Mechanical properties in bars (YS & UTS) are: Better than those of 316L and also those of 316LN, Better Corrosion Resistance than that of 316L The chemical composition is balanced to obtain 40-60% ferrite after annealing between 950 and 1050°C fol-lowed by a fast cooling. The sensitivity to pre

5x(C+N). Non-magnetic in annealed condition. Slight magnetism is produced by cold-working operations.PropertiesGeneralPropertyValueDensity7.95 g/cm³MechanicalPropertyValueElastic modulus200 GPaElongation31.0 - 52.0 %Reduction of area66.0 - 70.0 %Tensile strength620.0 - 760.0 MPaThermalPropertyValue

5x(C+N). Non-magnetic in annealed condition. Slight magnetism is produced by cold-working operations.PropertiesGeneralPropertyValueDensity7.95 g/cm³MechanicalPropertyValueElastic modulus200 GPaElongation56 %Reduction of area72.0 %Tensile strength560 MPaThermalPropertyValueCommentCoefficient of ther

UGI 4435 IRH is an austenitic stainless steel (not magnetic) with a high Mo content and produced by a special method to optimize its cleanliness. Its composition provides it with very good corrosion resistance and is perfectly suited for prolonged contact with the skin. This grade also offers improv

UGIMA® 4362 is an austeno-ferritic stainless steel (Duplex) with better machinability than a standard 1.4362 (UGI® 4362), due mainly to reduced tool wear and better chip breakability. UGIMA® 4362 complies with the specification of 1.4362 in accordance with EN 10088-3, but retains all the qualities

UGIMA® 4057 is a member of the UGIMA® family of improved machinability martensitic stainless steels. It is developed exclusively by Ugitech. Its properties are identical to those of 1.4057, except for its machinability which is even better than that of 1.4057: UGIMA® 4057’s new technological advan

UGIMA® 4057 is a member of the UGIMA® family of improved machinability martensitic stainless steels. It is developed exclusively by Ugitech. Its properties are identical to those of 1.4057, except for its machinability which is even better than that of 1.4057: UGIMA® 4057’s new technological advan

UGIMA®-X 4305 is a stainless steel of highly improved machinability manufactured only by Ugitech. Its properties are identical to those of other 1.4305s except for its machinability, which is even better than that of UGIMA® 4305, the 1.4305 grade from Ugitech with already improved machinability. UG

UGIMA®-X 4305 is a stainless steel of highly improved machinability manufactured only by Ugitech. Its properties are identical to those of other 1.4305s except for its machinability, which is even better than that of UGIMA® 4305, the 1.4305 grade from Ugitech with already improved machinability. UG

PropertiesGeneralPropertyValueConditionRelated StandardsDensity2.67 g/cm³H36AA StandardsMechanicalPropertyValueConditionRelated StandardsCommentBending Fatigue Strength130.0 MPaH36AA StandardsElastic modulus70.0 GPaH36AA StandardsHardness, Brinell73.0 [-]H36AA StandardsPlane-Strain Fracture Toughnes

PropertiesGeneralPropertyValueConditionRelated StandardsDensity2.67 g/cm³H34AA Standards, ASTM B209MechanicalPropertyValueConditionRelated StandardsCommentBending Fatigue Strength125.0 MPaH34AA StandardsElastic modulus70.0 GPaH34AA Standards, ASTM B209Hardness, Brinell68.0 [-]H34AA StandardsPlane-St

PropertiesGeneralPropertyValueConditionRelated StandardsDensity2.67 g/cm³H32AA Standards, ASTM B209MechanicalPropertyValueConditionRelated StandardsCommentBending Fatigue Strength115.0 MPaH32AA StandardsElastic modulus70.0 GPaH32AA Standards, ASTM B209Hardness, Brinell60.0 [-]H32AA StandardsPlane-St

PropertiesGeneralPropertyValueConditionRelated StandardsDensity2.64 g/cm³OAA Standards, ASTM B211, ASTM B316MechanicalPropertyValueConditionRelated StandardsCommentBending Fatigue Strength140.0 MPaOAA StandardsElastic modulus71.0 GPaOAA Standards, ASTM B211, ASTM B316Hardness, Brinell65.0 [-]OAA Sta

PropertiesGeneralPropertyValueConditionRelated StandardsDensity2.66 g/cm³OAA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B313, ASTM B547MechanicalPropertyValueConditionRelated StandardsCommentBending Fatigue Strength115.0 MPaOAA StandardsElastic modulus70.0 GPaOAA Standards, ASTM B20

PropertiesGeneralPropertyValueConditionRelated StandardsDensity2.66 g/cm³H34AA Standards, ASTM B209MechanicalPropertyValueConditionRelated StandardsCommentBending Fatigue Strength130.0 MPaH34AA StandardsElastic modulus70.0 GPaH34AA Standards, ASTM B209Hardness, Brinell73.0 [-]H34AA StandardsPlane-St

PropertiesGeneralPropertyValueConditionRelated StandardsDensity2.66 g/cm³H32AA Standards, ASTM B209MechanicalPropertyValueConditionRelated StandardsCommentBending Fatigue Strength125.0 MPaH32AA StandardsElastic modulus70.0 GPaH32AA Standards, ASTM B209Hardness, Brinell67.0 [-]H32AA StandardsPlane-St

PropertiesGeneralPropertyValueConditionRelated StandardsDensity2.66 g/cm³H32AA Standards, ASTM B209, ASTM B211, ASTM B313, ASTM B547MechanicalPropertyValueConditionRelated StandardsCommentBending Fatigue Strength125.0 MPaH32AA StandardsElastic modulus70.0 GPaH32AA Standards, ASTM B209, ASTM B211, AS

PropertiesGeneralPropertyValueConditionRelated StandardsDensity2.69 g/cm³OAA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547MechanicalPropertyValueConditionRelated StandardsCommentBending Fatigue Strength85.0 MPaOAA StandardsElastic modulus69.0 GPaOAA Standards, ASTM B209, ASTM B210

Extra High Strength SteelPropertiesGeneralPropertyValueCommentCarbon equivalent (CET)0.32 [-]Carbon equivalent (CEV)0.46 [-]for t ≤ 50 mm plate thickness0.48 [-]for 50 < t ≤100 mm plate thickness0.5 [-]for 100 < t ≤ 250 mm plate thicknessDensity7.8 - 7.9 g/cm³typical for low carbon steelMechan

PropertiesGeneralPropertyValueConditionRelated StandardsDensity2.68 g/cm³H28EN 573-3, EN 485, EN 754MechanicalPropertyValueConditionRelated StandardsCommentBending Fatigue Strength125.0 MPaH28EN 573-3, EN 485, EN 754Elastic modulus70.0 GPaH28EN 573-3, EN 485, EN 754Hardness, Brinell77.0 [-]H28EN 573