Wire fom copper alloy for general purposes.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C8.4 - 8.45 g/cm³MechanicalPropertyTemperatureValueCommentElastic modulus20.0 °C110 GPa100.0 °C106 GPa200.0 °C102 GPa300.0 °C97 GPa400.0 °C89 GPa500.0 °C79 GPaHardness, Vickers20.0 °C130 - 170 [-]Poisson

Steel 28 Cr 4 is suitable for smaller parts of a little higher load in vehicle manufacturing, engine and machine engineering (e.g. transmission gears, drive shafts). Lowest application temp. -25 °C.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.83 - 7.85 g/cm³MechanicalPropertyTemperatureV

CuZn5 (CW500L) is an unhardenable wrought alloy. High hardness and strength parameter are achievable by cold forming only. CuZn5 has a favorable conductivity, resistance to atmospheric corrosion and is ideal for enamelling. Processing properties: warm forming: moderately cold forming: good machinab

Copper alloy profiles and bars for general purposes.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C8.4 - 8.44 g/cm³MechanicalPropertyTemperatureValueCommentElastic modulus20.0 °C102 GPaHardness, Brinell20.0 °C120 [-]Hardness, Vickers20.0 °C125 - 130 [-]Poisson's ratio20.0 °C0.34 [-]Shea

CuZn5 (CW500L) is an unhardenable wrought alloy. High hardness and strength parameter are achievable by cold forming only. CuZn5 has a favorable conductivity, resistance to atmospheric corrosion and is ideal for enamelling. Processing properties: warm forming: moderately cold forming: good machinab

Wire fom copper alloy for general purposes.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C8.4 - 8.44 g/cm³MechanicalPropertyTemperatureValueCommentElastic modulus20.0 °C102 GPaHardness, Brinell20.0 °C100 - 145 [-]Hardness, Vickers20.0 °C100 - 180 [-]Poisson's ratio20.0 °C0.34 [-]Shear m

CuZn5 (CW500L) is an unhardenable wrought alloy. High hardness and strength parameter are achievable by cold forming only. CuZn5 has a favorable conductivity, resistance to atmospheric corrosion and is ideal for enamelling. Processing properties: warm forming: moderately cold forming: good machinab

CuZn5 (CW500L) is an unhardenable wrought alloy. High hardness and strength parameter are achievable by cold forming only. CuZn5 has a favorable conductivity, resistance to atmospheric corrosion and is ideal for enamelling. Processing properties: warm forming: moderately cold forming: good machinab