Aluminum DIN 3.0517 is a popular alloy that offers customers very good atmospheric corrosion resistance and moderate strength. Aluminum 3003 offers good machinability for aluminum alloys, though it is not heat treatable. Unlike other aluminum alloys, DIN 3.0517 is weldable by conventional welding me

Aluminum DIN 3.0517 is a popular alloy that offers customers very good atmospheric corrosion resistance and moderate strength. Aluminum 3003 offers good machinability for aluminum alloys, though it is not heat treatable. Unlike other aluminum alloys, DIN 3.0517 is weldable by conventional welding me

The alloy AlMn0,5Mg0,5 is special one for the packing planned alloy. The alloy belongs to the nature-hard aluminum materials. A strength increase can only occur by cold forming. It is very well warm and cold formable and is very well suitable to the deep-drawing (no lappet formation). Because of the

The alloy AlMn0,5Mg0,5 is special one for the packing planned alloy. The alloy belongs to the nature-hard aluminum materials. A strength increase can only occur by cold forming. It is very well warm and cold formable and is very well suitable to the deep-drawing (no lappet formation). Because of the

The alloy AlMn0,5Mg0,5 is special one for the packing planned alloy. The alloy belongs to the nature-hard aluminum materials. A strength increase can only occur by cold forming. It is very well warm and cold formable and is very well suitable to the deep-drawing (no lappet formation). Because of the

The alloy AlRMg1 belongs to the standardised glossing materials. It can be polished after preceding mechanical polishing chemically or electrolytically to high gloss. For using the high gloss surface a afterwards anodising is necessary. The degree of arranged reflection (gloss degree) dependents fro

The alloy AlRMg1 belongs to the standardised glossing materials. It can be polished after preceding mechanical polishing chemically or electrolytically to high gloss. For using the high gloss surface a afterwards anodising is necessary. The degree of arranged reflection (gloss degree) dependents fro

The alloy AlRMg1 belongs to the standardised glossing materials. It can be polished after preceding mechanical polishing chemically or electrolytically to high gloss. For using the high gloss surface a afterwards anodising is necessary. The degree of arranged reflection (gloss degree) dependents fro

The alloy AlRMg1 belongs to the standardised glossing materials. It can be polished after preceding mechanical polishing chemically or electrolytically to high gloss. For using the high gloss surface a afterwards anodising is necessary. The degree of arranged reflection (gloss degree) dependents fro

The alloy AlRMg1 belongs to the standardised glossing materials. It can be polished after preceding mechanical polishing chemically or electrolytically to high gloss. For using the high gloss surface a afterwards anodising is necessary. The degree of arranged reflection (gloss degree) dependents fro

The alloy Al99,85Mg1 belongs to the standardised glossing materials. It can be polished after preceding mechanical polishing chemically or electrolytically to high gloss. For using the high gloss surface a afterwards anodising is necessary. The degree of arranged reflection (gloss degree) dependents

The alloy Al99,85Mg1 belongs to the standardised glossing materials. It can be polished after preceding mechanical polishing chemically or electrolytically to high gloss. For using the high gloss surface a afterwards anodising is necessary. The degree of arranged reflection (gloss degree) dependents

The alloy Al99,85Mg1 belongs to the standardised glossing materials. It can be polished after preceding mechanical polishing chemically or electrolytically to high gloss. For using the high gloss surface a afterwards anodising is necessary. The degree of arranged reflection (gloss degree) dependents

The alloy Al99,85Mg1 belongs to the standardised glossing materials. It can be polished after preceding mechanical polishing chemically or electrolytically to high gloss. For using the high gloss surface a afterwards anodising is necessary. The degree of arranged reflection (gloss degree) dependents

The alloy Al99,85Mg1 belongs to the standardised glossing materials. It can be polished after preceding mechanical polishing chemically or electrolytically to high gloss. For using the high gloss surface a afterwards anodising is necessary. The degree of arranged reflection (gloss degree) dependents

The AlMg alloy is characterised all by a good corrosion resistance. It is sea water steady and resistant to saline atmosphere. The Mg content increase the strength, the cold forming capacity decreases with it. The alloys of this type are nature hard, i.e. only by a cold forming and not by a purposef

The alloy AlRMg0,5 belongs to the standardised shining materials. It can be polished after preceding mechanical polishing chemically or electrolytically to high gloss. If the high gloss surface is to be used with the material employment accordingly, is to be absolutely anodised afterwards.Properties

The alloy AlRMg0,5 belongs to the standardised shining materials. It can be polished after preceding mechanical polishing chemically or electrolytically to high gloss. If the high gloss surface is to be used with the material employment accordingly, is to be absolutely anodised afterwards.Properties

The alloy AlRMg0,5 belongs to the standardised shining materials. It can be polished after preceding mechanical polishing chemically or electrolytically to high gloss. If the high gloss surface is to be used with the material employment accordingly, is to be absolutely anodised afterwards.Properties

The alloy AlRMg0,5 belongs to the standardised shining materials. It can be polished after preceding mechanical polishing chemically or electrolytically to high gloss. If the high gloss surface is to be used with the material employment accordingly, is to be absolutely anodised afterwards.Properties