Material CuNi12Zn24, mat. No. CW403J is an alloy of high strength and hardness. To the comparabel DIN-mark CuNi12Zn24, mat. No. 2.0730, acc. to DIN 17663 : 1983-12 applies: Strength is further increasable due to the high strain hardening capability. The material does not embrittle at low temperatur

Material CuNi10Zn42Pb2, mat. No. CW402J, is incomparable to a DIN-mark. It is used in the form of bars, prematerial for forged parts, forged parts, wires and profiles.PropertiesGeneralPropertyTemperatureValueCommentDensity23.0 °C8.4 - 8.9 g/cm³Typical for Wrought Copper Nickel Silver GradeMechanical

Material CuNi10Zn42Pb2, mat. No. CW402J, is incomparable to a DIN-mark. It is used in the form of bars, prematerial for forged parts, forged parts, wires and profiles.PropertiesGeneralPropertyTemperatureValueCommentDensity23.0 °C8.4 - 8.9 g/cm³Typical for Wrought Copper Nickel Silver GradeMechanical

Material CuNi10Zn27, mat. No. CW401J, is incomparable to a DIN-mark. It is used in the form of wires.PropertiesGeneralPropertyTemperatureValueCommentDensity23.0 °C8.4 - 8.9 g/cm³Typical for Wrought Copper Nickel Silver GradeMechanicalPropertyTemperatureValueCommentElastic modulus23.0 °C120 - 140 GPa

Material CuNi10Zn27, mat. No. CW401J, is incomparable to a DIN-mark. It is used in the form of wires.PropertiesGeneralPropertyTemperatureValueCommentDensity23.0 °C8.4 - 8.9 g/cm³Typical for Wrought Copper Nickel Silver GradeMechanicalPropertyTemperatureValueCommentElastic modulus23.0 °C120 - 140 GPa

PropertiesGeneralPropertyTemperatureValueDensity20.0 °C8.4 - 8.44 g/cm³MechanicalPropertyTemperatureValueCommentElastic modulus20.0 °C102 GPaElongation20.0 °C8 %Elongation A1020.0 °C6 %Elongation A10020.0 °C4 %Shear modulus23.0 °C40 GPaTypical for Wrought Copper BrassTensile strength20.0 °C490 MPaYi

PropertiesGeneralPropertyTemperatureValueDensity20.0 °C8.4 g/cm³MechanicalPropertyTemperatureValueCommentElastic modulus20.0 °C102 GPaElongation20.0 °C8 %Elongation A1020.0 °C6 %Elongation A10020.0 °C4 %Shear modulus23.0 °C40 GPaTypical for Wrought Copper BrassTensile strength20.0 °C490 MPaYield str

CuZn40Mn1Pb1 (CW720R former identification: CuZn40MnPb) is an unhardenable copper alloy. High hardness and strength parameter are achievable by cold forming only. Manganes increases corrosion resistance and sliding qualities. Improved machinability by Pb-addition. Processing properties: warm forming

CuZr, mat. No CW120C, is counted among hardenable, low alloyed copper alloys. To the comparable make CuZr, mat. No 2.1580, acc. to DIN 17666 : 1983-12 applies: The strength properties of CuZr are not as favorable as for CuCrZr but it very well meets high requirements to tempering strength and creep

PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.83 - 7.85 g/cm³MechanicalPropertyTemperatureValueElastic modulus-100.0 °C217 GPa20.0 °C210 - 212.6 GPa100.0 °C205 - 207 GPa200.0 °C195 - 199 GPa300.0 °C185 - 192 GPa400.0 °C184 GPa500.0 °C175 GPa600.0 °C164 GPaElongation20.0 °C9 - 13 %Poisson&

Material CuZn36Sn1Pb (CW712R) is incomparable to a DIN-make. It is used in the form of rods, hollow rods, profiles, wires, forging prematerial and forged parts.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C8.3 g/cm³MechanicalPropertyTemperatureValueCommentElastic modulus23.0 °C100 - 125 GPa

Material CuZn36Sn1Pb (CW712R) is incomparable to a DIN-make. It is used in the form of rods, hollow rods, profiles, wires, forging prematerial and forged parts.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C8.3 g/cm³MechanicalPropertyTemperatureValueCommentElastic modulus23.0 °C100 - 125 GPa

Material CuZn32Pb2AsFeSi (CW709R) is incomparable to a DIN-make. It is used in the form of rods.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C8.4 g/cm³MechanicalPropertyTemperatureValueCommentElastic modulus23.0 °C100 - 125 GPaTypical for Wrought Copper BrassElongation20.0 °C15 %Elongation

Material CuZn32Pb2AsFeSi (CW709R) is incomparable to a DIN-make. It is used in the form of rods.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C8.4 g/cm³MechanicalPropertyTemperatureValueCommentElastic modulus23.0 °C100 - 125 GPaTypical for Wrought Copper BrassElongation20.0 °C20 %Elongation

PropertiesGeneralPropertyTemperatureValueDensity20.0 °C8.4 - 8.45 g/cm³MechanicalPropertyTemperatureValueCommentElastic modulus20.0 °C110 GPa100.0 °C106 GPa200.0 °C102 GPa300.0 °C97 GPa400.0 °C89 GPa500.0 °C79 GPaElongation20.0 °C25 %Poisson's ratio20.0 °C0.34 [-]Shear modulus23.0 °C40 GPaTypic

CuZn30 (CW505L) is an unhardenable wrought alloy. High hardness and strength parameter are achievable by cold forming only. Thermal and electrical conductivity are lower than for CuZn28. Corrosion resistance is similar to pure copper. Processing properties: warm forming: good cold forming: very goo

PropertiesGeneralPropertyTemperatureValueDensity20.0 °C8.75 - 8.8 g/cm³MechanicalPropertyTemperatureValueCommentElastic modulus20.0 °C122 GPaElongation20.0 °C20 %Elongation A5020.0 °C10 %Poisson's ratio20.0 °C0.34 [-]Shear modulus23.0 °C40 GPaTypical for Wrought Copper BrassTensile strength20.0

PropertiesGeneralPropertyTemperatureValueCommentDensity23.0 °C7.8 - 7.9 g/cm³Typical for High Carbon SteelMechanicalPropertyTemperatureValueCommentElastic modulus23.0 °C200 - 215 GPaTypical for High Carbon SteelHardness, Rockwell B23.0 °C98 [-]Hardness, Rockwell Superficial 15-T23.0 °C92 [-]Hardness

PropertiesGeneralPropertyTemperatureValueCommentDensity23.0 °C7.8 - 7.9 g/cm³Typical for High Carbon SteelMechanicalPropertyTemperatureValueCommentElastic modulus23.0 °C200 - 215 GPaTypical for High Carbon SteelHardness, Rockwell B23.0 °C98 [-]Hardness, Rockwell Superficial 15-T23.0 °C92 [-]Hardness

PropertiesGeneralPropertyTemperatureValueCommentDensity23.0 °C7.8 - 7.9 g/cm³Typical for High Carbon SteelMechanicalPropertyTemperatureValueCommentElastic modulus23.0 °C200 - 215 GPaTypical for High Carbon SteelHardness, Rockwell B23.0 °C98 [-]Hardness, Rockwell Superficial 15-T23.0 °C92 [-]Hardness