Steel L245MB is produced as welded pipe for flammable media in condition thermomechanically rolled. Its yield stress is between 245 and 440 N/mm². The steel is weldable, its carbon equivalent CEV accounts for max. 0.40. To the welding seam (welding methods SAW, COW) applies a mandrel-diameter for th

RoSt 44-2 is used for the manufacturing of welded tubes. Its applicated as fine-grained steel for dynamic loaded welded constructions up to - 25 °C.PropertiesGeneralPropertyTemperatureValueCommentDensity23.0 °C7.8 - 7.9 g/cm³Typical for Low Carbon SteelMechanicalPropertyTemperatureValueCommentElasti

RQSt 37-2 is used as folding grade for welded constructions stress dependent up to - 20 °C.PropertiesGeneralPropertyTemperatureValueCommentDensity23.0 °C7.8 - 7.9 g/cm³Typical for Low Carbon SteelMechanicalPropertyTemperatureValueCommentElastic modulus23.0 °C200 - 215 GPaTypical for Low Carbon Steel

S275JRC is used for folding, section cold forming and cold drawing grade. The steel is applicable for temperatures up to -20 °C. Compared to S235JRC is achievable a saving of material due to the by 40 MPa higher yield point. Max. product thickness amounts 20 mm for folding and 8 mm for cold roll for

S275J0C is used for folding, section cold forming and cold drawing grade. The steel is applicable for temperatures up to -20 °C subject to the load. Compared to S235J0C is achievable a saving of material due to the by 40 MPa higher yield point. Max. product thickness amounts 20 mm for folding and 8

S355K2G4C is used for folding, section cold forming and cold drawing grade. The high-tensile fine grained steel is applicable for welding constructions of dynamic load up to -20 °C. Compared to S235J2G3C is achievable a considerable saving of material due to the by 120 MPa higher yield point. The st

S355J2G4C is used for folding, section cold forming and cold drawing grade. The high-tensile fine grained steel is applicable for welding constructions of dynamic load up to -20 °C. Compared to S235J2G4C is achievable a considerable saving of material due to the by 120 MPa higher yield point. The st

S275J2G4C is used for folding, section cold forming and cold drawing grade. The steel is applicable for welding constructions of dynamic load up to -20 °C. Mechanical properties in thickness direction have to comply with EURONORM 164 by arrangement. Max. product thickness amounts 20 mm for folding a

Seamless tubes made from St 52.4 are used in the apparatus engineering, container and pipe construction as well as mechanical engineering. Operating temperature max. 300 °C, the allowed pressure is unlimited. The steel is weldable.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.83 g/cm³Mech

Seamless tubes made from St 44.4 are used in the apparatus engineering, container and pipe construction as well as mechanical engineering. Operating temperature max. 300 °C, the allowed pressure is unlimited. The steel is weldable.PropertiesGeneralPropertyTemperatureValueCommentDensity20.0 °C7.8 - 7

Seamless tubes made from St 37.4 are used in the apparatus engineering, container and pipe construction as well as mechanical engineering. Operating temperature max. 300 °C, the allowed pressure is unlimited. The steel is weldable.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.85 g/cm³Mech

High temperature steel. Application for shapes and flanges.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.85 g/cm³MechanicalPropertyTemperatureValueCommentElastic modulus-100.0 °C217 GPa20.0 °C212 GPa100.0 °C195 - 207 GPa200.0 °C195 - 199 GPa300.0 °C185 - 192 GPa400.0 °C175 - 184 GPa500.0

High temperature tube steel for seamless tubes. Applicable up to 500 °C wall temperature for continuous operation. Application: steam vessel and pressure vessel construction, apparatus construction, petrochemical industryPropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.85 g/cm³MechanicalProp

Successor note: Grade TTSt 35 V is replaced by P265NL (1.0453)PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.85 g/cm³MechanicalPropertyTemperatureValueCommentElastic modulus-100.0 °C217 GPa20.0 °C212 GPa100.0 °C207 GPa200.0 °C199 GPa300.0 °C192 GPa400.0 °C184 GPa500.0 °C175 GPa600.0 °C164

Material EN AC-AlMg3(b) is produced as sand and die cast. It shows the following casting characteristics and properties: plasticity: acceptable heat crack resistance: insufficient pressure tightness: insufficient workability (after heat-treatment): excellent corrosion resistance: excellent decorativ

Aluminium casting alloy (sand casting, permanent mould casting)PropertiesGeneralPropertyValueCommentDensity2.75 - 2.8 g/cm³Typical for Cast 2xx.x Series AluminiumMechanicalPropertyValueConditionRelated StandardsShapeCommentBending Fatigue Strength80.0 - 110.0 MPaT4EN 1706CastingElastic modulus72.0 G

Material EN AC-AlZn5Mg is produced as sand and die cast. It shows the following casting characteristics and properties: plasticity: acceptable heat crack resistance: insufficient pressure tightness: insufficient workability (after heat-treatment): excellent worability (casting condition): excellent

Aluminium casting alloy (sand casting, permanent mould casting, investment casting)PropertiesGeneralPropertyTemperatureValueConditionRelated StandardsShapeDensity2.6 g/cm³FEN 1706, EN 13195Casting20.0 °C2.6 g/cm³FEN 1706MechanicalPropertyTemperatureValueConditionRelated StandardsShapeCommentBending

Aluminium casting alloy (pressure die casting)PropertiesGeneralPropertyTemperatureValueConditionRelated StandardsShapeDensity2.6 g/cm³FEN 1706, EN 13195Casting20.0 °C2.6 g/cm³FEN 1706MechanicalPropertyTemperatureValueConditionRelated StandardsShapeCommentBending Fatigue Strength60.0 - 90.0 MPaFEN 17

Steel C25E is suitable for low strained parts of higher dimensions and complexer forms as well as higher demands for uniformity of properties and surface appearance in vehicle and machine engineering (e.g. piston rods, gear wheels).PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.82 g/cm³Mec