Tungsten hard material for wear protectionPropertiesGeneralPropertyTemperatureValueDensity23.0 °C15.25 g/cm³BinderCobalt binderGrain structureUltrafine grain sizeMechanicalPropertyTemperatureValueCompressive strength23.0 °C12500 MPaElastic modulus23.0 °C670 GPaHardness, Rockwell A23.0 °C95.2 [-]Hard

Tungsten hard material for wear protectionPropertiesGeneralPropertyTemperatureValueDensity23.0 °C14.3 g/cm³BinderCobalt binderGrain structureFine grain sizeMechanicalPropertyTemperatureValueCompressive strength23.0 °C4900 MPaElastic modulus23.0 °C560 GPaHardness, Rockwell A23.0 °C89.7 [-]Hardness, V

Tungsten hard material for wear protectionPropertiesGeneralPropertyTemperatureValueDensity23.0 °C14.75 g/cm³BinderCobalt binderGrain structureSubmicron grain sizeMechanicalPropertyTemperatureValueCompressive strength23.0 °C6700 MPaElastic modulus23.0 °C610 GPaHardness, Rockwell A23.0 °C92.6 [-]Hardn

Tungsten hard material for wear protectionPropertiesGeneralPropertyTemperatureValueDensity23.0 °C14.95 g/cm³BinderCobalt binderGrain structureSubmicron grain sizeMechanicalPropertyTemperatureValueCompressive strength23.0 °C7200 MPaElastic modulus23.0 °C625 GPaHardness, Rockwell A23.0 °C92.9 [-]Hardn

Tungsten hard material for wear protectionPropertiesGeneralPropertyTemperatureValueDensity23.0 °C14.95 g/cm³BinderCobalt binderGrain structureFine grain sizeMechanicalPropertyTemperatureValueCompressive strength23.0 °C6400 MPaElastic modulus23.0 °C625 GPaHardness, Rockwell A23.0 °C92.1 [-]Hardness,

Tungsten hard material for wear protectionPropertiesGeneralPropertyTemperatureValueDensity23.0 °C14.95 g/cm³BinderCobalt binderGrain structureFine grain sizeMechanicalPropertyTemperatureValueCompressive strength23.0 °C7000 MPaElastic modulus23.0 °C630 GPaHardness, Rockwell A23.0 °C92.7 [-]Hardness,

Tungsten hard material for wear protectionPropertiesGeneralPropertyTemperatureValueDensity23.0 °C13.05 g/cm³BinderCobalt binderGrain structureFine grain sizeMechanicalPropertyTemperatureValueCompressive strength23.0 °C5700 MPaElastic modulus23.0 °C525 GPaHardness, Rockwell A23.0 °C91 [-]Hardness, Vi

Tungsten hard material for wear protectionPropertiesGeneralPropertyTemperatureValueDensity23.0 °C12.4 g/cm³BinderCobalt binderGrain structureFine grain sizeMechanicalPropertyTemperatureValueCompressive strength23.0 °C5900 MPaElastic modulus23.0 °C515 GPaHardness, Rockwell A23.0 °C91.5 [-]Hardness, V

NP338 is a combination of two Norplex-Micarta grades, NP310 which is a canvas phenolic, on one side of the laminate, and NP315, a canvas phenolic with graphite added as a solid lubricant on the other side of the laminate. Material is conductive to electricity and should not be used where conductivit

VESTALITE® P 311 is a polyurethane based resin formulation specially designed as matrix for fast curing prepreg applications. It gives room temperature stable, dry and non-tacky prepregs, which can be formed thermoplastically at 70 - 100°C and cured at temperatures between 150 and 180°C.PropertiesGe

17 oz. aramid and soft glass fibers are combined to make a fabric that is stronger than pure aramid and less abrasive than glass fabrics. This material is impregnated with a high temperature epoxy resin matrix, which produces a composite with excellent mechanical strength at elevated temperatures an

Linen phenolic laminate with graphite added as a solid lubricant. The linen substrate provides better surface to machined parts, and, more uniform wear resistance than BP11NPG.PropertiesGeneralPropertyValueTesting StandardCommentBonding strength861.8 KgASTM D229Condition ADensity1.39 g/cm³ASTM D792M

BR60 is a natural colored composite made from a 24 oz/sq. yd canvas which is passed through the treater twice to insure impregnation of the fibers and to obtain the resin content desired for optimal performance. The resin system is a molybdenum disulfide filled phenolic with good impregnation qualit

A paper-base laminate with low phenolic resin content for hard, flat surfaces. It is typically hot punched for numerous low voltage electrical applications of less than 250 volts where the material is not subjected to high humidity.PropertiesGeneralPropertyValueTesting StandardCommentDensity1.3 g/cm

RT629 is a paper phenolic tube intended primarily for mechanical applications, but is suitable for electrical applications as well. The electrical properties are not quite as good as those of RT630. RT629 also complies with MIL-I-24768/11, Type PBG and ASTM D709 Type I Grade XX and IEC 612112-3-1-PF

Grade RT628 is an improved machining grade meeting NEMA XX for tubes. It has low moisture absorption and good dimensional stability. The primary application is in transformers.PropertiesGeneralPropertyValueTesting StandardCommentDensity1.22 g/cm³ASTM D792Moisture absorption1.25 %ASTM D570Condition D

RTB320Z is similar to RTB320X being composed of an extra-fine weave woven cotton fabric with a phenolic resin system. RTB320Z tubes have higher densities (minimum allowable specific gravity is 1.30) resulting in enhanced precise machining characteristics and are expected to give longer life in wear

RTB320X is composed of an extra-fine weave woven cotton fabric combined with a phenolic resin system to produce a tube product that has superior machining capability with smooth, fiber free surfaces. RTB320X also complies with MIL-I-24768/13, Type FBE, ASTM D709 Type II Grade LE, Federal Specificati

Tungsten hard material for wear protectionPropertiesGeneralPropertyTemperatureValueDensity23.0 °C15.35 g/cm³BinderCobalt binderGrain structureSubmicron grain sizeMechanicalPropertyTemperatureValueCompressive strength23.0 °C8500 MPaElastic modulus23.0 °C665 GPaHardness, Vickers, 1023.0 °C2020 [-]Plan

Being a hot oil treated version of BT25NPN, BT25SPN has low moisture absorption and excellent dimensional stability.PropertiesGeneralPropertyValueTesting StandardCommentDensity1.29 g/cm³ASTM D792Moisture absorption1.1 %ASTM D570Condition D₁-24/23MechanicalPropertyValueTesting StandardCommentCompress