With this mixture of ceramics, a small amount of zirconium dioxide is added to the aluminum oxide which significantly improves the hardness and stability and simultaneously increases the toughness. It has following features: Hardness Resistance to pressure Resistance to thermal shock Reistance to t

With this kind of mixed ceramic, a small amount of aluminum oxide is added to the zirconium oxide to significantly improve the wear-resistance, elasticity and toughness. It has following features: Thermal insulation Flexural Strenth Electrical insulation Temperature and thermo shock resistance Frac

Rolled and Molded Rods are made from an alpha paper impregnated with an electrical grade of phenolic resin. RM629 is used for electrical and mechanical applications, meeting NEMA XX requirements.PropertiesGeneralPropertyValueTesting StandardCommentDensity1.4 g/cm³ASTM D349Moisture absorption0.58 %AS

Fine weave canvas phenolic material with fabric construction weight intermediate to BT13NPN and BT25NPN. BT12NPN is designed for better machining than grade BT13NPN and lower cost than BT25NPN.PropertiesGeneralPropertyValueTesting StandardCommentDensity1.3 g/cm³ASTM D792Moisture absorption1.8 %ASTM

Being a heat treated version of BT12NPN, BT12HPN is a fine weave canvas phenolic material with fabric construction weight intermediate to BT13NPN and BT25NPN. BT12HPN is designed for better machining than grade BT13NPN and lower cost than BT25NPN.PropertiesGeneralPropertyValueTesting StandardComment

Grade RTB324 is constructed of a fine weave cotton fabric which has been bleached to remove impurities, and a modified phenolic resin with powdered PTFE added for lubrication. It has low moisture absorption and excellent dimensional stability and chemical resistance. Typical uses include bearing ret

Being a heat treated version of RT342, RT342H is a fine weave canvas phenolic material with fabric construction weight intermediate to RT310 and RTB320. RT342H is designed for better machining than grade RT310 and lower cost than RTB320.PropertiesGeneralPropertyValueTesting StandardCommentDensity1.3

Rolled and Molded Rods made from a glass fabric with a non-brominated epoxy resin system. RM500A combines excellent electrical characteristics with very good physical properties. Electrical properties maintained in high humidity conditions. RM500A is not flame resistant. Material meets NEMA G-10.Pro

Tungsten hard material for wear protectionPropertiesGeneralPropertyTemperatureValueDensity23.0 °C14.55 g/cm³BinderCobalt binderGrain structureUltrafine grain sizeMechanicalPropertyTemperatureValueCompressive strength23.0 °C4900 MPaElastic modulus23.0 °C580 GPaHardness, Rockwell A23.0 °C92.7 [-]Hardn

Tungsten hard material for wear protectionPropertiesGeneralPropertyTemperatureValueDensity23.0 °C14.55 g/cm³BinderCobalt binderGrain structureSubmicron grain sizeMechanicalPropertyTemperatureValueCompressive strength23.0 °C4800 MPaElastic modulus23.0 °C585 GPaHardness, Rockwell A23.0 °C91.8 [-]Hardn

Tungsten hard material for wear protectionPropertiesGeneralPropertyTemperatureValueDensity23.0 °C14.8 g/cm³BinderCobalt binderGrain structureFine grain sizeMechanicalPropertyTemperatureValueCompressive strength23.0 °C5000 MPaElastic modulus23.0 °C590 GPaHardness, Rockwell A23.0 °C90.9 [-]Hardness, V

Tungsten hard material for wear protectionPropertiesGeneralPropertyTemperatureValueDensity23.0 °C14.85 g/cm³BinderCobalt binderGrain structureMedium grain sizeMechanicalPropertyTemperatureValueCompressive strength23.0 °C4800 MPaElastic modulus23.0 °C605 GPaHardness, Rockwell A23.0 °C89.4 [-]Hardness

Tungsten hard material for wear protectionPropertiesGeneralPropertyTemperatureValueDensity23.0 °C14.05 g/cm³BinderCobalt binderGrain structureCoarse grain sizeMechanicalPropertyTemperatureValueCompressive strength23.0 °C3600 MPaElastic modulus23.0 °C530 GPaHardness, Rockwell A23.0 °C85.6 [-]Hardness

Grade BP11MPN is a medium weave cotton phenolic composite.PropertiesGeneralPropertyValueTesting StandardCommentBonding strength771.1 KgASTM D229Condition ADensity1.44 g/cm³ASTM D792Moisture absorption1.2 %ASTM D570Condition AMechanicalPropertyValueTesting StandardCommentCompressive strength262 MPaAS

NP575 is a woven glass fabric combined with a high temperature epoxy resin. It is engineered to provide superior characteristics at elevated temperatures.PropertiesGeneralPropertyValueTesting StandardCommentMoisture absorption0.07 %ASTM D570Condition D₁-24/23MechanicalPropertyTemperatureValueTesting

Grade RT507 has good electrical properties under humid conditions, superior heat resistance, and superior arc resistance. RT507 also complies with MIL-I-24768/17, Type GSG, ASTM D709 Type IV Grade G-7 and IEC 61212-3-1 SI GC 21.PropertiesGeneralPropertyValueTesting StandardCommentDensity1.93 g/cm³AS

Rolled and Molded Rods are made from an alpha paper impregnated with an electrical grade of phenolic resin.PropertiesGeneralPropertyValueTesting StandardCommentDensity1.4 g/cm³ASTM D349Moisture absorption0.58 %ASTM D349Condition D₁-24/23MechanicalPropertyValueTesting StandardCommentCompressive stren

Tungsten hard material for wear protectionPropertiesGeneralPropertyTemperatureValueDensity23.0 °C13.15 g/cm³BinderCobalt binderGrain structureCoarse grain sizeMechanicalPropertyTemperatureValueCompressive strength23.0 °C3100 MPaElastic modulus23.0 °C450 GPaHardness, Rockwell A23.0 °C81.7 [-]Hardness

Tungsten hard material for wear protectionPropertiesGeneralPropertyTemperatureValueDensity23.0 °C13.15 g/cm³BinderCobalt binderGrain structureCoarse grain sizeMechanicalPropertyTemperatureValueCompressive strength23.0 °C3200 MPaElastic modulus23.0 °C450 GPaHardness, Rockwell A23.0 °C82.6 [-]Hardness

Tungsten hard material for wear protectionPropertiesGeneralPropertyTemperatureValueDensity23.0 °C14.9 g/cm³BinderCobalt binderGrain structureMedium grain sizeMechanicalPropertyTemperatureValueCompressive strength23.0 °C6000 MPaElastic modulus23.0 °C615 GPaHardness, Rockwell A23.0 °C91.5 [-]Hardness,